Oxygen permeability and the mechanical and thermal properties of (low‐density polyethylene)/poly (ethylene‐co‐vinyl acetate)/organoclay blown film nanocomposites

Various (low‐density polyethylene)/poly(ethylene‐co‐vinyl acetate) (LDPE/EVA) nanocomposites containing organoclay were prepared by one‐ and two‐step procedures through melt blending. The resultant nanocomposites were then processed via the film blowing method. From the morphological point of view, X‐ray diffraction and optical microscopy studies revealed that although a prevalent intercalated morphology was evident in the absence of EVA, a remarkable increase of organoclay interlayer spacing occurred in the EVA‐containing systems. The advantages of the addition of EVA to the LDPE/organoclay nanocomposites were confirmed in terms of oxygen barrier properties. In other words, the oxygen transmission rates of the LDPE/EVA/organoclay systems were significantly lower than that of the LDPE/organoclay sample. The LDPE/EVA/organoclay films had better mechanical properties than their counterparts lacking the EVA, a result which could be attributed to the improvement of the organoclay reinforcement efficiency in the presence of EVA. Differential scanning calorimetry and thermogravimetric analysis experiments were performed to follow the effects of the EVA and/or organoclay on the thermal properties of LDPE. Finally, the films produced from the two‐step‐procedure compound showed enhanced oxygen barrier properties and mechanical behavior as compared to the properties of the films produced via the one‐step procedure. J. VINYL ADDIT. TECHNOL., 19:132–139, 2013. © 2013 Society of Plastics Engineers

[1]  S. Mazinani,et al.  Effect of stabilizer on the mechanical, morphological and thermal properties of compatibilized high density polyethylene/ethylene vinyl acetate copolymer/organoclay nanocomposites , 2012 .

[2]  I. Alemzadeh,et al.  Studies on the oxygen barrier and mechanical properties of low density polyethylene/organoclay nanocomposite films in the presence of ethylene vinyl acetate copolymer as a new type of compatibilizer , 2011 .

[3]  A. Shojaei,et al.  Rheological and mechanical characteristics of low density polyethylene/ethylene‐vinyl acetate/organoclay nanocomposites , 2010 .

[4]  H. Azizi,et al.  An investigation on the correlation between rheology and morphology of nanocomposite foams based on low-density polyethylene and ethylene vinyl acetate blends , 2010 .

[5]  M. Andersson,et al.  Solution-Processable Organic Molecule with Triphenylamine Core and Two Benzothiadiazole-Thiophene Arms for Photovoltaic Application , 2010 .

[6]  S. Ramazani,et al.  Investigation of oxygen barrier properties of organoclay/HDPE/EVA nanocomposite films prepared using a two-step solution method , 2009 .

[7]  N. Mohammadi,et al.  Practical work of crack growth and environmental stress cracking resistance of semicrystalline polymers , 2008 .

[8]  Q. Zhang,et al.  Molecular weight dependence of hybrid shish kebab structure in injection molded bar of polyethylene/inorganic whisker composites. , 2008, The journal of physical chemistry. B.

[9]  M. C. Branciforti,et al.  Rheological, mechanical and transport properties of blown films of high density polyethylene nanocomposites , 2008 .

[10]  A. Shchegolikhin,et al.  Thermal properties of polyethylene/montmorillonite nanocomposites prepared by intercalative polymerization , 2008 .

[11]  A. Galeski,et al.  Low density polyethylene–montmorillonite nanocomposites for film blowing , 2008 .

[12]  Xudong Shi,et al.  Preparation and characterization of poly(propylene carbonate)/montmorillonite nanocomposites by solution intercalation , 2007 .

[13]  S. Y. Zhang,et al.  Effects of raw fiber materials, fiber content, and coupling agent content on selected properties of polyethylene/wood fiber composites , 2007 .

[14]  C. Macosko,et al.  Intercalated linear low density polyethylene (LLDPE)/clay nanocomposites prepared with oxidized polyethylene as a new type compatibilizer: Structural, mechanical and barrier properties , 2007 .

[15]  Dustin W. Janes,et al.  Mechanical and oxygen barrier properties of organoclay‐polyethylene nanocomposite films , 2007 .

[16]  R. K. Shah,et al.  Blown films of nanocomposites prepared from low density polyethylene and a sodium ionomer of poly(ethylene-co-methacrylic acid) , 2006 .

[17]  E. Giannelis,et al.  Controlling the miscibility of polyethylene/layered silicate nanocomposites by altering the polymer/surface interactions , 2005 .

[18]  Mingshu Yang,et al.  Mechanical, thermal and flammability properties of polyethylene/clay nanocomposites , 2005 .

[19]  D. R. Paul,et al.  Nanocomposites formed from linear low density polyethylene and organoclays , 2004 .

[20]  R. Mülhaupt,et al.  Synthesis and thermal behaviour of layered silicate-EVA nanocomposites , 2001 .