论文信息 - Hydride morphology and striation formation during delayed hydride cracking in Zr-2.5% Nb - 字舞流文

Hydride morphology and striation formation during delayed hydride cracking in Zr-2.5% Nb

Y. Ma | M. Jovanović | G. Shek | D. Li | R. Eadie | H. Seahra

[1] S. Shi,et al. Criteria for fracture initiation at hydrides in zirconium alloys I. Sharp crack tip , 1994 .

[2] S. Macewen,et al. The influence of prior deformation on hydride precipitation in zircaloy , 1992 .

[3] M. Puls. Effects of crack tip stress states and hydride-matrix interaction stresses on delayed hydride cracking , 1990 .

[4] R. Eadie,et al. The effect of hydride precipitation on the stresses near the crack tip in a delayed hydride crack in zirconium-2.5% niobium , 1989 .

[5] R. Smith,et al. Modelling Delayed Hydride Cracking in Zirconium Alloys , 1988 .

[6] N. Moody,et al. The Effect of Stress State on Internal Hydrogen-Induced Crack Growth in Ti-6AI-6V-2Sn , 1982 .

[7] C. E. Coleman,et al. CANDU-PHW Pressure Tubes: Their Manufacture, Inspection, and Properties , 1982 .

[8] K. Tangri,et al. Metallographic observations on the developing hydride morphology at the crack tip during hydrogen induced delayed cracking in a Zr-2.5 Nb alloy , 1982 .

[9] N. Moody,et al. Hydrogen-induced slow crack growth in Ti-6Al-6V-2Sn , 1980 .

[10] M. P. Puls,et al. The effects of stress, temperature and hydrogen content on hydride-induced crack growth in Zr-2.5 Pct Nb , 1979 .

[11] L. A. Simpson,et al. Mechanisms of hydrogen induced delayed cracking in hydride forming materials , 1977 .

[12] K. Nuttall,et al. Metallographic observations of the interaction of hydride, stress and crack growth at 600°K in a Zr-2.5% Nb alloy , 1976 .