A Study of Sliver in C-Shaped Grain Selectors during Investment Casting of Single-Crystal Superalloy

In this study, the formation mechanism of sliver defects in C-shaped 2D grain selectors during investment casting of single-crystal superalloy was investigated by analyzing the effects of the C-shaped 2D grain selectors on the solidification behavior of superalloy. The physical field properties of the sliver formation and solidification characteristics of CM247LC nickel-based superalloy were determined. The temperature and stress fields were simulated using ProCAST. The results showed that the stress fields of solidification played an essential role in the formation of sliver, indicating that the solidification interval characteristics of the alloy and stress based on the geometry of the C-shaped 2D grain selector are crucial for the formation of sliver. In addition, the origin of sliver depended upon tensile stress during solidification, relying on the constraints of dendrite boundaries. The findings suggested that the joint sections of the starter block—i.e., selector and selector-casting joint of C-shaped selector sections—are stress-sensitive areas where sliver can form readily. Furthermore, sliver is formed in the final stages of solidification and especially originates in the grain selection part where the accumulated thermal stress is high, and there is only a small quantity of liquid phase with a low melting point between the dendrites. Therefore, the solidification and stress conditions generate thermal cracks, which can also cause sliver defects.

[1]  Qingyan Xu,et al.  Generation mechanism and motion behavior of sliver defect in single crystal Ni-based superalloy , 2022, Journal of Materials Science & Technology.

[2]  Ze Zhang,et al.  Temperature effects on deformation substructures and mechanisms of a Ni-based single crystal superalloy , 2021 .

[3]  L. Lou,et al.  Investigating the evolution of freckles into sliver defects in Ni-based single-crystal superalloy castings , 2021 .

[4]  Dichen Li,et al.  Sliver defect formation in single crystal Ni-based superalloy castings , 2020 .

[5]  J. Zhang,et al.  Evolution of Sliver Defect in Ni-Based Single Crystal Superalloy , 2020, Metallurgical and Materials Transactions A.

[6]  Ze Zhang,et al.  Microstructural evolution and creep mechanisms in Ni-based single crystal superalloys: A review , 2020 .

[7]  Qiang Yang,et al.  Grain Orientation Optimization of Two-Dimensional Grain Selector during Directional Solidification of Ni-Based Superalloys , 2020, Materials.

[8]  D. Ma,et al.  Formation of Sliver Defects in Single CrystalCastings of Superalloys , 2019 .

[9]  J. Zhang,et al.  Formation of Sliver Defect in Ni-Based Single Crystal Superalloy , 2019, Metallurgical and Materials Transactions A.

[10]  A. Bührig-Polaczek,et al.  Development of a High-Efficiency Z-Form Selector for Single Crystal Blades and Corresponding Grain Selection Mechanism , 2019, Materials.

[11]  A. Bührig-Polaczek,et al.  Grain Selection in a High-Efficiency 2D Grain Selector During Casting of Single-Crystal Superalloys , 2019, Materials.

[12]  Baicheng Liu,et al.  Numerical simulation of dendrite growth in Ni-based superalloy casting during directional solidification process , 2019, Transactions of Nonferrous Metals Society of China.

[13]  H. Fu,et al.  Formation of Lateral Sliver Defects in the Platform Region of Single-Crystal Superalloy Turbine Blades , 2019, Metallurgical and Materials Transactions A.

[14]  H. Fu,et al.  Formation of Slivers in the Extended Cross‐Section Platforms of Ni‐Based Single Crystal Superalloy , 2018 .

[15]  Shaolin Li,et al.  Experimental investigation and modelling of microstructure degradation in a DS Ni-based superalloy using a quantitative cross-correlation analysis method , 2018, Journal of Alloys and Compounds.

[16]  Hang Zhang,et al.  Simulation and Experimental Studies on Grain Selection and Structure Design of the Spiral Selector for Casting Single Crystal Ni-Based Superalloy , 2017, Materials.

[17]  Li Ma,et al.  Application of Finite Element, Phase-field, and CALPHAD-based Methods to Additive Manufacturing of Ni-based Superalloys. , 2017, Acta materialia.

[18]  Qingyan Xu,et al.  Multi-scale simulation of directional dendrites growth in superalloys , 2016 .

[19]  E. Karamian,et al.  Characterization and Investigation of Grain Selection in Spiral Grain Selectors during Casting Single-Crystal Turbine Blades , 2015 .

[20]  Howard Stone,et al.  On the origin of sliver defects in single crystal investment castings , 2013 .

[21]  H. Dai,et al.  Grain Selection in Spiral Selectors During Investment Casting of Single-Crystal Turbine Blades: Part I. Experimental Investigation , 2011 .

[22]  Z. Hu,et al.  Evolution of Grain Selection in Spiral Selector during Directional Solidification of Nickel-base Superalloys , 2011 .

[23]  S. Manneville,et al.  From stress-induced fluidization processes to Herschel-Bulkley behaviour in simple yield stress fluids , 2010, 1012.0693.

[24]  J. Gebelin,et al.  Effect of spiral shape on grain selection during casting of single crystal turbine blades , 2009 .

[25]  R. Cochrane,et al.  Mechanical deformation of dendrites by fluid flow during the solidification of undercooled melts , 2002 .

[26]  R. Napolitano,et al.  The convergence-fault mechanism for low-angle boundary formation in single-crystal castings , 2000 .

[27]  L. Arnberg,et al.  Modeling the fluid-flow-induced stress and collapse in a dendritic network , 1999 .

[28]  J. Pilling,et al.  Mechanical deformation of dendrites by fluid flow , 1996 .