Laser crystallisation during pulsed laser deposition of barium titanate thin films at low temperatures

Using a high dielectric material as substitute for SiO x N y in dielectric film capacitors of dynamic memories (DRAM) allows a significantly higher integration density and a reduction of the die size, even with planar capacitors. BaTiO 3 is such a material. A dielectric constant of e r > 1000 has been achieved in thin films, made by pulsed laser deposition (PLD). For applications in microelectronic memories it is necessary to produce crystalline, defect-free and oriented BaTiO 3 thin films at substrate temperatures, Ts < 450 °C. Sintered targets of BaTiO 3 are ablated by KrF excimer laser radiation. The processing gas atmosphere consists of O 2 at pressures of 0.1-50 Pa. The substrate is resitively heated to 360-440 °C and annealed after or during PLD on Pt/Ti/Si multilayer substrates using KrF excimer laser radiation with fluences up to 120 mJ/cm 2 . The temperature distribution in the BaTiO 3 /Pt/Ti/Si multilayers during laser annealing is dynamically modelled and related to the resulting crystal quality and the dielectric properties of the films. With PLD a minimum substrate temperature of 500 °C is necessary to deposit crystalline BaTiO 3 films. Using in situ laser crystallisation crystalline BaTiO 3 films can be deposited at substrate temperatures of T S = 360-440 °C showing a dielectric constant of up to e r = 1200. The ferroelectric and dielectric properties of the films are determined by C-V and P-V impedance measurements and correlated to the chemical and structural properties, as determined by X-ray photoemission spectroscopy, X-ray diffraction, micro Raman spectroscopy and scanning electron microscopy.

[1]  D. Dimos,et al.  Degradation Mechanisms in Ferroelectric and High-Permittivity Perovskites , 1996 .

[2]  M. Obara,et al.  Epitaxial Growth of BaTiO3 Optical Thin Films by Pulsed KrF Laser Deposition and in situ Pulsed Laser Annealing , 1997 .

[3]  G. Hubler,et al.  Pulsed Laser Deposition of Thin Films , 2003, Handbook of Laser Technology and Applications.

[4]  James F. Scott,et al.  The Physics of Ferroelectric Memories , 1998 .

[5]  M. Taga,et al.  One-Shot Excimer Laser Laminar Annealing of SrTiO3 Thin Films in Solidus Phase , 1994 .

[6]  J. Gottmann,et al.  Pulsed laser deposition of ceramic thin films using different laser sources , 1998 .

[7]  C. B. Sawyer,et al.  Rochelle Salt as a Dielectric , 1930 .

[8]  H. Achard,et al.  Integration of Ferroelectric Thin Films for Memory Applications , 1995 .

[9]  H. Ikoma,et al.  Oxynitridation of Silicon Using Helicon-Wave Excited and Inductively-Coupled Nitrogen Plasma , 1997 .

[10]  Thomas Klotzbuecher,et al.  Growth of ceramic thin films by pulsed laser deposition: the role of the kinetic energy of laser-ablated particles , 1998, Other Conferences.

[11]  T. Venkatesan,et al.  Preparation of Y‐Ba‐Cu oxide superconductor thin films using pulsed laser evaporation from high Tc bulk material , 1987 .

[12]  Ernst-Wolfgang Kreutz,et al.  Controlling crystal quality and orientation of pulsed-laser-deposited BaTiO3 thin films by the kinetic energy of the film-forming particles , 2000 .

[13]  W. Pfleging,et al.  Properties and applications of single-component (Al2O3, ZrO2, BN) and multi-component films (ZrO2, Ti) fabricated by pulsed laser deposition , 1994 .

[14]  Zu-liang Liu,et al.  Pulsed excimer (KrF) laser induced crystallization of PbZr0.44Ti0.56O3 amorphous films , 1995 .