High throughput laser texturing of super-hydrophobic surfaces on steel

Super-hydrophobic surfaces are nowadays of primary interest in several application fields, as for de-icing devices in the automotive and aerospace industries. In this context, laser surface texturing has widely demonstrated to be an easy one-step method to produce super-hydrophobic surfaces on several materials. In this work, a high average power (up to 40W), high repetition-rate (up to 1MHz), femtosecond infrared laser was employed to produce super-hydrophobic surfaces on 316L steel. The set of process and laser parameters for which the super-hydrophobic behavior is optimized, was obtained by varying the laser energy and repetition rate. The morphology of the textured surfaces was firstly analyzed by SEM and confocal microscope analyses. The contact angle was measured over time in order to investigate the effect of air environment on the hydrophobic properties and define the period of time necessary for the super-hydrophobic properties to stabilize. An investigation on the effect of after-processing cleaning solvents on the CA evolution was carried to assess the influence of the after-processing sample handling on the CA evaluation. Results show that the highest values of contact angle, that is the best hydrophobic behavior, are obtained at high repetition rate and low energy, this way opening up a promising scenario in terms of upscaling for reducing the overall process takt-time.

[1]  Rainer Kling,et al.  Extending ultra-short pulse laser texturing over large area , 2016 .

[2]  Seong J. Cho,et al.  One-step fabrication of superhydrophobic hierarchical structures by femtosecond laser ablation , 2014 .

[3]  Peter Englezos,et al.  Patterned superhydrophobic metallic surfaces. , 2009, Langmuir : the ACS journal of surfaces and colloids.

[4]  Eric Audouard,et al.  Time dependency of the hydrophilicity and hydrophobicity of metallic alloys subjected to femtosecond laser irradiations , 2013 .

[5]  C. Donnet,et al.  Influence of femtosecond laser marking on the corrosion resistance of stainless steels , 2006 .

[6]  Costas Fotakis,et al.  From ripples to spikes: A hydrodynamical mechanism to interpret femtosecond laser-induced self-assembled structures , 2015, 1505.04381.

[7]  S. Kamalb,et al.  Nanopatterned Metallic Surfaces: Their Wettability and Impact on Ice Friction , 2011 .

[8]  L. Boinovich,et al.  Hydrophobic materials and coatings: principles of design, properties and applications , 2008 .

[9]  R. Pogreb,et al.  Micrometrically scaled textured metallic hydrophobic interfaces validate the Cassie-Baxter wetting hypothesis. , 2006, Journal of colloid and interface science.

[10]  H. Zheng,et al.  Laser micro structuring on a Si substrate for improving surface hydrophobicity , 2009 .

[11]  J. Joines,et al.  Literature review on superhydrophobic self‐cleaning surfaces produced by electrospinning , 2012 .

[12]  Edward Bormashenko,et al.  The rigorous derivation of Young, Cassie–Baxter and Wenzel equations and the analysis of the contact angle hysteresis phenomenon , 2008 .

[13]  E. Loth,et al.  Ice Adhesion Performance of Superhydrophobic Coatings in Aerospace Icing Conditions , 2015 .

[14]  A. Vorobyev,et al.  Multifunctional surfaces produced by femtosecond laser pulses , 2015 .

[15]  T. Glynn,et al.  The effect of damage accumulation behaviour on ablation thresholds and damage morphology in ultrafast laser micro-machining of common metals in air , 2004 .