Optical gain and spontaneous emission of strain-compensated InGaN-AlGaN quantum wells including carrier screening effect

Strain-compensated InGaN quantum well (QW) active region employing tensile AlGaN barriers was analyzed as improved gain media for laser diodes emitting at 430-440 nm by taking into account the carrier screening effect. The use of strain-compensated InGaN-AlGaN structure is advantageous because the tensile barriers compensate the compressive strain in the InGaN QW and the larger band offset allows high temperature operation. The band structure is calculated by using a 6-band k times p formalism, taking into account valence band mixing, strain effect, spontaneous and piezoelectric polarizations. The carrier screening effect is incorporated in the calculation, which is solved self-consistently. The spontaneous emission spectra show a significant improvement of the radiative emission for strain-compensated structure. The optical gain analysis shows enhancement in the peak optical gain for the strain-compensated QW structures. Threshold analysis of both the conventional InGaN-GaN QW and strain-compensated InGaN-AlGaN QW active regions indicate a reduction in the threshold carrier density and threshold current density for diode laser employing the strain-compensated QW as its active region.

[1]  Toshiro Hayakawa,et al.  Reliable operation of strain‐compensated 1.06 μm InGaAs/InGaAsP/GaAs single quantum well lasers , 1996 .

[2]  Hisashi Yamada,et al.  Continuous-wave Operation of AlGaN-cladding-free Nonpolar m-Plane InGaN/GaN Laser Diodes , 2007 .

[3]  Nelson Tansu,et al.  Low-threshold-current-density 1300-nm dilute-nitride quantum well lasers , 2002 .

[4]  Nelson Tansu,et al.  Current injection efficiency of InGaAsN quantum-well lasers , 2005 .

[5]  Michael S. Shur,et al.  Enhanced Luminescence in InGaN Multiple Quantum Wells with Quaternary AlInGaN Barriers , 2000 .

[6]  Yoichi Kawakami,et al.  Photoluminescence property of InGaN single quantum well with embedded AlGaN δ layer , 2006 .

[7]  Nelson Tansu,et al.  Experimental evidence of carrier leakage in InGaAsN quantum-well lasers , 2003 .

[8]  Ronald A. Arif,et al.  Type-II InGaN-GaNAs quantum wells for lasers applications , 2008 .

[9]  Nelson Tansu,et al.  Physics and characteristics of high performance 1200 nm InGaAs and 1300–1400 nm InGaAsN quantum well lasers obtained by metal–organic chemical vapour deposition , 2004 .

[10]  Jerry R. Meyer,et al.  Band parameters for nitrogen-containing semiconductors , 2003 .

[11]  Takashi Mukai,et al.  Superbright Green InGaN Single-Quantum-Well-Structure Light-Emitting Diodes , 1995 .

[12]  Nelson Tansu,et al.  Extremely low threshold-current-density InGaAs quantum-well lasers with emission wavelength of 1215-1233 nm , 2003 .

[13]  Shun Lien Chuang,et al.  Optical gain of strained wurtzite GaN quantum-well lasers , 1996 .

[14]  E. F. Schubert,et al.  Efficiency of GaN/InGaN light-emitting diodes with interdigitated mesa geometry , 2001 .

[15]  T. Wen,et al.  400-nm InGaN-GaN and InGaN-AlGaN multiquantum well light-emitting diodes , 2002 .

[16]  Hyun-Surk Kim,et al.  Highly stable temperature characteristics of InGaN blue laser diodes , 2006 .

[17]  Ronald A. Arif,et al.  Polarization engineering via staggered InGaN quantum wells for radiative efficiency enhancement of light emitting diodes , 2007 .

[18]  Ronald A. Arif,et al.  Optical Gain Analysis of Strain Compensated InGaN-AlGaN Quantum Well Active Regions for Lasers Emitting at 420-500 nm , 2007 .

[19]  Vincenzo Fiorentini,et al.  Spontaneous versus Piezoelectric Polarization in III–V Nitrides: Conceptual Aspects and Practical Consequences , 1999 .

[20]  Shun Lien Chuang,et al.  k.p method for strained wurtzite semiconductors , 1996 .

[21]  Euijoon Yoon,et al.  Optical gain in InGaN∕GaN quantum well structures with embedded AlGaN δ layer , 2007 .

[22]  Weng W. Chow,et al.  Laser gain properties of AlGaN quantum wells , 2005 .