Enhancing the Performance of Quantum Dot Light-Emitting Diodes Using Solution-Processable Highly Conductive Spinel Structure CuCo2O4 Hole Injection Layer

Charge imbalance in quantum-dot light-emitting diodes (QLEDs) causes emission degradation. Therefore, many studies focused on improving hole injection into the QLEDs-emitting layer owing to lower hole conductivity compared to electron conductivity. Herein, CuCo2O4 has a relatively higher hole conductivity than other binary oxides and can induce an improved charge balance. As the annealing temperature decreases, the valence band maximum (VBM) of CuCo2O4 shifts away from the Fermi energy level (EF), resulting in an enhanced hole injection through better energy level alignment with hole transport layer. The maximum luminance and current efficiency of the CuCo2O4 hole injection layer (HIL) of the QLED were measured as 93,607 cd/m2 and 11.14 cd/A, respectively, resulting in a 656% improvement in luminous performance of QLEDs compared to conventional metal oxide HIL-based QLEDs. These results demonstrate that the electrical properties of CuCo2O4 can be improved by adjusting the annealing temperature, suggesting that solution-processed spinel can be applied in various optoelectronic devices.

[1]  H. Yu,et al.  Investigation of quantum dots light emitting diodes with different transition metal oxide as charge injection layers , 2022, Organic Electronics.

[2]  P. Smowton,et al.  Solution-processed Colloidal Quantum Dots for Light Emission , 2022, Materials Advances.

[3]  Yongsup Park,et al.  Al-doped TiO2 interfacial layer for effective hole injection characteristics of quantum-dot light emitting diodes , 2022, Journal of Materials Chemistry C.

[4]  Yu Qin,et al.  Metal oxide heterojunctions for high performance solution grown oxide thin film transistors , 2020 .

[5]  Jun Li,et al.  Synergistic effects of Li-doped NiO film prepared by low-temperature combustion as hole-injection layer for high performance OLED devices , 2020 .

[6]  A. Hagfeldt,et al.  Highly efficient, stable and hysteresis‒less planar perovskite solar cell based on chemical bath treated Zn2SnO4 electron transport layer , 2020 .

[7]  A. W. Maijenburg,et al.  Synthesis and Characterization of Spinel Cobaltite (Co3O4) Thin Films for Function as Hole Transport Materials in Organometallic Halide Perovskite Solar Cells , 2020 .

[8]  J. Jung,et al.  A Solution-Processed Spinel CuCo2O4 as an Effective Hole Transport Layer for Efficient Perovskite Solar Cells with Negligible Hysteresis , 2019, ACS Sustainable Chemistry & Engineering.

[9]  Shengdong Zhang,et al.  Beyond OLED: Efficient Quantum Dot Light-Emitting Diodes for Display and Lighting Application. , 2019, Chemical record.

[10]  W. Choy,et al.  Solution‐Processed Ternary Oxides as Carrier Transport/Injection Layers in Optoelectronics , 2019, Advanced Energy Materials.

[11]  U. Pal,et al.  Structural, Magnetic, and Catalytic Evaluation of Spinel Co, Ni, and Co–Ni Ferrite Nanoparticles Fabricated by Low-Temperature Solution Combustion Process , 2018, ACS omega.

[12]  M. Fung,et al.  Cu-Doped nickel oxide prepared using a low-temperature combustion method as a hole-injection layer for high-performance OLEDs , 2017 .

[13]  Fan Cao,et al.  High‐Efficiency and Stable Quantum Dot Light‐Emitting Diodes Enabled by a Solution‐Processed Metal‐Doped Nickel Oxide Hole Injection Interfacial Layer , 2017 .

[14]  Jang-kun Song,et al.  Quantum dot light-emitting diodes using a graphene oxide/PEDOT:PSS bilayer as hole injection layer , 2017 .

[15]  S. E. Moosavifard,et al.  Designing graphene-wrapped nanoporous CuCo2O4 hollow spheres electrodes for high-performance asymmetric supercapacitors , 2017 .

[16]  Hong-Ying Chen,et al.  Preparation of p-type CuCo2O4 thin films by sol-gel processing , 2017 .

[17]  Jaehoon Lim,et al.  Spectroscopic and Device Aspects of Nanocrystal Quantum Dots. , 2016, Chemical reviews.

[18]  V. Ponnuswamy,et al.  Cobalt oxide thin films prepared by NSP technique: Impact of molar concentration on the structural, optical, morphological and electrical properties , 2016 .

[19]  P. K. Nayak,et al.  Recent Developments in p‐Type Oxide Semiconductor Materials and Devices , 2016, Advanced materials.

[20]  Yang Zhao,et al.  Recent Developments and Understanding of Novel Mixed Transition‐Metal Oxides as Anodes in Lithium Ion Batteries , 2016 .

[21]  W. Lei,et al.  Size Tunable ZnO Nanoparticles To Enhance Electron Injection in Solution Processed QLEDs , 2016 .

[22]  X. W. Sun,et al.  Colloidal quantum-dot LEDs with a solution-processed copper oxide (CuO) hole injection layer , 2015 .

[23]  W. Choy,et al.  Post‐treatment‐Free Solution‐Processed Non‐stoichiometric NiOx Nanoparticles for Efficient Hole‐Transport Layers of Organic Optoelectronic Devices , 2015, Advanced materials.

[24]  Ki-Seok An,et al.  Performance Improvement of Quantum Dot-Light-Emitting Diodes Enabled by an Alloyed ZnMgO Nanoparticle Electron Transport Layer , 2015 .

[25]  Rasit Turan,et al.  Influence of thermal annealing on microstructural, morphological, optical properties and surface electronic structure of copper oxide thin films , 2014 .

[26]  Chun‐Sing Lee,et al.  Porous CuCo2O4 nanocubes wrapped by reduced graphene oxide as high-performance lithium-ion battery anodes. , 2014, Nanoscale.

[27]  Gerbrand Ceder,et al.  Identification and design principles of low hole effective mass p-type transparent conducting oxides , 2013, Nature Communications.

[28]  Linfeng Hu,et al.  Electrical Transport Properties of Large, Individual NiCo2O4 Nanoplates , 2012 .

[29]  Xingbo Liu,et al.  Electrophoretic deposition of (Mn,Co) 3O 4 spinel coating for solid oxide fuel cell interconnects , 2011 .

[30]  Hong Lin,et al.  Photophysical and Photocatalytic Properties of Core-Ring Structured NiCo2O4 Nanoplatelets , 2009 .

[31]  Alex Zunger,et al.  Origins of the p-Type Nature and Cation Deficiency in Cu2O and Related Materials , 2007 .

[32]  T. He,et al.  Solubility-Controlled Synthesis of High-Quality Co3O4 Nanocrystals , 2005 .

[33]  J. Koberstein,et al.  Copper oxide nanocrystals. , 2005, Journal of the American Chemical Society.

[34]  H. Ohta,et al.  Room-temperature fabrication of transparent flexible thin-film transistors using amorphous oxide semiconductors , 2004, Nature.

[35]  V. Parmon,et al.  Metal-support interactions in cobalt-aluminum co-precipitated catalysts: XPS and CO adsorption studies , 2001 .

[36]  Sergio Daolio,et al.  Composition and Microstructure of Cobalt Oxide Thin Films Obtained from a Novel Cobalt(II) Precursor by Chemical Vapor Deposition , 2001 .

[37]  Weidong Yang,et al.  Shape control of CdSe nanocrystals , 2000, Nature.

[38]  M. Bawendi,et al.  (CdSe)ZnS Core-Shell Quantum Dots - Synthesis and Characterization of a Size Series of Highly Luminescent Nanocrystallites , 1997 .

[39]  J. L. Gautier,et al.  Characterization of thin CuCo2O4 films prepared by chemical spray pyrolysis. Study of their electrochemical stability by ex situ spectroscopic analysis , 1997 .

[40]  L. Tjeng,et al.  Electronic structure of Cu2O and CuO. , 1988, Physical review. B, Condensed matter.

[41]  Masahiro Nishikawa,et al.  Hall measurement studies and an electrical conduction model of tin oxide ultrafine particle films , 1982 .

[42]  G. Sawatzky,et al.  SATELLITE STRUCTURE IN PHOTOELECTRON AND AUGER-SPECTRA OF COPPER DIHALIDES , 1981 .

[43]  L. Yin,et al.  X-ray photoelectron spectroscopy of nickel compounds , 1973 .