Hard turning using HiPIMS-coated carbide tools: Wear behavior under dry and minimum quantity lubrication (MQL)

Abstract In the present work, experimental investigations carried out to assess the applicability of HiPIMS (High Power Impulse Magnetron Sputtering)-coated carbide tools to hard turning (55 HRC) and to address the widely debated topic about the use of coolants in hard turning are presented. Tool wear progressions and hence, tool life, different tool wear forms and wear mechanisms observed for tools coated with HiPIMS coating technique, namely, nanocomposite AlTiN, nanocomposite multi-layer TiAlN/TiSiN and nanocrystalline AlTiCrN are presented along with the images captured by digital and electron microscope. Characterization results of all the coated tools in terms of their average coating thickness (measured using Calotest and Fractographs), adhesion strength of the coating(s) (determined using Scratch test), composition and microhardness (using EDAX and Vickers microhardness test, respectively) are presented. Experimental observations indicate higher tool life with nanocrystalline AlTiCrN coated carbide tools which shows encouraging potential of these tools to hard turning. Improvement in tool life of almost 20–25% has been observed under minimum quantity lubrication (MQL) due to better cooling and lubricating effects. However, this effect was more prominent at higher cutting speed of 150 m/min.

[1]  J. Fildes,et al.  Improved ball crater micro-abrasion test based on a ball on three disk configuration , 2012 .

[2]  S. K. Choudhury,et al.  Effect of work material hardness and cutting parameters on performance of coated carbide tool when turning hardened steel: An optimization approach , 2013 .

[3]  J. Alami,et al.  High power pulsed magnetron sputtering: Fundamentals and applications , 2009 .

[4]  F. Schäfers,et al.  Determination of the local environment of silicon and the microstructure of quaternary CrAl(Si)N films , 2007 .

[5]  Arutiun P. Ehiasarian,et al.  Interface microstructure engineering by high power impulse magnetron sputtering for the enhancement of adhesion , 2007 .

[6]  Myung-Chang Kang,et al.  Effect of the minimum quantity lubrication in high-speed end-milling of AISI D2 cold-worked die steel (62 HRC) by coated carbide tools , 2008 .

[7]  John W. Sutherland,et al.  Dry Machining and Minimum Quantity Lubrication , 2004 .

[8]  A. Gilewicz,et al.  Mechanical properties of multilayer TiAlN/CrN coatings deposited by cathodic arc evaporation , 2011 .

[9]  L. Dobrzański,et al.  Structure and properties of the multi-component TiAlSiN coatings obtained in the PVD process in the nitride tool ceramics , 2004 .

[10]  S. Carvalho,et al.  Pvd grown (Ti, Si, Al)N nanocomposite coatings and (Ti, Al)N/(Ti, Si)N multilayers: structural and mechanical properties , 2003 .

[11]  Yunn-Shiuan Liao,et al.  Mechanism of minimum quantity lubrication in high-speed milling of hardened steel , 2007 .

[12]  V. Klemm,et al.  Microstructure and hardness of nanocrystalline Ti1−x−yAlxSiyN thin films , 2007 .

[13]  D. Music,et al.  Ion-assisted physical vapor deposition for enhanced film properties on nonflat surfaces , 2005 .

[14]  L. Settineri,et al.  AlSiTiN nanocomposite coatings developed via Arc Cathodic PVD: Evaluation of wear resistance via tribological analysis and high speed machining operations , 2007 .

[15]  S. Sane,et al.  Characterisation of chromium nitride physical vapour deposition coating on diesel engine pistons , 2006 .

[16]  E. Bourhis,et al.  Effect of TiAlN PVD coatings on corrosion performance of WC–6%Co , 2010 .

[17]  Alexandre M. Abrão,et al.  The effect of cutting fluids on the machining of hardened AISI 4340 steel , 2001 .

[18]  Aldo Attanasio,et al.  Minimal quantity lubrication in turning: Effect on tool wear , 2006 .

[19]  H. Takaoka,et al.  Relationship between an affinity of (Ti1−x, Alx)N layer toward iron and its cutting performance , 2004 .

[20]  R. Galindo,et al.  Wear resistance of titanium–aluminium–chromium–nitride nanocomposite thin films , 2007 .

[21]  N. R. Dhar,et al.  Effects of minimum quantity lubrication on turning AISI 9310 alloy steel using vegetable oil­based cutting fluid , 2009 .

[22]  J. Kim,et al.  Deposition of superhard TiAlSiN thin films by cathodic arc plasma deposition , 2005 .

[23]  N. R. Dhar,et al.  An experimental investigation on effect of minimum quantity lubrication in machining AISI 1040 steel , 2007 .

[24]  P. Panjan,et al.  Comparison of mechanical properties of various PVD hard coatings for forming tools , 2007 .

[25]  L. Settineri,et al.  Evaluation of wear resistance of AlSiTiN and AlSiCrN nanocomposite coatings for cutting tools , 2008 .

[26]  H. Hasegawa,et al.  Microstructures of (Ti,Cr,Al,Si)N films synthesized by cathodic arc method , 2007 .

[27]  Anselmo Eduardo Diniz,et al.  Influence of refrigeration/lubrication condition on SAE 52100 hardened steel turning at several cutting speeds , 2003 .

[28]  I. Korkut,et al.  Determination of optimum cutting parameters during machining of AISI 304 austenitic stainless steel , 2004 .

[29]  A. S. Varadarajan,et al.  Investigations on hard turning with minimal cutting fluid application (HTMF) and its comparison with dry and wet turning , 2002 .

[30]  Sounak Kumar Choudhury,et al.  Experimental investigations to optimise and compare the machining performance of different coated carbide inserts during turning hardened steel , 2014 .

[31]  V. Sargade,et al.  Performance of PVD AlTiCrN coating during machining of austenitic stainless steel , 2013 .

[32]  B. Mishra,et al.  Effect of Pulsed Plasma Processing on Controlling Nanostructure And Properties of Thin Film/Coatings , 2004 .

[33]  S. Deevi,et al.  Single layer and multilayer wear resistant coatings of (Ti,Al)N: a review , 2003 .

[34]  H. Chan,et al.  Converse magnetoelectric effect in three-phase composites of piezoceramic, metal cap, and magnet , 2007 .

[35]  Sounak Kumar Choudhury,et al.  Investigations on machinability aspects of hardened AISI 4340 steel at different levels of hardness using coated carbide tools , 2013 .

[36]  Michela Simoncini,et al.  Effect of the lubrication-cooling technique, insert technology and machine bed material on the workpart surface finish and tool wear in finish turning of AISI 420B , 2006 .