Crack Deflection by Core Junctions in Sandwich Structures

The paper treats the problem of crack propagation in sandwich panels with interior core junctions. When a face–core interface crack approaches a tri-material wedge, as it may happen at a sandwich core junction, two options exist for further crack advance; one is for the interface crack to penetrate the wedge along the face–core interface, and the second is deflection along the core junction interface. Crack deflection is highly relevant and a requirement for the functionality of a newly developed peel stopper for sandwich structures. The physical model presented in this paper enables the quantitative prediction of the ratio of the toughnesses of the two wedge interfaces required to control the crack propagation, and the derived results can be applied directly in future designs of sandwich structures. The solution strategy is based on finite element analysis (FEA), and a realistic engineering practice example of a tri-material composition (face and core materials) is presented.

[1]  Magnus Burman,et al.  Fatigue of foam core sandwich beams—1: undamaged specimens , 1997 .

[2]  C. Berggreen,et al.  Non-uniform Compressive Strength of Debonded Sandwich Panels – I. Experimental Investigation , 2005 .

[3]  Ole Thybo Thomsen,et al.  Structurally graded core junctions in sandwich beams: fatigue loading conditions , 2005 .

[4]  Elena Bozhevolnaya,et al.  Local effects at core junctions of sandwich structures under different types of loads , 2006 .

[5]  James R. Rice,et al.  Elastic Fracture Mechanics Concepts for Interfacial Cracks , 1988 .

[6]  E. Bozhevolnaya,et al.  Crack kinking of a delamination at an inclined core junction interface in a sandwich beam , 2008 .

[7]  C. Berggreen,et al.  Non-uniform Compressive Strength of Debonded Sandwich Panels – II. Fracture Mechanics Investigation , 2005 .

[8]  C. Shih,et al.  Elastic-Plastic Analysis of Cracks on Bimaterial Interfaces: Part I—Small Scale Yielding , 1988 .

[9]  F. Avilés,et al.  Experimental Study of Debonded Sandwich Panels under Compressive Loading , 2006 .

[10]  Anthony G. Evans,et al.  Kinking of a Crack out of an Interface: Role of In‐Plane Stress , 1991 .

[11]  S. Pageau,et al.  The order of stress singularities for bonded and disbonded three-material junctions , 1994 .

[12]  E. Bozhevolnaya,et al.  Fatigue Performance of Sandwich Beams With Peel Stoppers , 2009 .

[13]  D. Zenkert,et al.  Handbook of Sandwich Construction , 1997 .

[14]  Bo Cerup Simonsen,et al.  Experimental and Numerical Study of Interface Crack Propagation in Foam-cored Sandwich Beams , 2007 .

[15]  S. Tsai,et al.  Composite Materials: Design and Applications , 2002 .

[16]  J. Hutchinson,et al.  Kinking of A Crack Out of AN Interface , 1989 .

[17]  John W. Hutchinson,et al.  Crack deflection at an interface between dissimilar elastic-materials , 1989 .

[18]  Ole Thybo Thomsen,et al.  Structurally graded core junctions in sandwich elements , 2005 .

[19]  J. Dundurs.  Discussion: ``Edge-Bonded Dissimilar Orthogonal Elastic Wedges Under Normal and Shear Loading'' (Bogy, D. B., 1968, ASME J. Appl. Mech., 35, pp. 460-466) , 1969 .

[20]  Ole Thybo Thomsen,et al.  Parametric study of structurally graded core junctions , 2006 .

[21]  Leif A. Carlsson,et al.  Crack path in foam cored DCB sandwich fracture specimens , 2005 .

[22]  Tao Wang,et al.  Kinking of an interface crack between two dissimilar anisotropic elastic solids , 1994 .

[23]  Brian Moran,et al.  Energy release rate along a three-dimensional crack front in a thermally stressed body , 1986, International Journal of Fracture.

[24]  J. Rice,et al.  Plane Problems of Cracks in Dissimilar Media , 1965 .

[25]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[26]  David B. Bogy,et al.  Edge-Bonded Dissimilar Orthogonal Elastic Wedges Under Normal and Shear Loading , 1968 .

[27]  Ole Thybo Thomsen,et al.  Structurally graded core junctions in sandwich beams: quasi static loading conditions , 2005 .

[28]  J. Dundurs,et al.  Discussion of Edge-Bonded Dissimilar Orthogonal Elastic Wedges under Normal and Shear Loading , 1969 .

[29]  Z. Suo,et al.  Interface crack between two elastic layers , 1990 .

[30]  John R. Rice,et al.  The Bending of Plates of Dissimilar Materials With Cracks , 1964 .

[31]  Ole Thybo Thomsen,et al.  New Peel Stopper Concept for Sandwich Structures , 2007 .

[32]  J. Rice.  A path-independent integral and the approximate analysis of strain , 1968 .

[33]  D. Zenkert,et al.  Fatigue of foam core sandwich beams—2: effect of initial damage , 1997 .

[34]  Bent F. Sørensen,et al.  Measurement of Interface Fracture Toughness of Sandwich Structures under Mixed Mode Loadings , 2007 .

[35]  R. Salganik,et al.  The strength of adhesive joints using the theory of cracks , 1984 .

[36]  C. F. Shih,et al.  Elastic-Plastic Analysis of Cracks on Bimaterial Interfaces: Part II—Structure of Small-Scale Yielding Fields , 1989 .

[37]  Christian Berggreen,et al.  A modified DCB sandwich specimen for measuring mixed-mode cohesive laws , 2008 .

[38]  C. Shih,et al.  Crack extension and kinking in laminates and bicrystals , 1992 .