SummaryThe aim of this study was to ascertain whether the use of liquid acrylic resin or NeoCryl XK-53 acrylic emulsion or etching of the bone surface with phosphoric acid or the application of both these methods would improve the bonding of CMW bone cement or Concise and Silar composite resin to bone. The test materials were applied to fresh cortical bovine bone. Their bonding capacity was measured by the Instron Universal Testing Machine. The surfaces of the test materials and the bone surfaces were examined by means of optic microscope or scanning electron microscope. The bonding strength of the bone cement and composite resins as such were found to be of the same magnitude. A three- to five-fold improvement was obtained with liquid acrylic intermediary material. Acid etching impaired the bonding.ZusammenfassungDas Ziel dieser Untersuchung war, herauszufinden, ob der Gebrauch von füissigen zusammengesetzten Acryl-Harzen oder von NeoCryl XK-53 Acryl-Emulsionen oder von Ätzung der Knochenoberfläche mit Phosphorsäure oder die Anwendung von beiden Methoden die Fixierung des Knochenzements CMW oder der zusammengesetzten Harze Concise und Silar verbessern wurde. Die untersuchten Materialien wurden an frischen corticalen Rinderknochen angebracht. Die Fixierungskapazität wurde mit dem Universal-Gerät Instron fur Material-tests gemessen. Die Oberflächen des Testmaterials und des Knochens wurden mit Hilfe eines optischen oder Raster-Elektronenmikroskops untersucht. Die Resultate bewiesen, daß sich der Knochenzement wie die zusammengesetzten Harze an dem Knochen fixierten. Das als Zwischenstoff verwendete flüssige Acryl verbesserte die Haftfahigkeit um das 3–5fache. Die Ätzungen mit Säure verschlechterte die Häftfahigkeit.