Fracture healing and transport properties of wellbore cement in the presence of supercritical CO2

This paper investigates the process and rate of carbonation reaction of Class A wellbore cement exposed to CO2-saturated solution at confined conditions similar to those employed in geological storage of CO2. The main goal was to investigate whether reaction improves or degrades the sealing/healing capacity of fractured Type A cement plugs. Batch reaction experiments were performed for up to three months, on both intact and fractured Class A Portland cement cylinders, at a constant confining pressure of 30 MPa, a temperature of 80 °C and a CO2 pressure of 10 MPa. The experiments were carried out on water-saturated samples, exposing them to the supercritical CO2 at one end. All samples were jacketed in sleeves to seal them from the high pressure confining medium. The results indicate that cement carbonation front advanced in time, leading to a densification of the material. Extrapolation of the reaction rates to 1-year period indicates a carbonation depth of about 1.38 mm, and about 7.56 mm after 30 years of exposure to CO2-saturated solution. Thermogravimetric analyses, Scanning Electron Microscopy observations and permeability measurements indicate that carbonation of wellbore cement leads to a decrease of the porosity of the material on the reaction front and moreover, has the potential for healing pre-existent fractures and for improving the sealing properties of good-quality cement samples in time, at reservoir conditions.

[1]  Michael A. Celia,et al.  Wellbore integrity analysis of a natural CO2 producer , 2009 .

[2]  Dale P. Bentz,et al.  Modelling cement microstructure: Pixels, particles, and property prediction , 1999 .

[3]  F. Mulders,et al.  The feasibility of effective and safe carbon dioxide storage in the De Lier gas field , 2008 .

[4]  Stefan Bachu,et al.  CO2 storage in geological media: Role, means, status and barriers to deployment , 2008 .

[5]  C. Andrade,et al.  New insights on the use of supercritical carbon dioxide for the accelerated carbonation of cement pastes , 2008 .

[6]  Christian Meyer,et al.  Hydration kinetics modeling of Portland cement considering the effects of curing temperature and applied pressure , 2009 .

[7]  Sam Holloway,et al.  STORAGE OF FOSSIL FUEL-DERIVED CARBON DIOXIDE BENEATH THE SURFACE OF THE EARTH , 2001 .

[8]  J. Carey,et al.  Geochemical effects of CO2 sequestration on fractured wellbore cement at the cement/caprock interface , 2009 .

[9]  O. Koronthályová,et al.  THE CARBONATION OF AUTOCLAVED AERATED CONCRETE , 1997 .

[10]  Barbara Sherwood Lollar,et al.  Solubility trapping in formation water as dominant CO2 sink in natural gas fields , 2009, Nature.

[11]  Dale P. Bentz,et al.  Prediction of Adiabatic Temperature Rise in Conventional and High-Performance Concretes Using a 3-D Microstructural Model , 1998 .

[12]  Adnan Çolak.  A new model for the estimation of compressive strength of Portland cement concrete , 2006 .

[13]  Alan B. Poole,et al.  Effect of carbonation on properties of blended and non-blended cement solidified waste forms , 1997 .

[14]  Karsten Pruess,et al.  Numerical studies of fluid leakage from a geologic disposal reservoir for CO2 show self‐limiting feedback between fluid flow and heat transfer , 2005 .

[15]  B. V. D. Meer,et al.  Carbon Dioxide Storage in Natural Gas Reservoirs , 2005 .

[16]  C. Andrade,et al.  Accelerated carbonation of cement pastes in situ monitored by neutron diffraction , 2008 .

[17]  J. Beaudoin,et al.  Effect of Applied Hydrostatic Stress on the Hydration of Portland Cement and C3S , 2003 .

[18]  P. Nawrocki,et al.  Why Oilwells Leak: Cement Behavior and Long-Term Consequences , 2000 .

[19]  John W. Morse,et al.  Crystallization pressure versus “crack seal” as the mechanism for banded veins , 2001 .

[20]  P. Longuemare,et al.  Analyzing the Risk of Well Plug Failure after Abandonment , 2007 .

[21]  B. Kutchko,et al.  Degradation of well cement by CO2 under geologic sequestration conditions. , 2007, Environmental science & technology.

[22]  C. Hills,et al.  The effect of carbon dioxide on β-dicalcium silicate and Portland cement , 2006 .

[23]  V. Lagneau,et al.  Experimental measurement of portlandite carbonation kinetics with supercritical CO2 , 2009 .

[24]  A. Bentur,et al.  Structural Properties of Calcium Silicate Pastes: II, Effect of Curing Temperature , 1979 .

[25]  Corinne Le Quéré,et al.  Climate Change 2013: The Physical Science Basis , 2013 .

[26]  Karsten Pruess,et al.  Numerical modeling of injection and mineral trapping of CO2 with H2S and SO2 in a Sandstone Formation , 2007 .

[27]  Getting to the Root of Gas Migration , 1996 .

[28]  Veronique Barlet-Gouedard,et al.  Mitigation strategies for the risk of CO2 migration through wellbores , 2006 .

[29]  F. P. Glasser,et al.  The chemistry of blended cements and backfills intended for use in radioactive waste disposal , 1999 .

[30]  John Gale,et al.  Geological storage of CO2: What do we know, where are the gaps and what more needs to be done? , 2004 .

[31]  Veronique Barlet-Gouedard,et al.  Well Technologies for CO2 Geological Storage: CO2-Resistant Cement , 2007 .

[32]  P. Lichtner,et al.  Analysis and performance of oil well cement with 30 years of CO2 exposure from the SACROC Unit, West Texas, USA , 2007 .

[33]  S. Bachu,et al.  Experimental assessment of brine and/or CO2 leakage through well cements at reservoir conditions , 2009 .

[34]  Carlos García,et al.  Microstructural changes induced in Portland cement-based materials due to natural and supercritical carbonation , 2008 .

[35]  L. E. Kukacka,et al.  Carbonation of geothermal grouts — Part 1: CO2 attack at 150°C , 1986 .

[36]  F. Brunet,et al.  Heterogeneous Porosity Distribution in Portland Cement Exposed to CO2-rich Fluids , 2008 .

[37]  Michael A. Celia,et al.  Spatial characterization of the location of potentially leaky wells penetrating a deep saline aquifer in a mature sedimentary basin , 2004 .

[38]  Patrick Dangla,et al.  Investigation of the Carbonation Front Shape on Cementitious Materials: Effects of the Chemical Kinetics , 2007 .

[39]  P. K. Mehta,et al.  Concrete: Microstructure, Properties, and Materials , 2005 .

[40]  G. Rimmelé,et al.  A solution against well cement degradation under CO2 geological storage environment , 2009 .

[41]  Jian-Fu Shao,et al.  Experimental study of mechanical behaviour of cement paste under compressive stress and chemical degradation , 2008 .

[42]  Robert J. Flatt,et al.  Thermodynamics of Crystallization Stresses in DEF , 2008 .

[43]  B. Kutchko,et al.  Rate of CO2 attack on hydrated Class H well cement under geologic sequestration conditions. , 2008, Environmental science & technology.

[44]  G. Saoût,et al.  Chemical structure of cement aged at normal and elevated temperatures and pressures Part I. Class G oilwell cement , 2006 .

[45]  D. Damidot,et al.  Effect of curing conditions on oilwell cement paste behaviour during leaching: Experimental and modelling approaches , 2009 .

[46]  S. Bachu.  Screening and ranking of sedimentary basins for sequestration of CO2 in geological media in response to climate change , 2003 .

[47]  F. Lea.  The chemistry of cement and concrete , 1970 .