Influence of oxygen treatment on electric double-layer capacitance of activated carbon fabrics

Abstract Oxygen treatment at 250°C on polyacrylonitrile-based activated carbon fabric was conducted to explore the influence of carbon–oxygen complexes on the performance of capacitors fabricated with the carbon fabric. Surface analysis showed that most of the oxygen functional groups created from the oxygen treatment were the carbonyl or quinone type. The performance of the capacitors was tested in 1 M H 2 SO 4 , using potential sweep cyclic voltammetry and constant current charge–discharge cycling. It was found that the Faradaic current, the contributor of pseudocapacitance, increased significantly with the extent of oxygen treatment, while the increase in the double-layer capacitance was minor. Due to the treatment the overall specific capacitance showed an increase up to 25% (e.g., from 120 to 150 F g −1 at a current density of 0.5 mA cm −2 ). However, the distributed capacitance effect, the inner resistance and the leakage current were found to increase with the extent of oxidation. It is suggested that due to the local changes of charge density and the increase in redox activity the presence of the carbonyl- or quinone-type functional groups may induce double-layer formation, Faradaic current, surface polarity, and electrolyte decomposition.

[1]  Hardcover,et al.  Carbon: Electrochemical and Physicochemical Properties , 1988 .

[2]  T. Osaka,et al.  An Electrochemical Double Layer Capacitor Using an Activated Carbon Electrode with Gel Electrolyte Binder , 1999 .

[3]  Hang Shi,et al.  Studies of activated carbons used in double-layer capacitors , 1998 .

[4]  F. Carrasco-Marín,et al.  Thermal regeneration of an activated carbon exhausted with different substituted phenols , 1995 .

[5]  R. McCreery,et al.  Control of reactivity at carbon electrode surfaces , 1994 .

[6]  I. Tanahashi,et al.  Effect of concentration of surface acidic functional groups on electric double-layer properties of activated carbon fibers , 1990 .

[7]  R. Weiss,et al.  Chemical interactions between the carbon fibre surface and epoxy resins , 1980 .

[8]  T. Takahagi,et al.  XPS studies by use of the digital difference spectrum technique of functional groups on the surface of carbon fiber , 1984 .

[9]  S. Biniak,et al.  The electrochemical behaviour of carbon fibre electrodes in various electrolytes. Double-layer capacitance , 1995 .

[10]  M. Ishikawa,et al.  Effect of treatment of activated carbon fiber cloth electrodes with cold plasma upon performance of electric double-layer capacitors , 1996 .

[11]  I. Tanahashi,et al.  Electrochemical Characterization of Activated Carbon‐Fiber Cloth Polarizable Electrodes for Electric Double‐Layer Capacitors , 1990 .

[12]  A. Soffer,et al.  Double Layer Capacitance and Charging Rate of Ultramicroporous Carbon Electrodes , 1977 .

[13]  B. Harrison,et al.  Surface studies on graphite: An estimation of the average polarity of the oxygen complexes , 1972 .

[14]  F. Rodríguez-Reinoso,et al.  The use of steam and CO2 as activating agents in the preparation of activated carbons , 1995 .

[15]  R. D. Levie,et al.  On porous electrodes in electrolyte solutions: I. Capacitance effects☆ , 1963 .

[16]  T. Osaka,et al.  Electrochemical modification of active carbon fiber electrode and its application to double-layer capacitor , 1996 .

[17]  W. Stickle,et al.  Handbook of X-Ray Photoelectron Spectroscopy , 1992 .

[18]  B. Conway.  Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications , 1999 .

[19]  L. G. Austin,et al.  The Triangular Voltage Sweep Method for Determining Double‐Layer Capacity of Porous Electrodes Part I . Theory , 1973 .

[20]  P. J. Reucroft,et al.  Vapor adsorption on coal- and wood-based chemically activated carbons: (I) Surface oxidation states and adsorption of H2O , 1999 .

[21]  Takeshi Morimoto,et al.  Electric double-layer capacitor using organic electrolyte , 1996 .

[22]  R. Jenkins,et al.  Characterization of oxygen-containing surface complexes created on a microporous carbon by air and nitric acid treatment , 1993 .

[23]  T. Osaka,et al.  Properties of Electric Double‐Layer Capacitors with Various Polymer Gel Electrolytes , 1997 .

[24]  C. Pittman,et al.  Surface characterization of electrochemically oxidized carbon fibers , 1999 .

[25]  Atsushi Ochi,et al.  Fabrication of high-power electric double-layer capacitors , 1996 .

[26]  Hang Shi,et al.  Activated carbons and double layer capacitance , 1996 .