Synthesis and characterization of polymer-CDS nanocomposites

The synthesis and characterization of polymer composite system containing quantum-confined CdS nanoparticles entrapped in an Acrylic acid-hydroxypropyl acrylate copolymer (AC-HAC) is reported. The results showed that the CdS nanoparticles had an average particles size of 3.6nm in diameter and the band edge (λedge) of the entrapped CdS nanoparticles was 391nm. The colloidal solution exhibited a band-edge emission peak around 420nm due to the surface passivation. In order to observe the stability of the colloidal solution, it was exposed to air at room temperature for certain days. It was found that the colloidal solution remained as a colloidal solution of CdS nanoparticles even after 65 days exposition.

Gaorong Han | Jianxi Yao | Gaoling Zhao

[1] S. A. Bilmes,et al. Parameters Involved in the Sol-Gel Transition of Titania in Reverse Micelles , 1998 .

[2] Chunhua Yan,et al. Synthesis of CdS nanocrystal within copolymer , 2000 .

[3] Louis E. Brus,et al. Size effects in the excited electronic states of small colloidal CdS crystallites , 1984 .

[4] D. Kaplan,et al. The enzymatic synthesis of thiol-containing polymers to prepare polymer-CdS nanocomposites , 1997 .

[5] J. Boilot,et al. 3D morphology of II VI semiconductor nanocrystals grown in inverted micelles , 1999 .

[6] Bai Yang,et al. Assembly of modified CdS particles/cationic polymer based on electrostatic interactions , 1996 .

[7] D. Sarma,et al. Size-Selected Zinc Sulfide Nanocrystallites: Synthesis, Structure, and Optical Studies , 2000 .