Polymethylsilsesquioxane and hydroxyl-terminated polydimethylsiloxane composite: Vapor incubation before thermal curing

A composite film of polymethylsilsesquioxane (PMSQ) and hydroxyl-terminated polydimethylsiloxane (PDMS) was prepared by incubating PMSQ prepolymer and PDMS solution in a vapor environment before thermal curing. Vapor incubation has a significant influence on the morphology and properties of the cured composite, and the vapor incubation was conducted under three different conditions, i.e., acidic, neutral, and basic. In the acidic vapor of a pH rather lower than the isoelectric point (IEP) of the silanol, the reaction between PMSQ and PDMS through silanol condensation was promoted by the protonation of silanol. PDMS rubber particles with a domain size of about 100 nm were formed in PMSQ matrix, and the flexible modulus of the film was improved. While, the morphology of the resultant film was smooth and uniform after incubation in a neutral water vapor. The basic vapor facilitated the gelation of composite due to high pH inducing more rapid silanol condensation in PMSQ than phase separation. Moreover, excellent optical transparency, insulation, and thermal stability of the composite were also retained after the PDMS incorporation. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009

[1]  D. Y. Yoon,et al.  Infrared Spectroscopy Study of Microstructures of Poly(silsesquioxane)s , 2008 .

[2]  Yudong Huang,et al.  Effects of silsesquioxane coating structure on mechanical interfacial properties of carbon fibre/polyarylacetylene composites , 2007 .

[3]  G. Schmidt-naake,et al.  Synthesis and Characterization of Silsesquioxane Prepolymers Bearing Phenyl and Methacryloxypropyl Groups Obtained by Cohydrolysis , 2007 .

[4]  J. E. Mark.  Some novel polymeric nanocomposites. , 2006, Accounts of chemical research.

[5]  Y. Chujo,et al.  Synthesis of anionic polymer–silica hybrids by controlling pH in an aqueous solution , 2005 .

[6]  F. Mcgarry,et al.  Temperature effect on mechanical properties of toughened silicone resins , 2005 .

[7]  J. Brennan,et al.  A New Route to Monolithic Methylsilsesquioxanes: Gelation Behavior of Methyltrimethoxysilane and Morphology of Resulting Methylsilsesquioxanes under One-Step and Two-Step Processing , 2005 .

[8]  J. Hay,et al.  Preparation of Silsesquioxane Particles via a Nonhydrolytic Sol−Gel Route , 2005 .

[9]  R. Boomishankar,et al.  Recent developments in the synthesis and structure of organosilanols. , 2004, Chemical reviews.

[10]  B. Mather,et al.  Effect of pH on the Gelation Time of Hexylene-Bridged Polysilsesquioxanes , 2004 .

[11]  Y. Abe,et al.  Oligo- and polysiloxanes , 2004 .

[12]  F. Mcgarry,et al.  Toughening of a Polysilsesquioxane Network by Simultaneous Incorporation of Short and Long PDMS Chain Segments , 2004 .

[13]  Wen‐Chang Chen,et al.  Synthesis and characterization of oligomeric phenylsilsesquioxane-titania hybrid optical thin films , 2004 .

[14]  Vladimir V. Tsukruk,et al.  Reorganization of Binary Polymer Brushes: Reversible Switching of Surface Microstructures and Nanomechanical Properties , 2003 .

[15]  Zhengping Zhang,et al.  Methyltrimethoxysilane Sol-Gel Polymerization in Acidic Ethanol Solutions Studied by 29Si NMR Spectroscopy , 2003 .

[16]  D. Y. Yoon,et al.  Observation of low molecular weight poly(methylsilsesquioxane)s by graphite plate laser desorption/ionization time-of-flight mass spectrometry. , 2000, Analytical chemistry.

[17]  F. Mcgarry,et al.  Toughening of a polysilsesquioxane network by homogeneous incorporation of polydimethylsiloxane segments , 2000 .

[18]  W. Wallace,et al.  Polymeric silsesquioxanes: degree-of-intramolecular-condensation measured by mass spectrometry , 2000 .

[19]  Yen Wei,et al.  Atomic Force Microscopy Study of Organic−Inorganic Hybrid Materials , 1998 .

[20]  L. Hornak,et al.  Characterization of poly(phenylsilsesquioxane) thin-film planar optical waveguides , 1997, IEEE Photonics Technology Letters.

[21]  Douglas A. Loy,et al.  BRIDGED POLYSILSESQUIOXANES. HIGHLY POROUS HYBRID ORGANIC-INORGANIC MATERIALS , 1995 .

[22]  A. Takahara,et al.  PHASE SEPARATED MORPHOLOGY OF AN IMMOBILIZED ORGANOSILANE MONOLAYER STUDIED BY A SCANNING PROBE MICROSCOPE , 1995 .

[23]  George W. Scherer,et al.  An organic/inorganic single-phase composite , 1995 .