Evanescent wave optical micro-sensor based on chalcogenide glass

A micro-sensor based on chalcogenide glasses was developed on oxidized silicon substrate for evanescent wave detection in near-infrared spectral domain. This micro-sensor is composed of ridge waveguides based on chalcogenide glass deposited by RF magnetron sputtering associated with a microfluidic system. Optical losses of the ridge waveguide were measured at 1.55 μm and were about of 0.4 dB/cm, a value sufficiently low to enable detection in near-IR spectral range by evanescent waves. Suitability of the sensor for chemical-sensing has been demonstrated by detecting phenylethylamine molecules absorbing specifically at 1.55 μm. The efficiency of the optical sensor was tested as a function of the phenylethylamine concentration in the solution and as a function of the waveguide effective area. The best sensitivity was obtained for the waveguide presenting the smallest effective area of about 1 μm × 1 μm when the attenuation was nearly linear with the phenylethylamine concentration. Experimentally, the resolution was about 0.1 mol L−1 and the sensitivity was 0.87 dB/(mol L−1). A theoretical study was set-up to better control the evanescent wave sensor performance in terms of sensitivity and of resolution of the optical chalcogenide micro-sensor. Finally, selenide micro-waveguides were developed on CaF2 substrates suitable for detection in mid-IR spectral range.

[1]  Kathleen Richardson,et al.  Fabrication and testing of planar chalcogenide waveguide integrated microfluidic sensor. , 2007, Optics express.

[2]  S. Shaji,et al.  NIR vibrational overtone spectra of N-methylaniline, N,N-dimethylaniline and N,N-diethylaniline--a conformational structural analysis using local mode model. , 2004, Spectrochimica acta. Part A, Molecular and biomolecular spectroscopy.

[3]  B. Luther-Davies,et al.  Submicrometer-Thick Low-Loss As $_2$S$_3$ Planar Waveguides for Nonlinear Optical Devices , 2010, IEEE Photonics Technology Letters.

[4]  D. Aspnes.  Optical properties of thin films , 1982 .

[5]  T. Kanamori,et al.  Ultrafast all-optical switching using highly nonlinear chalcogenide glass fiber , 1992, IEEE Photonics Technology Letters.

[6]  J. Adam,et al.  Surface plasmon resonance in chalcogenide glass-based optical system , 2008 .

[7]  Michael J. Schöning,et al.  PLD-prepared cadmium sensors based on chalcogenide glasses—ISFET, LAPS and μISE semiconductor structures , 2006 .

[8]  Florent Colas,et al.  Chalcogenide Glass Optical Waveguides for Infrared Biosensing , 2009, Sensors.

[9]  Martin Richardson,et al.  Development of novel integrated bio/chemical sensor systems using chalcogenide glass materials , 2009 .

[10]  D. Hewak,et al.  Deposition and characterization of germanium sulphide glass planar waveguides. , 2004, Optics express.

[11]  Kathleen Richardson,et al.  Demonstration of chalcogenide glass racetrack microresonators. , 2008, Optics letters.

[12]  S Spälter,et al.  Strong self-phase modulation in planar chalcogenide glass waveguides. , 2002, Optics letters.

[13]  Feng Luan,et al.  High-Resolution Optical Sampling of 640-Gb/s Data Using Four-Wave Mixing in Dispersion-Engineered Highly Nonlinear As$_2$S $_3$ Planar Waveguides , 2010, Journal of Lightwave Technology.

[14]  Joseph Maria Kumar Irudayaraj,et al.  Planar chalcogenide glass waveguides for IR evanescent wave sensors , 2006 .

[15]  Kathleen Richardson,et al.  Planar waveguide-coupled, high-index-contrast, high-Q resonators in chalcogenide glass for sensing. , 2008, Optics letters.

[16]  Robert W. Eason,et al.  Pulsed laser deposition of Ga‐La‐S chalcogenide glass thin film optical waveguides , 1993 .