Effect of Dissolved Oxygen on Stress Corrosion Cracking of X70 Pipeline Steel in Near-Neutral pH Solution

Abstract To clarify the role of dissolved oxygen in near-neutral pH stress corrosion cracking (SCC), slow strain rate test (SSRT), dynamic polarization technique, and electrochemical impedance spec...

[1]  Y. F. Cheng,et al.  Corrosion behavior of X-70 pipe steel in near-neutral pH solution , 2007 .

[2]  Y. F. Cheng.  Analysis of electrochemical hydrogen permeation through X-65 pipeline steel and its implications on pipeline stress corrosion cracking , 2007 .

[3]  T. Veziroglu.  IJHE grows with Hydrogen Economy , 2007 .

[4]  J. González-Rodríguez,et al.  Effect of hydrogen on the mechanical properties of X-70 pipeline steel in diluted NaHCO3 solutions at different heat treatments , 2005 .

[5]  David Scott,et al.  Fossil Sources: “Running Out” is Not the Problem , 2005 .

[6]  K. Darowicki,et al.  Investigations of the passive layer cracking by means of Dynamic Electrochemical Impedance Spectroscopy , 2003 .

[7]  Andrej Atrens,et al.  Review of stress corrosion cracking of pipeline steels in “low” and “high” pH solutions , 2003 .

[8]  Weixing Chen,et al.  Environmental aspects of near-neutral pH stress corrosion cracking of pipeline steel , 2002 .

[9]  H. Sohn,et al.  In situ surface enhanced Raman spectroscopic study on the effect of dissolved oxygen on the corrosion film on low carbon steel in 0.01 M NaCl solution , 2001 .

[10]  M. Elboujdaini,et al.  Development of a Predictive Model for the Initiation and Early Stage Growth of Near Neutral pH SCC of Pipeline Steels , 2001 .

[11]  X. Mao,et al.  Transgranular Stress Corrosion Cracking of X-80 and X-52 Pipeline Steels in Dilute Aqueous Solution with Near-Neutral pH , 1999 .

[12]  Jing-Li Luo,et al.  Hydrogen-Facilitated Anodic Dissolution-Type Stress Corrosion Cracking of Pipeline Steels in Near-Neutral pH Solution , 1999 .

[13]  Stein Olsen,et al.  An Electrochemical Model for Prediction of Corrosion of Mild Steel in Aqueous Carbon Dioxide Solutions , 1996 .

[14]  J. Bardwell,et al.  In situ XANES study of galvanostatic reduction of the passive film on iron , 1995 .

[15]  B. A. Harle,et al.  Technical Note: Low-pH Stress Corrosion Crack Propagation in API X-65 Line Pipe Steel , 1993 .

[16]  G. McIntire,et al.  THE EFFECT OF DISSOLVED CO2 AND O2 ON THE CORROSION OF IRON , 1990 .

[17]  C. M. Rangel,et al.  VOLTAMMETRIC STUDIES OF THE TRANSPASSIVE DISSOLUTION OF MILD STEEL IN CARBONATE/BICARBONATE SOLUTIONS , 1989 .

[18]  R. N. Parkins,et al.  Current Topics in Corrosion: Factors Influencing Stress Corrosion Crack Growth Kinetics , 1987 .