Grafting of epoxy chains onto graphene oxide for epoxy composites with improved mechanical and thermal properties

Abstract Epoxy composites filled with both graphene oxide (GO) and diglycidyl ether of bisphenol-A functionalized GO (DGEBA–f–GO) sheets were prepared at different filler loading levels. The correlations between surface modification, morphology, dispersion/exfoliation and interfacial interaction of sheets and the corresponding mechanical and thermal properties of the composites were systematically investigated. The surface functionalization of DGEBA layer was found to effectively improve the compatibility and dispersion of GO sheets in epoxy matrix. The tensile test indicated that the DGEBA–f–GO/epoxy composites showed higher tensile modulus and strength than either the neat epoxy or the GO/epoxy composites. For epoxy composite with 0.25 wt% DGEBA–f–GO, the tensile modulus and strength increased from 3.15 ± 0.11 to 3.56 ± 0.08 GPa (∼13%) and 52.98 ± 5.82 to 92.94 ± 5.03 MPa (∼75%), respectively, compared to the neat epoxy resin. Furthermore, enhanced quasi-static fracture toughness ( K IC ) was measured in case of the surface functionalization. The GO and DGEBA–f–GO at 0.25 wt% loading produced ∼26% and ∼41% improvements in K IC values of epoxy composites, respectively. Fracture surface analysis revealed improved interfacial interaction between DGEBA–f–GO and matrix. Moreover, increased glass transition temperature and thermal stability of the DGEBA–f–GO/epoxy composites were also observed in the dynamic mechanical properties and thermo-gravimetric analysis compared to those of the GO/epoxy composites.

[1]  Scott S. Verbridge,et al.  Electromechanical Resonators from Graphene Sheets , 2007, Science.

[2]  I. Martín-Gullón,et al.  Impressive Fatigue Life and Fracture Toughness Improvements in Graphene Oxide/Epoxy Composites , 2012 .

[3]  M. Fang,et al.  Constructing hierarchically structured interphases for strong and tough epoxy nanocomposites by amine-rich graphene surfaces , 2010 .

[4]  Biqiong Chen,et al.  Reinforcement and interphase of polymer/graphene oxide nanocomposites , 2012 .

[5]  Bin Shen,et al.  Chemical functionalization of graphene oxide toward the tailoring of the interface in polymer composites , 2013 .

[6]  C. A. May,et al.  Epoxy Resins: Chemistry and Technology , 1973 .

[7]  Zhong Zhang,et al.  A novel failure analysis of multi-walled carbon nanotubes in epoxy matrix , 2011 .

[8]  G. Eda,et al.  Large-area ultrathin films of reduced graphene oxide as a transparent and flexible electronic material. , 2008, Nature nanotechnology.

[9]  Guohua Chen,et al.  Preparation of graphene by exfoliation of graphite using wet ball milling , 2010 .

[10]  Jie Jin,et al.  An investigation of the mechanism of graphene toughening epoxy , 2013 .

[11]  M. Singh,et al.  Graphene oxide modified with PMMA via ATRP as a reinforcement filler , 2010 .

[12]  Y. Mai,et al.  Synthesis of epoxy composites with high carbon nanotube loading and effects of tubular and wavy morphology on composite strength and modulus , 2011 .

[13]  R. Ruoff,et al.  Chemical methods for the production of graphenes. , 2009, Nature nanotechnology.

[14]  N. Koratkar,et al.  Fracture and fatigue in graphene nanocomposites. , 2010, Small.

[15]  Cao Chen,et al.  Melt blending in situ enhances the interaction between polystyrene and graphene through π-π stacking. , 2011, ACS applied materials & interfaces.

[16]  J. Kysar,et al.  Measurement of the Elastic Properties and Intrinsic Strength of Monolayer Graphene , 2008, Science.

[17]  N. Koratkar,et al.  Enhanced electrical conductivity in polystyrene nanocomposites at ultra-low graphene content. , 2011, ACS applied materials & interfaces.

[18]  Hongbing Lu,et al.  Constructing sacrificial bonds and hidden lengths for ductile graphene/polyurethane elastomers with improved strength and toughness , 2012 .

[19]  Zhong-Zhen Yu,et al.  Simultaneous surface functionalization and reduction of graphene oxide with octadecylamine for electrically conductive polystyrene composites , 2011 .

[20]  S. Bose,et al.  Recent advances in graphene based polymer composites , 2010 .

[21]  A. Yee,et al.  Epoxy Nanocomposites with Highly Exfoliated Clay: Mechanical Properties and Fracture Mechanisms , 2005 .

[22]  Xu Wang,et al.  Mechanical properties and fracture behaviors of epoxy composites with multi-scale rubber particles , 2013 .

[23]  M. A. Gómez,et al.  Polymeric Modification of Graphene through Esterification of Graphite Oxide and Poly(vinyl alcohol) , 2009 .

[24]  J. Coleman.  Liquid exfoliation of defect-free graphene. , 2013, Accounts of chemical research.

[25]  S. Stankovich,et al.  Graphene-based composite materials , 2006, Nature.

[26]  Lihua Feng,et al.  A graphite nanoplatelet/epoxy composite with high dielectric constant and high thermal conductivity , 2013 .

[27]  Jonathan N. Coleman,et al.  Approaching the theoretical limit for reinforcing polymers with graphene , 2012 .

[28]  Yern Seung Kim,et al.  Surface modifications for the effective dispersion of carbon nanotubes in solvents and polymers , 2012 .

[29]  Lee Luong,et al.  Epoxy/graphene platelets nanocomposites with two levels of interface strength , 2011 .

[30]  N. Koratkar,et al.  Enhanced mechanical properties of nanocomposites at low graphene content. , 2009, ACS nano.

[31]  N. Tennent,et al.  Degradation of epoxy polymers: Part 4—Thermal degradation of bisphenol-A diglycidyl ether cured with ethylene diamine , 1986 .

[32]  L. Ye,et al.  Fracture mechanisms of epoxy-based ternary composites filled with rigid-soft particles , 2012 .

[33]  Steven Nutt,et al.  Covalent polymer functionalization of graphene nanosheets and mechanical properties of composites , 2009 .

[34]  Ana M. Benito,et al.  Flexible conductive graphene paper obtained by direct and gentle annealing of graphene oxide paper , 2012 .

[35]  G. Lai,et al.  Fracture toughness and electrical conductivity of epoxy composites filled with carbon nanotubes and spherical particles , 2013 .

[36]  Hsu-Chiang Kuan,et al.  Covalently bonded interfaces for polymer/graphene composites , 2013 .

[37]  A. Kinloch.  Adhesion and Adhesives: Science and Technology , 2010 .

[38]  X. She,et al.  Synthesis of network reduced graphene oxide in polystyrene matrix by a two-step reduction method for superior conductivity of the composite , 2012 .

[39]  Zhanhu Guo,et al.  Polyaniline stabilized barium titanate nanoparticles reinforced epoxy nanocomposites with high dielectric permittivity and reduced flammability , 2013 .

[40]  Zhong Zhang,et al.  Improved electrical conductivity of polyamide 12/graphene nanocomposites with maleated polyethylene-octene rubber prepared by melt compounding. , 2012, ACS applied materials & interfaces.

[41]  C. Ma,et al.  Thermal conductivity and structure of non-covalent functionalized graphene/epoxy composites , 2011 .

[42]  Lin Li,et al.  Poly(vinyl alcohol) nanocomposites filled with poly(vinyl alcohol)-grafted graphene oxide. , 2012, ACS applied materials & interfaces.

[43]  Zhongyuan Huang,et al.  Chemically modified graphene/polyimide composite films based on utilization of covalent bonding and oriented distribution. , 2012, ACS applied materials & interfaces.

[44]  Jie Jin,et al.  Preparation and characterisation of covalent polymer functionalized graphene oxide , 2011 .

[45]  Lei Song,et al.  In situ preparation of functionalized graphene oxide/epoxy nanocomposites with effective reinforcements , 2011 .

[46]  D. Dean,et al.  Magnetically processed carbon nanotube/epoxy nanocomposites: Morphology, thermal, and mechanical properties , 2010 .

[47]  N. Koratkar,et al.  Enhanced thermal stability in graphene oxide covalently functionalized with 2-amino-4,6-didodecylamino-1,3,5-triazine , 2011 .

[48]  Yen-Hsun Su,et al.  Electrostatic studies of π–π interaction for benzene stacking on a graphene layer , 2011 .

[49]  F. Xia,et al.  Ultrafast graphene photodetector , 2009, CLEO/QELS: 2010 Laser Science to Photonic Applications.

[50]  Lee Luong,et al.  From carbon nanotubes and silicate layers to graphene platelets for polymer nanocomposites. , 2012, Nanoscale.

[51]  N. Koratkar,et al.  Dramatic increase in fatigue life in hierarchical graphene composites. , 2010, ACS applied materials & interfaces.

[52]  Fan Yang,et al.  Control of the functionality of graphene oxide for its application in epoxy nanocomposites , 2013 .

[53]  E. Zussman,et al.  Simultaneous in situ reduction, self-alignment and covalent bonding in graphene oxide/epoxy composites , 2013 .

[54]  J. Wuest,et al.  Interaction of substituted aromatic compounds with graphene. , 2009, Langmuir : the ACS journal of surfaces and colloids.

[55]  Fan Yang,et al.  Attapulgite–graphene oxide hybrids as thermal and mechanical reinforcements for epoxy composites , 2013 .

[56]  Zhong Zhang,et al.  Fracture mechanisms of epoxy filled with ozone functionalized multi-wall carbon nanotubes , 2011 .

[57]  Zhiping Luo,et al.  Polyaniline stabilized magnetite nanoparticle reinforced epoxy nanocomposites. , 2012, ACS applied materials & interfaces.

[58]  T. Chou,et al.  Processing-structure-multi-functional property relationship in carbon nanotube/epoxy composites , 2006 .

[59]  G. Shi,et al.  Strong and ductile poly(vinyl alcohol)/graphene oxide composite films with a layered structure , 2009 .

[60]  K. Friedrich,et al.  Fracture behaviours of in situ silica nanoparticle-filled epoxy at different temperatures , 2008 .

[61]  Huafeng Yang,et al.  Covalent functionalization of chemically converted graphene sheets via silane and its reinforcement , 2009 .

[62]  J. Barrat,et al.  Mechanical testing of glassy and rubbery polymers in numerical simulations: role of boundary conditions in tensile stress experiments. , 2009, The Journal of chemical physics.

[63]  Liping Zhao,et al.  Fabrication of exfoliated graphene-based polypropylene nanocomposites with enhanced mechanical and thermal properties , 2011 .

[64]  Zhongxin Chen,et al.  Bioinspired approaches for optimizing the strength and toughness of graphene-based polymer nanocomposites , 2012 .

[65]  D. Yan,et al.  The effect of graphene dispersion on the mechanical properties of graphene/epoxy composites , 2013 .

[66]  J. Dai,et al.  An efficient way to functionalize graphene sheets with presynthesized polymer via ATNRC chemistry , 2011 .

[67]  Ming-Yu Yen,et al.  Preparation of covalently functionalized graphene using residual oxygen-containing functional groups. , 2010, ACS applied materials & interfaces.

[68]  J. Coleman,et al.  Improving the mechanical properties of graphene oxide based materials by covalent attachment of polymer chains , 2013, Carbon.

[69]  A. Dasari,et al.  Functionalization and reduction of graphene oxide with p-phenylene diamine for electrically conductive and thermally stable polystyrene composites. , 2012, ACS applied materials & interfaces.

[70]  R. Car,et al.  Single Sheet Functionalized Graphene by Oxidation and Thermal Expansion of Graphite , 2007 .

[71]  Yan Wang,et al.  Molecular‐Level Dispersion of Graphene into Poly(vinyl alcohol) and Effective Reinforcement of their Nanocomposites , 2009 .

[72]  L. Brinson,et al.  Functionalized graphene sheets for polymer nanocomposites. , 2008, Nature nanotechnology.

[73]  Lei Song,et al.  Covalent functionalization of graphene with organosilane and its use as a reinforcement in epoxy composites , 2012 .

[74]  D. Gournis,et al.  p-Xylylenediamine intercalation of graphene oxide for the production of stitched nanostructures with a tailored interlayer spacing , 2013 .

[75]  Roberto Car,et al.  Functionalized single graphene sheets derived from splitting graphite oxide. , 2006, The journal of physical chemistry. B.

[76]  Lei Chen,et al.  Tailoring the characteristics of graphite oxide nanosheets for the production of high-performance poly(vinyl alcohol) composites , 2012 .

[77]  A. Ryan,et al.  Toughening by nanostructure , 2008 .

[78]  Qiang Fu,et al.  Enhanced epoxy/silica composites mechanical properties by introducing graphene oxide to the interface. , 2012, ACS applied materials & interfaces.

[79]  D. Yan,et al.  Improved dispersion and interface in the graphene/epoxy composites via a facile surfactant-assisted process , 2013 .

[80]  Hua Bai,et al.  Functional Composite Materials Based on Chemically Converted Graphene , 2011, Advanced materials.

[81]  Q. Fu,et al.  Preparation of polyester/reduced graphene oxide composites via in situ melt polycondensation and simultaneous thermo-reduction of graphene oxide , 2011 .

[82]  Liqun Zhang,et al.  Grafting of Polyester onto Graphene for Electrically and Thermally Conductive Composites , 2012 .

[83]  S. Stankovich,et al.  Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide , 2007 .

[84]  Lee Luong,et al.  A Facile Approach to Chemically Modified Graphene and its Polymer Nanocomposites , 2012 .

[85]  Jang‐Kyo Kim,et al.  Dispersion, interfacial interaction and re-agglomeration of functionalized carbon nanotubes in epoxy composites , 2010 .

[86]  R. Verdejo,et al.  Graphene filled polymer nanocomposites , 2011 .

[87]  Xufeng Zhou,et al.  Mechanical and Thermal Properties of Epoxy Resin Nanocomposites Reinforced with Graphene Oxide , 2012 .

[88]  Jiachun Feng,et al.  Graphene oxide sheets covalently functionalized with block copolymers via click chemistry as reinforcing fillers , 2011 .

[89]  Micah J. Green,et al.  Non-covalent functionalization of pristine few-layer graphene using triphenylene derivatives for conductive poly (vinyl alcohol) composites , 2012 .

[90]  Jie Yin,et al.  Graphene oxide/polybenzimidazole composites fabricated by a solvent-exchange method , 2011 .

[91]  Tapas Kuila,et al.  Enhanced mechanical properties of silanized silica nanoparticle attached graphene oxide/epoxy composites , 2013 .

[92]  J. Coleman,et al.  Liquid Exfoliation of Layered Materials , 2013, Science.