Quantitative SHINERS analysis of temporal changes in the passive layer at a gold electrode surface in a thiosulfate solution.

Shell-isolated gold nanoparticles (SHINs) were employed to record shell-isolated nanoparticle-enhanced Raman spectra (SHINERS) of a passive layer formed at a gold surface during gold leaching from thiosulfate solutions. The (3-aminopropyl)triethoxysilane (APTES) and a sodium silicate solution were used to coat gold nanoparticles with a protective silica layer. This protective silica layer prevented interactions between the thiosulfate electrolyte and the gold core of the SHINs when the SHINs-modified gold electrode was immersed into the thiosulfate lixiviant. The SHINERS spectra of the passive layer, formed from thiosulfate decomposition, contained bands indicative of hydrolyzed APTES. We have demonstrated how to exploit the presence of these APTES bands as an internal standard to compensate for fluctuations of the surface enhancement of the electric field of the photon. We have also developed a procedure that allows for removal of the interfering APTES bands from the SHINERS spectra. These methodological advancements have enabled us to identify the species forming the passive layer and to determine that the formation of elemental sulfur, cyclo-S8, and polymeric sulfur chains is responsible for inhibition of gold dissolution in oxygen rich thiosulfate solutions.

[1]  J. Vázquez,et al.  Electrochemical behaviour of aqueous SO2 at polycrystalline gold electrodes in acidic media: a voltammetric and in situ vibrational study: Part 1. Reduction of SO2: deposition of monomeric and polymeric sulphur , 2000 .

[2]  W. M. Heston,et al.  The Solubility of Amorphous Silica in Water , 1954 .

[3]  J. Lipkowski,et al.  “Surface-enhanced Raman spectroscopy studies of the passive layer formation in gold leaching from thiosulfate solutions in the presence of cupric ion” , 2014, Journal of Solid State Electrochemistry.

[4]  J. Lipkowski,et al.  Application of PM-IRRAS to study thin films on industrial and environmental samples , 2013, Analytical and Bioanalytical Chemistry.

[5]  J. Lipkowski,et al.  SERS and electrochemical studies of the gold–electrolyte interface under thiosulfate based leaching conditions , 2013 .

[6]  Douglas J. Moffatt,et al.  Fourier Self-Deconvolution: A Method for Resolving Intrinsically Overlapped Bands , 1981 .

[7]  C. Brosseau,et al.  Electrochemical SERS study of a biomimetic membrane supported at a nanocavity patterned Ag electrode , 2013 .

[8]  G. Senanayake.  The role of ligands and oxidants in thiosulfate leaching of gold , 2005 .

[9]  J. Lipkowski,et al.  A SERS characterization of the stability of polythionates at the gold–electrolyte interface , 2015 .

[10]  R. Woods,et al.  A Spectroelectrochemical Study of Surface Species Formed in the Gold/Thiosulfate System , 2006 .

[11]  M. Moskovits.  Surface‐enhanced Raman spectroscopy: a brief retrospective , 2005 .

[12]  R. Woods,et al.  A SERS spectroelectrochemical investigation of the interaction of sulfide species with gold surfaces , 2008 .

[13]  G. Senanayake.  Gold leaching by thiosulphate solutions: a critical review on copper(II)–thiosulphate–oxygen interactions , 2005 .

[14]  Zhong Lin Wang,et al.  Shell-isolated nanoparticle-enhanced Raman spectroscopy , 2010, Nature.

[15]  Lon A. Porter,et al.  Gold and Silver Nanoparticles Functionalized by the Adsorption of Dialkyl Disulfides. , 1998, Langmuir : the ACS journal of surfaces and colloids.

[16]  J. Lipkowski,et al.  Electrochemical methods to measure gold leaching current in an alkaline thiosulfate solution , 2011 .

[17]  De‐Yin Wu,et al.  Extraordinary enhancement of Raman scattering from pyridine on single crystal Au and Pt electrodes by shell-isolated Au nanoparticles. , 2011, Journal of the American Chemical Society.

[18]  Zhilin Yang,et al.  SHINERS and plasmonic properties of Au Core SiO2 shell nanoparticles with optimal core size and shell thickness , 2013 .

[19]  Z. Gabelica.  Structural study of solid inorganic thiosulfates by infrared and Raman spectroscopy , 1980 .

[20]  I. Noda.  Generalized Two-Dimensional Correlation Method Applicable to Infrared, Raman, and other Types of Spectroscopy , 1993 .

[21]  P. Breuer,et al.  The reduction of copper(II) and the oxidation of thiosulfate and oxysulfur anions in gold leaching solutions , 2003 .

[22]  R. Woods,et al.  Identification of surface species that inhibit and passivate thiosulfate leaching of gold , 2008 .

[23]  A. Gewirth,et al.  Investigating the effect of aging on transpassive behavior of Ni-based alloys in sulfuric acid with shell-isolated nanoparticle enhanced Raman spectroscopy (SHINERS) , 2013 .

[24]  G. Senanayake.  Role of copper(II), carbonate and sulphite in gold leaching and thiosulphate degradation by oxygenated alkaline non-ammoniacal solutions , 2005 .

[25]  Jian-feng Li,et al.  In situ SHINERS at electrochemical single-crystal electrode/electrolyte interfaces: tuning preparation strategies and selected applications. , 2013, ACS nano.

[26]  Yong Ding,et al.  Surface analysis using shell-isolated nanoparticle-enhanced Raman spectroscopy , 2012, Nature Protocols.

[27]  A. E. Dowrey,et al.  Generalized Two-Dimensional Correlation Spectroscopy , 2000 .

[28]  David M. Muir,et al.  Thiosulfate leaching of gold—A review , 2001 .

[29]  Paul A. Kohl,et al.  Electrochemical Study of the Gold Thiosulfate Reduction , 1997 .

[30]  M. J. Weaver,et al.  Adsorption and electrooxidative pathways for sulfide on gold as probed by real-time surface-enhanced Raman spectroscopy , 1992 .

[31]  S. Yannopoulos,et al.  Probing the sulfur polymerization transition in situ with Raman spectroscopy , 2003 .

[32]  M. Leskovac,et al.  Density functional study of gamma- aminopropyltriethoxysilane , 2006 .

[33]  Yukihiro Ozaki,et al.  Two-Dimensional Correlation Spectroscopy - Applications in Vibrational and Optical Spectroscopy: Noda/Two-Dimensional Correlation Spectroscopy - Applications in Vibrational and Optical Spectroscopy , 2005 .

[34]  G. A. Newman,et al.  Raman spectroscopy of thiosulphates , 1993 .

[35]  H. F. Shurvell,et al.  Surface-enhanced Raman scattering of inorganic oxoanions , 1997 .

[36]  J. Koenig,et al.  The structure of aminofunctional silane coupling agents: 1. γ-Aminopropyltriethoxysilane and its analogues , 1982 .

[37]  P. Breuer,et al.  The impact of thiosulfate oxidation products on the oxidation of gold in ammonia thiosulfate solutions , 2003 .

[38]  A. Jacobson,et al.  Monodisperse SnO2-coated gold nanoparticles are markedly more stable than analogous SiO2-coated gold nanoparticles. , 2013, ACS applied materials & interfaces.

[39]  J. Deventer,et al.  The effect of sulphur species on thiosulphate leaching of gold , 2007 .

[40]  I. Noda.  Two-dimensional codistribution spectroscopy to determine the sequential order of distributed presence of species , 2014 .

[41]  H. Okabayashi,et al.  Raman scattering study of polyaminopropylsiloxane and its compounds for characterization of 3-aminopropylsilane-modified silica gel. Utility of the CH2 rock and skeletal stretch modes , 1997 .

[42]  B. Meyer,et al.  RAMAN SPECTROMETRIC STUDY OF THE THERMAL DECOMPOSITION OF AQUEOUS TRI-AND TETRATHIONATE , 1982 .

[43]  S. Khan,et al.  Raman spectroscopic determination of oxoanions in aqueous polysulfide electrolyte solutions , 2011 .

[44]  B. Meyer,et al.  Raman spectrometric determination of oxysulfur anions in aqueous systems , 1980 .

[45]  J. Collins,et al.  Infrared studies of the potential controlled adsorption of sodium dodecyl sulfate at the Au(111) electrode surface. , 2012, Langmuir : the ACS journal of surfaces and colloids.

[46]  L. Bistričić,et al.  Conformational and vibrational analysis of gamma-aminopropyltriethoxysilane , 2007 .