Effect of the Cooling Rate of Thermal Simulation on the Microstructure and Mechanical Properties of Low-Carbon Bainite Steel by Laser-Arc Hybrid Welding

A new kind of low-carbon bainite steel with excellent strength and toughness was developed, serving as the bogie of the next-generation high-speed train. However, the softening of the heat-affected zone (HAZ) in laser-arc hybrid welding (LAHW) needs to be overcome. In this study, the effect of the cooling rate of the LAHW process on the microstructure and mechanical properties in the HAZ was explored via thermal simulation. The results showed that with increased cooling rate, the grain size increased, the content of lath martensite decreased, and the lath bainite gradually changed to a granular shape in the thermal simulation specimen. With the decrease in the cooling rate, i.e., with the increase of t8/5, the strength–toughness matching of the material showed a downward trend. The thermal simulation specimen with a t8/5 of 6~8 s had higher strength and good toughness, which can be considered a potential welding parameter reference. The content of martensitic austenite (M-A) constituents was the main factor that determined the strength and toughness of the joint. During the tensile test, the axial force caused the material to tighten, and the transverse stress as obvious in the part of the M-A constituents that are prone to microcracks and many defects, resulting in cracks, paths, and multi-component layers in the center. As a result, the thermal cycle specimens had mixed fracture characteristics.

[1]  E. Bassini,et al.  Assessment of the Hardening Behavior and Tensile Properties of a Cold-Rolled Bainitic–Ferritic Steel , 2021, Materials.

[2]  T. Baudin,et al.  Welding Thermal Cycle Impact on the Microstructure and Mechanical Properties of Thermo–Mechanical Control Process Steels , 2021, steel research international.

[3]  G. Testa,et al.  Stress triaxiality effect on cleavage fracture stress , 2020 .

[4]  Liqing Chen,et al.  Microstructural Characteristics and Impact Fracture Behaviors of a Novel High-Strength Low-Carbon Bainitic Steel with Different Reheated Coarse-Grained Heat-Affected Zones , 2020, Metallurgical and Materials Transactions A.

[5]  L. Lan,et al.  Morphological evolution of HAZ microstructures in low carbon steel during simulated welding thermal cycle. , 2020, Micron.

[6]  Ying Liang,et al.  The effect of arc position on laser-arc hybrid welding of 12-mm-thick high strength bainitic steel , 2020 .

[7]  F. Lu,et al.  Effect of Trace Element on Microstructure and Fracture Toughness of Weld Metal , 2019, Acta Metallurgica Sinica (English Letters).

[8]  E. Palmiere,et al.  Influence of cooling rate on the grain-refining effect of austenite deformation in a HSLA steel , 2019, Materials Characterization.

[9]  A. Gerlich,et al.  Effect of martensite-austenite (MA) distribution on mechanical properties of inter-critical Reheated Coarse Grain heat affected zone in X80 linepipe steel , 2019, Materials Science and Engineering: A.

[10]  M. Zhang,et al.  Effect of Heat Input on M-A Constituent and Toughness of Coarse Grain Heat-Affected Zone in an X100 Pipeline Steel , 2019, Journal of Materials Engineering and Performance.

[11]  X. Di,et al.  Microstructural evolution and its influence on toughness in simulated inter-critical heat affected zone of large thickness bainitic steel , 2019, Materials Science and Engineering: A.

[12]  Xia Liu,et al.  Effect of Ti content and martensite–austenite constituents on microstructure and mechanical property , 2018 .

[13]  A. Kaplan,et al.  Deep penetration fiber laser-arc hybrid welding of thick HSLA steel , 2018, Journal of Materials Processing Technology.

[14]  Xu Zhang,et al.  Effect of welding thermal cycle on microstructural evolution of Al–Zn–Mg–Cu alloy , 2018 .

[15]  Michael W. Hester,et al.  Recycling welding rod residuals based on development of a top-down nanomanufacturing system employing indexing equal channel angular pressing , 2018 .

[16]  F. Cheng,et al.  Effect of martensite–austenite constituent on toughness of simulated inter-critically reheated coarse-grained heat-affected zone in X70 pipeline steel , 2016 .

[17]  M. Wahba,et al.  Single pass hybrid laser-arc welding of 25 mm thick square groove butt joints , 2016 .

[18]  Caifu Yang,et al.  Effect of nitrogen content on the second phase particles in V–Ti microalloyed shipbuilding steel during weld thermal cycling , 2016 .

[19]  Jun Xiong,et al.  Thermal cycle and microstructure of backing weld in double-sided TIG arc horizontal welding of high-strength steel thick plate , 2015 .

[20]  S. Subramanian,et al.  Influence of Martensite–Austenite constituents formed at different intercritical temperatures on toughness , 2015 .

[21]  Paul Kah,et al.  Multi-wire SAW of 640 MPa Arctic shipbuilding steel plates , 2014 .

[22]  R. Misra,et al.  An analysis of the microstructure of the heat-affected zone of an ultra-low carbon and niobium-bearing acicular ferrite steel using EBSD and its relationship to mechanical properties , 2010 .

[23]  Wei Yan,et al.  Delamination Fracture Related to Tempering in a High-Strength Low-Alloy Steel , 2009 .

[24]  Takao Araki,et al.  Micro-fracture behaviour induced by M-A constituent (Island Martensite) in simulated welding heat affected zone of HT80 high strength low alloyed steel , 1984 .