Design and properties of 100% waste-based ternary alkali-activated mortars: Blast furnace slag, olive-stone biomass ash and rice husk ash

Abstract Alkali-activated cements (AACs) technology is being widely investigated as a replacement for ordinary Portland cement (OPC) for environmental benefits. Blast furnace slag (BFS) is one of the most well known precursors used in AACs, having comparable properties to those of traditional OPC-based materials. AACs require alkali solutions, which are commonly based on a combination of sodium or potassium hydroxides with sodium or potassium silicates in high concentration. These alkali solutions represent the use of chemical reagents, and thus can have major environmental, health and economic impacts. Olive-stone (also known as olive pits) biomass ash (OBA) is a residue mainly composed of calcium and potassium oxides. Rice husk ash (RHA) is a rich silica residue from the combustion of rice husk. The combination of both residues can produce a good activating reagent for BFS-based AACs. In the present work, 100% waste-based ternary alkali-activated mortars (TAAM) based on BFS activated by OBA and RHA were developed. The mortars were assessed in terms of their dosage, curing treatment and time evolution. Finally an eco-friendly 100% waste-based TAAM with 67.39 ± 0.44 MPa after 90 days of curing at 20 °C is obtained and a complete microstructural characterization shows a dense and compact matrix with binding gel products labelled as C(K)–S(A)-H and C(K)–S–H.

[1]  Keun-Hyeok Yang,et al.  Assessment of CO2 reduction of alkali-activated concrete , 2013 .

[2]  Qiang He,et al.  Synergistic utilization of red mud for flue-gas desulfurization and fly ash-based geopolymer preparation. , 2019, Journal of hazardous materials.

[3]  L. Soriano,et al.  A 100% waste-based alkali-activated material by using olive-stone biomass ash (OBA) and blast furnace slag (BFS) , 2017 .

[4]  Qiang He,et al.  Mechanical and microstructural characterization of geopolymers derived from red mud and fly ashes , 2018, Journal of Cleaner Production.

[5]  L. Soriano,et al.  Effect of sugar cane straw ash (SCSA) as solid precursor and the alkaline activator composition on alkali-activated binders based on blast furnace slag (BFS) , 2017 .

[6]  Zahra Abdollahnejad,et al.  Comparison of alkali and silica sources in one-part alkali-activated blast furnace slag mortar , 2018, Journal of Cleaner Production.

[7]  R. M. Gutiérrez,et al.  Rice husk ash and spent diatomaceous earth as a source of silica to fabricate a geopolymeric binary binder , 2016 .

[8]  Francisca Puertas,et al.  Alkali-activated slag mortars: Mechanical strength behaviour , 1999 .

[9]  F. Puertas,et al.  Rice husk ash as a source of silica in alkali-activated fly ash and granulated blast furnace slag systems , 2013 .

[10]  Robbie M. Andrew,et al.  Global CO2 emissions from cement production, 1928–2018 , 2018, Earth System Science Data.

[11]  L. Soriano,et al.  Mechanical and durability properties of alkali-activated mortar based on sugarcane bagasse ash and blast furnace slag , 2015 .

[12]  K. Ohenoja,et al.  One-part geopolymer cement from slag and pretreated paper sludge , 2018, Journal of Cleaner Production.

[13]  M. Ramli,et al.  The hybridizations of coal fly ash and wood ash for the fabrication of low alkalinity geopolymer load bearing block cured at ambient temperature , 2015 .

[14]  N. Zhao,et al.  Hydrothermal synthesis of Mg-Al layered double hydroxides (LDHs) from natural brucite and Al(OH)3 , 2012 .

[15]  Robert D. Moser,et al.  Effect of elevated temperature on alkali-activated geopolymeric binders compared to portland cement-based binders , 2016 .

[16]  John L. Provis,et al.  Evaluation of the potential improvement in the environmental footprint of geopolymers using waste-derived activators , 2017 .

[17]  L. Soriano,et al.  Olive-stone biomass ash (OBA): An alternative alkaline source for the blast furnace slag activation , 2018, Construction and Building Materials.

[18]  L. Soriano,et al.  New use of sugar cane straw ash in alkali-activated materials: A silica source for the preparation of the alkaline activator , 2018 .

[19]  A. V. Riessen,et al.  Bayer-geopolymers: An exploration of synergy between the alumina and geopolymer industries , 2013 .

[20]  C. Leonelli,et al.  Geopolymer binders from metakaolin using sodium waterglass from waste glass and rice husk ash as alternative activators: A comparative study , 2016 .

[21]  F. Collins,et al.  Carbon dioxide equivalent (CO2-e) emissions: A comparison between geopolymer and OPC cement concrete , 2013 .

[22]  Erich D. Rodríguez,et al.  Performance at high temperature of alkali-activated slag pastes produced with silica fume and rice husk ash based activators , 2015 .

[23]  J. Brito,et al.  Mechanical performance of bedding mortars made with olive biomass bottom ash , 2016 .

[24]  A. Neville.  Properties of Concrete , 1968 .

[25]  H. Lee,et al.  Setting and mechanical properties of alkali-activated fly ash/slag concrete manufactured at room temperature , 2013 .

[26]  L. Soriano,et al.  Refluxed rice husk ash/NaOH suspension for preparing alkali activated binders , 2014 .

[27]  Francisca Puertas,et al.  Waste glass in the geopolymer preparation. Mechanical and microstructural characterisation , 2015 .

[28]  Hubert Rahier,et al.  Potassium-rich biomass ashes as activators in metakaolin-based inorganic polymers , 2016 .

[29]  P. Chindaprasirt,et al.  Potassium alkali concentration and heat treatment affected metakaolin-based geopolymer , 2016 .

[30]  P. L. Pratt,et al.  Alkali-activated slag cement and concrete: a review of properties and problems , 1995 .

[31]  Somnath Ghosh,et al.  Effect of Alkali Content on Strength and Microstructure of GGBFS Paste , 2013 .

[32]  T. Miranda,et al.  Sustainable alkali activated materials: Precursor and activator derived from industrial wastes , 2017 .

[33]  R. Shirley,et al.  Alkali activated solidification/stabilisation of air pollution control residues and co-fired pulverised fuel ash. , 2011, Journal of hazardous materials.

[34]  J. Monzó,et al.  Carbon footprint of geopolymeric mortar: Study of the contribution of the alkaline activating solution and assessment of an alternative route , 2014 .

[35]  L. Soriano,et al.  Use of residual diatomaceous earth as a silica source in geopolymer production , 2018, Materials Letters.