Synthesis of ZnO nanospheres with uniform nanopores by a hydrothermal process

Abstract ZnO nanospheres were successfully synthesized by a hydrothermal process (S1 sample) and a wet-chemical method (S2 sample). Following synthesis, calcination treatment at 450 °C was performed for the sample prepared by the wet-chemical method (S3 sample). All of the samples possessed a regular spherical shape. A polycrystalline wurtzite structure was confirmed in the S1 and S3 samples by X-ray diffraction and selected area electron diffraction, whereas a mixture of ZnO nanoparticles and amorphous materials was observed in the sample S2. The surface area and pore structure of the samples were investigated by nitrogen adsorption–desorption measurements. Uniform nanopores with a diameter of 4.07 nm were present in the S1 sample while a broad pore size distribution was obtained for the S2 and S3 samples. The highest surface area was obtained for the S1 sample and a possible formation mechanism was studied.

[1]  X. W. Sun,et al.  Enzymatic glucose biosensor based on ZnO nanorod array grown by hydrothermal decomposition , 2006 .

[2]  G. Cao,et al.  Effect of an Ultrathin TiO2 Layer Coated on Submicrometer‐Sized ZnO Nanocrystallite Aggregates by Atomic Layer Deposition on the Performance of Dye‐Sensitized Solar Cells , 2010, Advanced materials.

[3]  Jiaguo Yu,et al.  A One-Pot Approach to Hierarchically Nanoporous Titania Hollow Microspheres with High Photocatalytic Activity , 2008 .

[4]  Renata Solarska,et al.  Low-temperature roll-to-roll coating procedure of dye-sensitized solar cell photoelectrodes on flexible polymer-based substrates , 2011 .

[5]  S. Gosavi,et al.  Controlled synthesis of ZnO from nanospheres to micro-rods and its gas sensing studies. , 2008, Talanta.

[6]  Yan Qiao,et al.  New Nanostructured TiO2 for Direct Electrochemistry and Glucose Sensor Applications , 2008 .

[7]  G. Cao,et al.  Effects of Lithium Ions on Dye-Sensitized ZnO Aggregate Solar Cells , 2010 .

[8]  Guozhong Cao,et al.  Aggregation of ZnO nanocrystallites for high conversion efficiency in dye-sensitized solar cells. , 2008, Angewandte Chemie.

[9]  H. Arami,et al.  Flower-like bundles of ZnO nanosheets as an intermediate between hollow nanosphere and nanoparticles , 2006 .

[10]  Pooi See Lee,et al.  One-Pot Synthesis of Hierarchically Assembled Tungsten Oxide (Hydrates) Nano/Microstructures by a Crystal-Seed-Assisted Hydrothermal Process , 2009 .

[11]  K. Leung,et al.  Template-free single-step electrochemical synthesis of ZnO hollow nanospheres: Self-assembly of hollow nanospheres from nanoparticles , 2009 .

[12]  Xiao Wei,et al.  Formation of single-crystal SrTiO3 dendritic nanostructures via a simple hydrothermal method , 2009 .

[13]  Caofeng Pan,et al.  Highly Sensitive Amperometric Cholesterol Biosensor Based on Pt-Incorporated Fullerene-like ZnO Nanospheres , 2010 .

[14]  Yifan Zheng,et al.  Synthesis of MnO2 Nanostructures with Sea Urchin Shapes by a Sodium Dodecyl Sulfate-Assisted Hydrothermal Process , 2007 .

[15]  Xiaolin Li,et al.  Synthesis and characterization of nanocrystalline niobates , 2003 .

[16]  F. Jona,et al.  Atomic underlayer formation during the reaction of Ti{0001} with nitrogen , 1976 .

[17]  Polycarpos Falaras,et al.  Synergetic effect of carboxylic acid functional groups and fractal surface characteristics for efficient dye sensitization of titanium oxide , 1998 .

[18]  S. Manorama,et al.  Hydrothermal synthesis of highly crystalline ZnO nanoparticles: A competitive sensor for LPG and EtOH , 2006 .

[19]  Guozhong Cao,et al.  Polydisperse Aggregates of ZnO Nanocrystallites: A Method for Energy‐Conversion‐Efficiency Enhancement in Dye‐Sensitized Solar Cells , 2008 .

[20]  M. Jayaraj,et al.  Red luminescence from hydrothermally synthesized Eu-doped ZnO nanoparticles under visible excitation , 2010 .

[21]  M. K. Jayaraj,et al.  Synthesis of ZnO nanoparticles by hydrothermal method , 2007, SPIE NanoScience + Engineering.

[22]  Y. Kanemitsu,et al.  Fabrication and optical properties of Eu3+-doped ZnO nanospheres and nanorods , 2008 .

[23]  B. Wang,et al.  Study on effects of time and temperature on growth of nanocrystalline zinc selenide synthesized by hydrothermal method , 2009 .

[24]  Y. Qian,et al.  A hydrothermal method for low-temperature growth of nanocrystalline pyrite nickel diselenide , 2000 .

[25]  Zhong Lin Wang.  Zinc oxide nanostructures: growth, properties and applications , 2004 .

[26]  S. Ramakrishna,et al.  Controlled synthesis and application of ZnO nanoparticles, nanorods and nanospheres in dye-sensitized solar cells , 2009, Nanotechnology.

[27]  Guozhong Cao,et al.  Hierarchically Structured ZnO Film for Dye‐Sensitized Solar Cells with Enhanced Energy Conversion Efficiency , 2007 .

[28]  Jie Liu,et al.  Synthesis and photoluminescence of Cl-doped ZnO nanospheres , 2008 .

[29]  K. Ariga,et al.  An investigation on co-precipitation derived ZnO nanospheres. , 2009, Journal of nanoscience and nanotechnology.

[30]  S. K. Mishra,et al.  Photoconductivity, dark-conductivity and photoluminescence study of hydrothermally synthesized ZnO nanoparticles , 2009, 2009 International Conference on Emerging Trends in Electronic and Photonic Devices & Systems.

[31]  M. Jaroniec,et al.  Gas adsorption characterization of ordered organic-inorganic nanocomposite materials , 2001 .