Application of Nanomechanical Methods in Investigation of C–S–H Gel/Cement Grain Interface

Investigation on the mechanical properties of cement-based materials at micron and submicron scales is important for understanding the overall performance, particularly of high-performance concrete (HPC). Due to low water-tocement ratio of HPC, a large amount of unhydrated cement grains remain in matrix, and a significant impact of the interface between C–S–H gel and cement grains on concrete behavior could be expected. Recent progress in experimental nanomechanics opens new access to nanoengineering of cement-based composites. In this paper, nanoindentation and viscoelastic modulus mapping were used to study the interfacial properties. The interface width measured by modulus mapping was around 200 nm as compared to a rough estimation of less than 5 μm by nanoindentation, due to the fact that two orders of magnitude increase in spatial resolution could be achieved with modulus mapping.

[1]  Surendra P. Shah,et al.  Properties of interfacial transition zones in recycled aggregate concrete tested by nanoindentation , 2013 .

[2]  J. A. Ohlhausen,et al.  Measurement of elastic properties of calcium silicate hydrate with atomic force microscopy , 2012 .

[3]  W. Yao,et al.  Nano-scratch as a new tool for assessing the nano-tribological behavior of cement composite , 2011 .

[4]  V. Li,et al.  Nanoscale characterization of engineered cementitious composites (ECC) , 2011 .

[5]  M. Jirásek,et al.  Critical aspects of nano-indentation technique in application to hardened cement paste , 2011 .

[6]  Franz-Josef Ulm,et al.  Nanogranular packing of C–S–H at substochiometric conditions , 2010 .

[7]  François Toutlemonde,et al.  The nano-mechanical signature of Ultra High Performance Concrete by statistical nanoindentation techniques , 2008 .

[8]  Mahalia Miller,et al.  Surface Roughness Criteria for Cement Paste Nanoindentation , 2008 .

[9]  Surendra P. Shah,et al.  Nanoscale Characterization of Cementitious Materials , 2008 .

[10]  Surendra P. Shah,et al.  A Reliable Technique to Determine the Local Mechanical Properties at the Nanoscale for Cementitious Materials , 2007 .

[11]  Jeffrey J. Thomas,et al.  A multi-technique investigation of the nanoporosity of cement paste , 2007 .

[12]  F. Ulm,et al.  The nanogranular nature of C–S–H , 2007 .

[13]  Matthew J. DeJong,et al.  The nanogranular behavior of C-S-H at elevated temperatures (up to 700 °C) , 2007 .

[14]  G W Marshall,et al.  Evaluation of a new modulus mapping technique to investigate microstructural features of human teeth. , 2004, Journal of biomechanics.

[15]  F. Ulm,et al.  The effect of two types of C-S-H on the elasticity of cement-based materials: Results from nanoindentation and micromechanical modeling , 2004 .

[16]  F. Ulm,et al.  On the use of nanoindentation for cementitious materials , 2003 .

[17]  Denis Damidot,et al.  Determination by nanoindentation of elastic modulus and hardness of pure constituents of Portland cement clinker , 2001 .

[18]  J. E. Gillott,et al.  Microstructural investigation of innovative UHPC , 1999 .

[19]  P. Richard,et al.  Composition of reactive powder concretes , 1995 .

[20]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .