Effects of cryogenic cooling on surface layer alterations in machining of AISI 52100 steels

Abstract Microstructural phase transformations, commonly known as white layer formation in hard turned steel components, have in recent times become an interesting research topic in machining as they are related to the surface integrity and functional performance of components. Three main theories have been proposed to justify the mechanisms of white layer formation: (1) rapid heating and quenching; (2) severe plastic deformation; and (3) surface reaction with the environment. Coolant application also affects the surface microstructural alterations resulting from machining operations, which have a significant influence on product performance and life. The present work aims at understanding the effects of cryogenic coolant application on the machined surface alterations during machining of hardened AISI 52100 bearing steel. Experiments were performed under dry and cryogenic cooling conditions using cubic boron nitride tool inserts with varying initial work material hardness, tool shape, cutting speed and feedrate. Optical and scanning electron microscopes (SEM) were used to analyse the affected layer in the machined subsurface, while X-ray diffraction technique was utilised to investigate the microstructural phase composition. The experimental results prove that the microstructural phase changes are heavily influenced by the cutting process parameters and the use of cryogenic cooling, in some cases leading to the total removal of martensite.

[1]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[2]  A. Torrance,et al.  Surface transformations in scuffing , 1974 .

[3]  Permanent Deformation of Bearing Raceway Surfaces , 1976 .

[4]  B. J. Griffiths,et al.  White Layer Formations at Machined Surfaces and Their Relationship to White Layer Formations at Worn Surfaces , 1985 .

[5]  W. Konig,et al.  Machining hard materials with geometrically defined cutting edges , 1990 .

[6]  S. Nutt,et al.  Adiabatic shear band formation during dynamic torsional deformation of an HY-100 steel , 1993 .

[7]  F. Hengerer,et al.  Through-Hardening or Case-Hardening for Tapered Roller Bearings? , 1993 .

[8]  G. Krauss,et al.  Elastic limit and microplastic response of hardened steels , 1993, Metallurgical and Materials Transactions A.

[9]  W. Konig,et al.  Top-quality components not only by grinding , 1994 .

[10]  J. Duffy,et al.  Shear band formation in 4340 steel: A TEM study☆ , 1994 .

[11]  Structural alterations in the surface layer during hard machining , 1997 .

[12]  Wanci Shen,et al.  Microstructures of surface white layer and internal white adiabatic shear band , 1997 .

[13]  Christopher J. Evans,et al.  White Layers and Thermal Modeling of Hard Turned Surfaces , 1997, Manufacturing Science and Engineering: Volume 2.

[14]  Jiajun Liu,et al.  Tribo-metallographic behavior of high carbon steels in dry sliding: III. Dynamic microstructural changes and wear , 1999 .

[15]  Jeffrey D. Thiele,et al.  Residual Stress and Sub-Surface Flow in Finish Hard Turned AISI 4340 and 52100 Steels: A Comparative Study , 1999, Manufacturing Science and Engineering.

[16]  Fukuo Hashimoto,et al.  Surface Integrity Generated by Precision Hard Turning , 1999 .

[17]  I. Jawahir,et al.  Tool-wear mechanisms in hard turning with polycrystalline cubic boron nitride tools , 2001 .

[18]  Werner Österle,et al.  Investigation of white etching layers on rails by optical microscopy, electron microscopy, X-ray and synchrotron X-ray diffraction , 2001 .

[19]  Kevin Barraclough,et al.  I and i , 2001, BMJ : British Medical Journal.

[20]  Srinivasan Chandrasekar,et al.  Formation of white layers in steels by machining and their characteristics , 2002 .

[21]  Gerry Byrne,et al.  TEM study on the surface white layer in two turned hardened steels , 2002 .

[22]  R. Ghosh,et al.  Investigation of White Layers Formed in Conventional and Cryogenic Hard Turning of Steels , 2003 .

[23]  Shreyes N. Melkote,et al.  Analysis of white layers formed in hard turning of AISI 52100 steel , 2005 .

[24]  Ericka Stricklin-Parker,et al.  Ann , 2005 .

[25]  Ekkard Brinksmeier,et al.  Capability Profile of Hard Cutting and Grinding Processes , 2005 .

[26]  Gérard Poulachon,et al.  An experimental investigation of work material microstructure effects on white layer formation in PCBN hard turning , 2005 .

[27]  Yuebin Guo,et al.  The influence of machining induced residual stress and phase transformation on the measurement of subsurface mechanical behavior using nanoindentation , 2006 .

[28]  Nathaniel Pappas.  Calculating Retained Austenite in Steel Post Magnetic Processing Using X-Ray Diffraction , 2007 .

[29]  Jia Li,et al.  A microstructural investigation of the surface of a drilled hole in carbon steels , 2007 .

[30]  Shreyes N. Melkote,et al.  White layer formation due to phase transformation in orthogonal machining of AISI 1045 annealed steel , 2008 .

[31]  Shreyes N. Melkote,et al.  Modeling of white layer formation under thermally dominant conditions in orthogonal machining of hardened AISI 52100 steel , 2008 .

[32]  E. S. Perdahcıoğlu,et al.  Mechanically induced martensitic transformation as a stress-driven process , 2009 .

[33]  Liang Li,et al.  Investigation on White Layer Formation in PCBN Hard Turning GCr15 , 2010 .

[34]  J. Zhang,et al.  An experimental investigation of affected layers formed in grinding of AISI 52100 steel , 2011 .

[35]  W. Marsden.  I and J , 2012 .

[36]  H. K. D. H. Bhadeshia,et al.  Steels for bearings , 2012 .