Erosion behavior of human tooth enamel in citric acid solution

Abstract In vitro erosion behavior of human tooth enamel in citric acid solution (pH=3.2) has been investigated. The surfaces of enamel after different erosion times were analyzed by means of various microscopic examinations. Results showed that no obvious substance loss occurred on the enamel surface at the early stage of erosion, and the erosive lesion was characterized mainly by partial demineralization and decreased microhardness. As the erosion time increased, a honeycomb-like structure appeared on the enamel surface as a result of severe dissolution of the enamel rods. Then substantial erosive substance loss happened. The loss increased almost linearly with the erosion time. Further friction-wear tests by a nano-scratch tester indicated that the erosion of enamel had significant influence on its friction and wear behaviors. Both the friction coefficient and wear loss of eroded enamel showed a strong dependence on erosion time. Understanding of dental erosion behavior would be useful for improving clinical management of tooth wear.

[1]  M. McGurk,et al.  Killey's fractures of the mandible , 1992 .

[2]  G W Marshall,et al.  Mechanical properties of human dental enamel on the nanometre scale. , 2001, Archives of oral biology.

[3]  C. Ganss,et al.  A comparative profilometric in vitro study of the susceptibility of polished and natural human enamel and dentine surfaces to erosive demineralization. , 2000, Archives of oral biology.

[4]  S. Taher,et al.  A sample preparation technique to study the organic phase of tooth enamel under scanning electron microscopy , 2000 .

[5]  Zhongrong Zhou,et al.  Tribology of dental materials: a review , 2008 .

[6]  Zhou Zhongrong,et al.  On the friction and wear behaviour of human tooth enamel and dentin , 2003 .

[7]  K. Jandt,et al.  In vitro demineralization/remineralization cycles at human tooth enamel surfaces investigated by AFM and nanoindentation. , 2004, Journal of colloid and interface science.

[8]  M. Eisenburger,et al.  Erosion and attrition of human enamel in vitro part I: interaction effects. , 2002, Journal of dentistry.

[9]  L H Mair,et al.  Wear in dentistry--current terminology. , 1992, Journal of dentistry.

[10]  Michele E Barbour,et al.  Human enamel dissolution in citric acid as a function of pH in the range 2.30< or =pH< or =6.30--a nanoindentation study. , 2003, European journal of oral sciences.

[11]  M. Bolla,et al.  In vitro action of Bordeaux red wine on the microhardness of human dental enamel. , 2003, Archives of oral biology.

[12]  A. Lussi,et al.  Effect of Amine/Sodium Fluoride Rinsing on Toothbrush Abrasion of Softened Enamel in situ , 2004, Caries Research.

[13]  T. Attin,et al.  In vitro evaluation of different remineralization periods in improving the resistance of previously eroded bovine dentine against tooth-brushing abrasion. , 2001, Archives of oral biology.

[14]  A J Gwinnett,et al.  Structure and composition of enamel. , 1992, Operative dentistry.

[15]  N X West,et al.  Effects of pH and concentration of citric, malic and lactic acids on enamel, in vitro. , 2000, Journal of dentistry.

[16]  T. P. Weihs,et al.  Nanoindentation mapping of the mechanical properties of human molar tooth enamel. , 2002, Archives of oral biology.

[17]  T. Stolarski,et al.  Wear: mechanisms, manifestations and measurement. Report of a workshop. , 1996, Journal of dentistry.

[18]  H. Näveri,et al.  Experimental sports drinks with minimal dental erosion effect. , 1990, Scandinavian journal of dental research.

[19]  N X West,et al.  The protective effects of toothpaste against erosion by orange juice: studies in situ and in vitro. , 2007, Journal of dentistry.