Characterization of Acacia mangium wood based activated carbons prepared in the presence of basic activating agents

The aim of this study was to observe the effects of alkaline activating agents on the characteristics, composition, and surface morphology of the designed activated carbons. Activated carbons were prepared by pyrolysis of Acacia mangium wood in the presence of two basic activating agents (calcium oxide and potassium hydroxide). The extent of impregnation ratio of precursor to activating agents was fixed at 2:1(w/w). Prior to pyrolysis, 24 hours soaking was conducted at 348 K. Activation was carried out in a stainless steel capped graphite crucible at 773 K for 2 hours in the absence of purge gas. The burn-off percentage was found to be 70.27±0.93% for CaO activated carbon (COAC) and 73.30±0.20% for KOH activated carbon (PHAC). The activating agents had a strong influence on the surface functional groups as well as elemental composition of these activated carbons. Characterization of the activated carbon obtained was performed with field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDX), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and nitrogen adsorption as Brunauer, Emmett and Teller (BET) and Dubinin-Radushkevich (DR) isotherms.

[1]  P. Pavasant,et al.  Activated carbon from Eucalyptus camaldulensis Dehn bark using phosphoric acid activation. , 2008, Bioresource technology.

[2]  Marit Jagtoyen,et al.  Activated carbons from yellow poplar and white oak by H3PO4 activation , 1998 .

[3]  P. Williams,et al.  Thermal processing of biomass natural fibre wastes by pyrolysis , 2004 .

[4]  François Béguin,et al.  Surface functionality and porosity of activated carbons obtained from chemical activation of wood , 2000 .

[5]  P. J. Reucroft,et al.  Vapor adsorption on coal- and wood-based chemically activated carbons (II) adsorption of organic vapors , 1999 .

[6]  K. Sing,et al.  Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity (Provisional) , 1982 .

[7]  R. Pugmire,et al.  Evolution of carbon structure in chemically activated wood , 1995 .

[8]  S. Alam,et al.  Adsorption of acid blue 1 on activated carbon produced from the wood of Ailanthus altissima , 2009 .

[9]  M. Rafatullah,et al.  Kinetics for the Removal of Paraquat Dichloride from Aqueous Solution by Activated Date (Phoenix dactylifera) Stone Carbon , 2010 .

[10]  C. Faur,et al.  Production of fibrous activated carbons from natural cellulose (jute, coconut) fibers for water treatment applications , 2006 .

[11]  J. Tascón,et al.  Synthetic carbons activated with phosphoric acid: I. Surface chemistry and ion binding properties , 2002 .

[12]  L. Giraldo,et al.  Study of activated carbons by pyrolysis of cassava peel in the presence of chloride zinc , 2010 .

[13]  Norashid Aziz,et al.  Isotherms, kinetics and thermodynamics of acid dye adsorption on activated palm ash , 2007 .