Enhancement of electrochromic contrast by tethering conjugated polymer chains onto polyhedral oligomeric silsesquioxane nanocages

Copolymerization of aniline with octa(aminophenyl) silsesquioxane (OAPS) was performed, which resulted in polyaniline-tethered, polyhedral oligomeric silsesquioxane (POSS-PANI), with star-like molecular geometry. The spectro-electrochemical studies show that the electrochromic contrast of POSS-PANI is much higher than that of polyaniline (PANI). The great improvement can be attributed to the more accessible doping sites and the facile ion movement during the redox switching, brought by the loose packing of the PANI chains. This was evidenced by a drastic increase in ionic conductivity, a decrease in the electrical conductivity, and a decrease in the crystallinity and crystal size, with the increase of the OAPS concentration in the POSS-PANI.

[1]  J. Reynolds,et al.  Conducting Poly(3,4-alkylenedioxythiophene) Derivatives as Fast Electrochromics with High-Contrast Ratios , 1998 .

[2]  R. Santos,et al.  Enhancing the performance of an electrochromic device by template synthesis of the active layers , 2004 .

[3]  Heung Cho Ko,et al.  Enhancement of Electrochromic Contrast of Poly(3,4‐Ethylenedioxythiophene) by Incorporating a Pendant Viologen , 2004 .

[4]  Anilesh Kumar,et al.  Dendronized electrochromic polymer based on poly(3,4-ethylenedioxythiophene) , 2002 .

[5]  Xuehong Lu,et al.  Nano-hybrid luminescent dot: synthesis, characterization and optical properties , 2006 .

[6]  José A. Pomposo,et al.  A simplified all-polymer flexible electrochromic device , 2004 .

[7]  Gajanana C. Birur,et al.  Large, Switchable Electrochromism in the Visible Through Far‐Infrared in Conducting Polymer Devices , 2002 .

[8]  Jianwei Xu,et al.  Thermal degradation of electrical conductivity of polyacrylic acid doped polyaniline: effect of molecular weight of the dopants , 2003 .

[9]  Seung Il Cho,et al.  Nanotube‐Based Ultrafast Electrochromic Display , 2005 .

[10]  R. Laine,et al.  Octa(aminophenyl)silsesquioxane as a nanoconstruction site. , 2001, Journal of the American Chemical Society.

[11]  Chaobin He,et al.  Highly efficient luminescent organic clusters with quantum dot-like properties. , 2004, Journal of the American Chemical Society.

[12]  R. Holze,et al.  Spectroelectrochemical Investigations of Soluble Polyaniline Synthesized via New Inverse Emulsion Pathway , 2005 .

[13]  Jianwei Xu,et al.  Electrical conductivity of polyaniline–dodecylbenzene sulphonic acid complex: thermal degradation and its mechanism , 2002 .

[14]  Wusheng Yin,et al.  Soluble polyaniline co-doped with dodecyl benzene sulfonic acid and hydrochloric acid , 2000 .

[15]  Jianwei Xu,et al.  Blends of polyimide and dodecylbenzene sulfonic acid-doped polyaniline: Effects of polyimide structure on electrical conductivity and its thermal degradation , 2006 .

[16]  P. Hammond,et al.  Multiple-Color Electrochromism from Layer-by-Layer-Assembled Polyaniline/Prussian Blue Nanocomposite Thin Films , 2004 .

[17]  John R. Reynolds,et al.  Enhanced Contrast Ratios and Rapid Switching in Electrochromics Based on Poly(3,4-propylenedioxythiophene) Derivatives , 1999 .

[18]  P. Pickup.  Alternating current impedance study of a polypyrrole-based anion-exchange polymer , 1990 .

[19]  Dean M. DeLongchamp,et al.  Layer-by-layer assembly of PEDOT/polyaniline electrochromic devices , 2001 .

[20]  John R. Reynolds,et al.  Poly(ProDOT‐Et2): A High‐Contrast, High‐Coloration Efficiency Electrochromic Polymer , 2002 .

[21]  K. Akagi,et al.  Electrochemical Synthesis and Optical Properties of a Chiral Poly[1,4‐bis(3′,4′‐ethylenedioxythienyl)‐phenylene] Derivative , 2005 .

[22]  K. Suh,et al.  Novel Electrochromic Displays Using Monodisperse Viologen‐Modified Porous Polymeric Microspheres , 2006 .

[23]  Jenq-Neng Hwang,et al.  Multicolored Electrochromism in Polymers: Structures and Devices , 2004 .

[24]  M. Marcaccio,et al.  Electrochemical and electrochromic investigation of poly-bithiophene films on a mesoporous TiO2 surface , 2006 .