High Burnup Fuel Cladding Materials R&D for Advanced Nuclear Systems

Cladding materials development is crucial to realize highly efficient and high-burnup operation over 100GWd/t of so called Generation IV nuclear energy systems, such as supercritical-water-cooled reactor (SCWR) and lead-cooled fast reactor (LFR). Oxide dispersion strengthening (ODS) ferritic/martensitic steels, which contain 9–12%Cr, show rather high resistance to neutron irradiation embrittlement and high strength at elevated temperatures. However, their corrosion resistance is not good enough in SCW and in lead at high temperatures. In order to improve corrosion resistance of the ODS steels in such environment, high-Cr ODS steels have been developed at Kyoto University. An increase in Cr content resulted in a drastic improvement of corrosion resistance in SCW and in lead, while it was expected to cause an enhancement of aging embrittlement as well as irradiation embrittlement. Anisotropy in tensile properties is another issue. In order to overwhelm these issues, surveillance tests of the material performance have been performed for high Cr-ODS steels produced by new processing technologies. It is demonstrated that high-Cr ODS steels have a high potential as fuel cladding materials for SCWR and LFR with high efficiency and high burnup.

[1]  H. Ullmaier,et al.  The mechanical properties of an Alloy 718 window after irradiation in a spallation environment , 2001 .

[2]  H. Matsui,et al.  High resistance to helium embrittlement in reduced activation martensitic steels , 2002 .

[3]  Edward A. Kenik,et al.  Stability of Ferritic MA/ODS Alloys at High Temperatures , 2004, Microscopy and Microanalysis.

[4]  T. Okuda,et al.  Tube manufacturing and characterization of oxide dispersion strengthened ferritic steels , 2000 .

[5]  H. Matsui,et al.  Irradiation hardening of reduced activation martensitic steels , 1996 .

[6]  A. Kimura,et al.  Effects of hydrogen on the mechanical properties of oxide dispersion strengthening steels , 2004 .

[7]  T. Sample,et al.  Liquid metal embrittlement (LME) susceptibility of the 8?9% Cr martensitic steels F82H-mod., OPTIFER IVb and their simulated welded structures in liquid Pb?17Li , 2000 .

[8]  Shigeharu Ukai,et al.  Development of oxide dispersion strengthened steels for FBR core application, (II). Morphology improvement by martensite transformation , 1998 .

[9]  P. Fauvet,et al.  Corrosion of austenitic and martensitic stainless steels in flowing 17Li83Pb alloy , 1988 .

[10]  T. Yoshitake,et al.  Burst properties of irradiated oxide dispersion strengthened ferritic steel claddings , 2002 .

[11]  A. Kimura,et al.  Development of Fuel Clad Materials for High Burn-up Operation of SCPR , 2003 .

[12]  S. Ukai,et al.  Improvement of 9Cr-ODS martensitic steel properties by controlling excess oxygen and titanium contents , 2004 .

[13]  H. Kolbe,et al.  Effects of Pb17Li on the tensile properties of steels , 1988 .

[14]  Ryuta Kasada,et al.  Annealing behavior of irradiation hardening and microstructure in helium-implanted reduced activation martensitic steel , 2000 .

[15]  H. Borgstedt,et al.  Corrosion testing of steel X 18 CrMoVNb 12 1 (1.4914) in A Pb17Li pumped loop , 1988 .

[16]  J. Schlosser,et al.  Lifetime of Be-, CFC- and W-armoured ITER divertor plates , 1996 .

[17]  Todd R. Allen,et al.  The effects of low dose rate irradiation and thermal aging on reactor structural alloys , 1999 .

[18]  G. Benamati,et al.  Mechanical and corrosion behaviour of EUROFER 97 steel exposed to Pb–17Li , 2002 .

[19]  T. Sample,et al.  The effects of hydrogen and Pb17Li on the tensile properties of 1.4914 martensitic steel , 1992 .

[20]  A. Kimura,et al.  Corrosion properties of oxide dispersion strengthened steels in super-critical water environment , 2004 .

[21]  T. Okuda,et al.  Development of Oxide Dispersion Strengthened Ferritic Steels for FBR Core Application, (I). Improvement of Mechanical Properties by Recrystallization Processing.:Improvement of Mechanical Properties by Recrystallization Processing , 1997 .

[22]  T. Sample,et al.  Liquid metal embrittlement susceptibility of welded MANET II (DIN 1.4914) in liquid Pb17Li. , 1996 .