Current crowding effect on copper dual damascene via bottom failure for ULSI applications

Reliability of interconnect via is increasing an important issue in submicron technology. Electromigration experiments are performed on line/via structures in two level Cu dual damascene interconnection system and it is found that wide line/via fails earlier than the narrow line/via. Atomic flux divergence based finite element analyses is performed and stress-migration is found to be important in the failure rate behavior observed. Semi-classical width dependence Black's equation together with the finite element analysis revealed that the difference in the time to failure is due to the much larger average current density along the interface between the line and via for the wide line/via structure, and good agreement is obtained between the simulation and experimental results.

[1]  Michael Lane,et al.  Relationship between interfacial adhesion and electromigration in Cu metallization , 2003 .

[2]  D. Schneider,et al.  Non-destructive characterization and evaluation of thin films by laser-induced ultrasonic surface waves , 1996 .

[3]  Yu-Lin Shen,et al.  Temperature-dependent inelastic response of passivated copper films: Experiments, analyses, and implications , 2003 .

[4]  C. Q. Ru,et al.  Intrinsic instability of electromigration induced mass transport in a two-dimensional conductor , 1999 .

[5]  Bi-Shiou Chiou,et al.  Effects of Underlayer Dielectric on the Thermal Characteristics and Electromigration Resistance of Copper Interconnect , 2003 .

[6]  James R. Lloyd,et al.  A model for conductor failure considering diffusion concurrently with electromigration resulting in a current exponent of 2 , 1986 .

[7]  Wen-Jie Qi,et al.  Thermomechanical property of diffusion barrier layer and its effect on the stress characteristics of copper submicron interconnect structures , 2002, Microelectron. Reliab..

[8]  Guo Weiling,et al.  The electromigration and reliability of VLSI metallization under temperature gradient conditions , 1998, 1998 5th International Conference on Solid-State and Integrated Circuit Technology. Proceedings (Cat. No.98EX105).

[9]  King-Ning Tu,et al.  The effect of contact resistance on current crowding and electromigration in ULSI multi-level interconnects , 2003 .

[10]  Stefan P. Hau-Riege,et al.  The Effects of the Mechanical Properties of the Confinement Material on Electromigration in Metallic Interconnects , 2000 .

[11]  Chao-Kun Hu,et al.  IN SITU SCANNING ELECTRON MICROSCOPE COMPARISON STUDIES ON ELECTROMIGRATION OF CU AND CU(SN) ALLOYS FOR ADVANCED CHIP INTERCONNECTS , 1995 .

[12]  Paul S. Ho,et al.  Electromigration reliability issues in dual-damascene Cu interconnections , 2002, IEEE Trans. Reliab..

[13]  J. S. Huang,et al.  Direct observation of void morphology in step-like electromigration resistance behavior and its correlation with critical current density , 2001 .

[14]  J. A. Walls.  The influence of TiN ARC thickness on stress-induced void formation in tungsten-plug vias , 1997 .

[15]  Paul S. Ho,et al.  Thermal stress characteristics of Cu/oxide and Cu/low-k submicron interconnect structures , 2003 .

[16]  M. Nathan,et al.  On the unusual electromigration behavior of copper interconnects , 1996 .

[17]  Jen‐Sue Chen,et al.  Microstructural and electrical characteristics of reactively sputtered Ta-N thin films , 2002 .

[18]  Cher Ming Tan,et al.  Dynamic study of the physical processes in the intrinsic line electromigration of deep-submicron copper and aluminum interconnects , 2004, IEEE Transactions on Device and Materials Reliability.

[19]  Joe W. McPherson,et al.  Stress-induced voiding under vias connected to wide Cu metal leads , 2002, 2002 IEEE International Reliability Physics Symposium. Proceedings. 40th Annual (Cat. No.02CH37320).

[20]  Andrew H. Simon,et al.  Effect of liner thickness on electromigration lifetime , 2003 .

[21]  Deenesh Padhi,et al.  Effect of electron flow direction on model parameters of electromigration-induced failure of copper interconnects , 2003 .

[22]  Yu‐Lin Shen.  Analysis of Joule heating in multilevel interconnects , 1999 .

[23]  James R. Lloyd,et al.  Copper metallization reliability , 1999 .

[24]  T. F. Retajczyk,et al.  Elastic stiffness and thermal expansion coefficients of various refractory silicides and silicon nitride films , 1980 .

[25]  T. L. Hebble,et al.  Phonon and electron components of the thermal conductivity of tantalum at intermediate temperatures , 1982 .

[26]  J. Black,et al.  Electromigration—A brief survey and some recent results , 1969 .

[27]  J. Bisschop,et al.  Effect of thermal gradients on the electromigration life-time in power electronics , 2004, 2004 IEEE International Reliability Physics Symposium. Proceedings.

[28]  C. Tan,et al.  Comparison of the Time-Dependent Physical Processes in the Electromigration of Deep Submicron Copper and Aluminum Interconnects , 2003 .

[29]  Seungmin Lee,et al.  Heat transport in thin dielectric films , 1997 .

[30]  Kirsten Weide-Zaage,et al.  Three-Dimensional Voids Simulation in chip Metallization Structures: a Contribution to Reliability Evaluation , 2001, Microelectron. Reliab..

[31]  Chenming Hu,et al.  Correlation of electromigration lifetime distribution to failure mode in dual damascene Cu/SiLK interconnects , 2003 .