A damage model for crack prediction in brittle and quasi-brittle materials solved by the FFT method

In this paper, we present a damage model and its numerical solution by means of Fast Fourier Transforms (FFT). The FFT-based formulation initially proposed for linear and non-linear composite homogenization (Moulinec and Suquet in CR Acad Sci Paris Ser II 318:1417–1423 1994; Comput Methods Appl Mech Eng 157:69–94 1998) was adapted to evaluate damage growth in brittle materials. A non-local damage model based on the maximal principal stress criterion was proposed for brittle materials. This non-local model was then connected to the Griffith criterion with the aim of predicting crack growth. By using the proposed model, we carried out several numerical simulations on different specimens in order to assess the fracture process in brittle materials. From these studies, we can conclude that the present FFT-based analysis is capable of dealing with crack initiation and crack growth in brittle materials with high accuracy and efficiency.

[1]  Hervé Moulinec,et al.  A Computational Method Based on Augmented Lagrangians and Fast Fourier Transforms for Composites with High Contrast , 2000 .

[2]  Bhushan Lal Karihaloo,et al.  Lattice modelling of the failure of particle composites , 2003 .

[3]  R. Zimbelmann,et al.  A contribution to the problem of cement-aggregate bond , 1985 .

[4]  Z. Bažant,et al.  Nonlocal damage theory , 1987 .

[5]  M. Williams.  The Bending Stress Distribution at the Base of a Stationary Crack , 1961 .

[6]  J. Michel,et al.  Effective properties of composite materials with periodic microstructure : a computational approach , 1999 .

[7]  Hervé Moulinec,et al.  Macroscopic behavior and field fluctuations in viscoplastic composites: Second-order estimates versus full-field simulations , 2006 .

[8]  G. C. Sih,et al.  Handbook of stress-intensity factors : stress-intensity factor solutions and formulas for reference , 1973 .

[9]  Hervé Moulinec,et al.  A numerical method for computing the overall response of nonlinear composites with complex microstructure , 1998, ArXiv.

[10]  G. Bonnet,et al.  Green’s operator for a periodic medium with traction-free boundary conditions and computation of the effective properties of thin plates , 2008 .

[11]  Yi Liu,et al.  On the accuracy of the self-consistent approximation for polycrystals: comparison with full-field numerical simulations , 2004 .

[12]  J. Mier,et al.  3D lattice type fracture model for concrete , 2003 .

[13]  Michel Bornert,et al.  Bounds and estimates for the effective yield surface of porous media with a uniform or a nonuniform distribution of voids , 2007 .

[14]  Modelling the failure behaviour of brittle or quasi-brittle materials by analysing the growth of micro-cracks , 2009 .

[15]  G. R. Irwin,et al.  Linear fracture mechanics, fracture transition, and fracture control , 1968 .

[16]  Martin Ostoja-Starzewski,et al.  Spring network models in elasticity and fracture of composites and polycrystals , 1996 .

[17]  Alberto Carpinteri,et al.  Boundary element method for the strain-softening response of quasi-brittle materials in compression , 2001 .

[18]  A. Paskin,et al.  Molecular dynamic simulations of crack propagation , 1987 .

[19]  Alberto Carpinteri,et al.  Size effects in brittle specimen with microcrack interaction , 1997 .

[20]  J. Lankford.  THE INFLUENCE OF MICROSTRUCTURE ON THE GROWTH OF SMALL FATIGUE CRACKS , 1985 .

[21]  E. Bringa,et al.  A viscoplastic micromechanical model for the yield strength of nanocrystalline materials , 2006 .

[22]  Harold S. Park,et al.  An introduction to computational nanomechanics and materials , 2004 .

[23]  H. Moulinec,et al.  A fast numerical method for computing the linear and nonlinear mechanical properties of composites , 1994 .

[24]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .

[25]  M. Mullins.  Molecular dynamics simulation of propagating cracks , 1982 .

[26]  N. Frost,et al.  A Relation between the Critical Alternating Propagation Stress and Crack Length for Mild Steel , 1959 .