Accelerated test analysis of reversal potential caused by fuel starvation during PEMFCs operation

The performance of polymer electrolyte membrane fuel cells (PEMFCs) was reduced due to the degradation of the catalyst layer when reverse potential was generated by fuel starvation in PEMFCs. Detailed analysis was performed through accelerated reversal potential tests. The electrochemical impedance spectroscopy (EIS) measurement results showed that the charge transfer resistance increased and the electrochemical active surface area (ECSA) reduction was confirmed through the cyclic voltammetry (CV) measurements. Corrosion of the carbon used as the catalyst support was detected by confirming the CO peak in the 1st cyclic voltammogram in the CV measurements. Growth of the Pt catalyst due to the agglomeration and sintering of Pt was confirmed during increasing cycles of the accelerated reversal potential through X-ray diffraction (XRD) and transmission electron microscopy (TEM) analyses.

[1]  Chao-Yang Wang,et al.  Dynamics of polymer electrolyte fuel cells undergoing load changes , 2006 .

[2]  Héctor R. Colón-Mercado,et al.  Stability of platinum based alloy cathode catalysts in PEM fuel cells , 2006 .

[3]  A. Taniguchi,et al.  Analysis of electrocatalyst degradation in PEMFC caused by cell reversal during fuel starvation , 2004 .

[4]  Antonio J. Martín,et al.  Comparative analysis of the electroactive area of Pt/C PEMFC electrodes in liquid and solid polymer contact by underpotential hydrogen adsorption/desorption , 2009 .

[5]  Liang Hong,et al.  Carbon-supported Pt nanoparticles as catalysts for proton exchange membrane fuel cells , 2005 .

[6]  K. R. Cooper,et al.  Electrical test methods for on-line fuel cell ohmic resistance measurement , 2006 .

[7]  Zhixiang Liu,et al.  Behavior of PEMFC in starvation , 2006 .

[8]  Jiujun Zhang,et al.  A review of accelerated stress tests of MEA durability in PEM fuel cells , 2009 .

[9]  A. Vahidi,et al.  A review of the main parameters influencing long-term performance and durability of PEM fuel cells , 2008 .

[10]  Won-Yong Lee,et al.  Current distribution in a single cell of PEMFC , 2003 .

[11]  K. Reifsnider,et al.  Mechanical Endurance of Polymer Electrolyte Membrane and PEM Fuel Cell Durability , 2006 .

[12]  D. Candusso,et al.  A review on polymer electrolyte membrane fuel cell catalyst degradation and starvation issues: Causes, consequences and diagnostic for mitigation , 2009 .

[13]  Jun Shen,et al.  A review of PEM fuel cell durability: Degradation mechanisms and mitigation strategies , 2008 .

[14]  M. De Francesco,et al.  Comparison of high surface Pt/C catalysts by cyclic voltammetry , 2002 .

[15]  F. Hahn,et al.  In situ FTIRS study of the electrocatalytic oxidation of carbon monoxide and methanol at platinum–ruthenium bulk alloy electrodes , 1998 .

[16]  Sirivatch Shimpalee,et al.  The effect of stoichiometry on dynamic behavior of a proton exchange membrane fuel cell (PEMFC) during load change , 2004 .

[17]  H. Tang,et al.  PEM fuel cell cathode carbon corrosion due to the formation of air/fuel boundary at the anode , 2006 .

[18]  Bing Wu,et al.  Current density distribution in PEFC , 2005 .

[19]  David L. Wood,et al.  PEM fuel cell electrocatalyst durability measurements , 2006 .

[20]  Zhigang Shao,et al.  The effect of H2S and CO mixtures on PEMFC performance , 2007 .