Reaction Control System Thruster Cracking Consultation: NASA Engineering and Safety Center (NESC) Materials Super Problem Resolution Team (SPRT) Findings

The shuttle orbiter s reaction control system (RCS) primary thruster serial number 120 was found to contain cracks in the counter bores and relief radius after a chamber repair and rejuvenation was performed in April 2004. Relief radius cracking had been observed in the 1970s and 1980s in seven thrusters prior to flight; however, counter bore cracking had never been seen previously in RCS thrusters. Members of the Materials Super Problem Resolution Team (SPRT) of the NASA Engineering and Safety Center (NESC) conducted a detailed review of the relevant literature and of the documentation from the previous RCS thruster failure analyses. It was concluded that the previous failure analyses lacked sufficient documentation to support the conclusions that stress corrosion cracking or hot-salt cracking was the root cause of the thruster cracking and lacked reliable inspection controls to prevent cracked thrusters from entering the fleet. The NESC team identified and performed new materials characterization and mechanical tests. It was determined that the thruster intergranular cracking was due to hydrogen embrittlement and that the cracking was produced during manufacturing as a result of processing the thrusters with fluoride-containing acids. Testing and characterization demonstrated that appreciable environmental crack propagation does not occur after manufacturing.

[1]  Reiner Kirchheim,et al.  HYDROGEN ADSORPTION AT CRACKS IN Fe, Nb AND Pd , 1982 .

[2]  K. Salama,et al.  Effects of hydrogen on near-threshold crack propagation in niobium , 1983 .

[3]  E. Gileadi,et al.  Interfacial electrochemistry: An experimental approach , 1975 .

[4]  P. McIntyre,et al.  The low-temperature embrittlement of niobium and vanadium by both dissolved and precipitated hydrogen , 1973 .

[5]  R. N. Parkins Stress Corrosion Cracking , 1964 .

[6]  H. K. Birnbaum,et al.  Low temperature hydrogen embrittlement of niobium II—Microscopic observations☆ , 1977 .

[7]  Russel H. Jones,et al.  Stress-corrosion cracking , 1992 .

[8]  Ronald W. Armstrong,et al.  Low energy cleavage fracture associated with the hydrogen embrittlement of refractory metal alloys , 1989 .

[9]  Noboru Yoshikawa,et al.  An in situ observation of hydrogen induced crack in niobium , 1987 .

[10]  T. E. Scott,et al.  The effects of interstitials and hydrogen-interstitial interactions on low temperature hardening and embrittlement in V, Nb, and Ta , 1986 .

[11]  H. K. Birnbaum,et al.  Hydrogen embrittlement of Nb I—Macroscopic behavior at low temperatures☆ , 1977 .

[12]  R. P. Wei,et al.  On the dilatation field in front of a moving crack , 1972 .

[13]  R. H. Van Stone,et al.  Direct Current Electrical Potential Measurement of the Growth of Small Cracks , 1992 .

[14]  H. K. Birnbaum,et al.  Hydrogen embrittlement of niobium III: high-temperature behavior. Technical report. [125 to 500 C, H/Nb < or = 0. 9] , 1977 .

[15]  R. Winston Revie,et al.  Mechanistic Aspects of Stress Corrosion Crack Initiation and Early Propagation , 1999 .

[16]  M. W. Mahoney,et al.  The Effect of Oxygen, Nitrogen, and Hydrogen on the Mechanical Properties of Cb-752 , 1974 .

[17]  T. E. Scott,et al.  Effects of nitrogen on the mechanical behavior of hydrogenated V, Nb, and Ta , 1986 .

[18]  M. K. Bahl,et al.  ESCA studies of some niobium compounds , 1974 .

[19]  W. T. Chandler,et al.  Effect of Water Vapor/Hydrogen Environments on Niobium, B-66 Niobium Alloy, Tantalum, and Ta-10W Alloy , 1991 .

[20]  William R. Jones The properties of perfluoropolyethers used for space applications , 1993 .

[21]  G. Pressouyre,et al.  Trap theory of Hydrogen embrittlement , 1980 .

[22]  K. Salama,et al.  Hydrogen embrittlement in single- and poly-crystal niobium , 1981 .