Studies on thermal and mechanical properties of polyimide-clay nanocomposites

Abstract Nanocomposites from polyimide and clay were prepared aiming at finding a promising method for enhancing particularly the tensile modulus of polyimide films. Polyimide–clay hybrids were prepared by blending of poly(amide acid) and organically modified-montmorillonite (OMMT) as a type of layered clays. Poly(amide acid) was prepared from the reaction of 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and p-phenylenediamine (PDA). Also, poly(amide acid) from pyromellitic dianhydride (PMDA) and 4,4′-oxydianiline (ODA) was prepared for comparison. OMMT was prepared by surface treatment of montmorillonite (MMT) with ammonium chloride salt of 12-aminolauric acid. XRD indicated that the OMMT layers were exfoliated and dispersed into the poly(amide acid) and polyimide film. Tensile properties measurements of polyimide–clay hybrids indicated that the addition of 2 wt.% of OMMT increased the tensile modulus of BPDA/PDA polyimide up to 12.1 GPa, which is ca. 42% higher than the pristine BPDA/PDA polyimide. Tensile modulus of PMDA/ODA also increased up to 6.2 GPa, which is ca. 110% higher than that of the original PMDA/ODA polyimide. The glass transition temperatures of the BPDA/PDA nanocomposites were higher than that of the original polyimide. The thermal expansion coefficient of the BPDA/PDA polyimide film decreased by the inclusion of clay. Isothermal and dynamic TGA showed that the both types of polyimide nanocomposites have higher decomposition temperatures in comparison with the original polyimides.

[1]  K. Wei,et al.  Enhancement of imidization of poly(amic acid) through forming poly(amic acid)/organoclay nanocomposites , 1999 .

[2]  B. Jang.  Control of interfacial adhesion in continuous carbon and kevlar fiber reinforced polymer composites , 1992 .

[3]  Stephen Z. D. Cheng,et al.  Dianhydride architectural effects on the relaxation behaviors and thermal and optical properties of organo-soluble aromatic polyimide films , 1999 .

[4]  T. Agag,et al.  Polybenzoxazine–montmorillonite hybrid nanocomposites: synthesis and characterization , 2000 .

[5]  Thomas J. Pinnavaia,et al.  Mechanism of Clay Tactoid Exfoliation in Epoxy-Clay Nanocomposites , 1995 .

[6]  J. E. Mark,et al.  Nanocomposites Prepared by Threading Polymer Chains through Zeolites, Mesoporous Silica, or Silica Nanotubes , 1996 .

[7]  J. E. Sohn.  Improved Matrix-Filler Adhesion , 1985 .

[8]  V. Mehrotra,et al.  Nanometer scale multilayers of electroactive polymers: intercalation of polypyrrole in mica-type silicates , 1992 .

[9]  N. Takahashi,et al.  High modulus polyimide/polyimide molecular composite films that utilize acetylene unit as a crosslink site , 1994 .

[10]  M. Inagaki,et al.  Carbonization and graphitization of polyimide films : Effect of size of leaving group at imidization , 1998 .

[11]  A. Okada,et al.  Synthesis and properties of polyimide-clay hybrid films , 1997 .

[12]  Emmanuel P. Giannelis,et al.  Polymer Layered Silicate Nanocomposites , 1996 .

[13]  Bruce M. Novak,et al.  Hybrid nanocomposite materials―between inorganic glasses and organic polymers , 1993 .

[14]  T. Kurauchi,et al.  Synthesis and properties of polyimide–clay hybrid , 1993 .

[15]  S. Qutubuddin,et al.  Synthesis and Characterization of ‘Epoxyphilic’ Montmorillonites , 1994, Clay Minerals.

[16]  T. Kurauchi,et al.  Swelling behavior of montmorillonite cation exchanged for ω-amino acids by ∊-caprolactam , 1993 .

[17]  Thomas J. Pinnavaia,et al.  On the Nature of Polyimide-Clay Hybrid Composites , 1994 .

[18]  E. Giannelis,et al.  Synthesis and properties of new poly(dimethylsiloxane) nanocomposites , 1995 .

[19]  M. Inagaki,et al.  Carbonization and graphitization of BPDA/PDA polyimide films: effect of structure of polyimide precursor , 1999 .

[20]  Jie Yin,et al.  Preparation and properties of hybrids of organo-soluble polyimide and montmorillonite with various chemical surface modification methods , 1999 .