Acoustic emission monitoring of a wind turbine blade during a fatigue test
暂无分享,去创建一个
A fatigue test of a wind turbine blade was conducted at the National Renewable Energy Laboratory in the fall of 1994. Acoustic emission monitoring of the test was performed, starting with the second loading level. The acoustic emission data indicated that this load exceeded the strength of the blade. From the first cycle at the new load, an oil can type of deformation occurred in two areas of the upper skin of the blade. One of these was near the blade root and the other was about the middle of the tested portion of the blade. The emission monitoring indicated that no damage was taking place in the area near the root, but in the deforming area near the middle of the blade, damage occurred from the first cycles at the higher load. The test was stopped after approximately one day and the blade was declared destroyed, although no gross damage had occurred. Several weeks later the test was resumed, to be continued until gross damage occurred. The upper skin tore approximately one half hour after the cycling was restarted.
[1] R. C. Mcmaster. Nondestructive testing handbook , 1959 .
[2] H. J. Sutherland,et al. The application of non-destructive techniques to the testing of a wind turbine blade , 1994 .
[3] A. G. Beattie,et al. Acoustic emission, principles and instrumentation , 1983 .