Nanosized Nb-TiO/sub 2/ gas sensors derived from alkoxides hydrolization

Nanocrystalline TiO/sub 2/ modified with Nb has been produced through the sol-gel technique. Nanopowders have been obtained by means of the hydrolysis of pure alkoxides with deionized water and peptization of the resulting hydrolysate with diluted acid nitric at 100/spl deg/C. The addition of Nb stabilizes the anatase phase to higher temperatures. XRD spectra of the undoped and the Nb-doped samples show that the undoped sample has been almost totally converted to rutile at 600/spl deg/C, meanwhile the doped samples present still a low percentage of rutile phase. Nanocrystalline powders stabilized at 600/spl deg/C with grain sizes of about 17 nm have successfully been synthesized by the addition of Nb with a concentration of 2% at., which appears to be an adequate additive concentration to improve the gas sensor performances, such as it is suggested by the catalytic conversion efficiency experiments performed from FTIR measurements. FTIR absorbance spectra show that catalytic conversion of CO occurs at lower temperatures when niobium is introduced. The electrical response of the films to different concentrations of CO and ethanol has been monitored in dry and wet environments in order to test the influence of humidity in the sensor response. The addition of Nb decreases the working temperature and increases the stability of the layers. Also, large enhancement of the response time is obtained even with lower working temperatures. Moreover, humidity effects on the gas sensor response toward CO and ethanol are less important in Nb-doped samples than in the undoped ones.

[1]  Kui Yao,et al.  Platinum-titania oxygen sensors and their sensing mechanisms , 1993 .

[2]  R. Ionescu,et al.  Role of water vapour in the interaction of SnO2 gas sensors with CO and CH4 , 1999 .

[3]  V. Brynzari,et al.  Electrical behavior of SnO2 thin films in humid atmosphere , 1999 .

[4]  Giorgio Sberveglieri,et al.  TiO2 thin films by a novel sol–gel processing for gas sensor applications , 2000 .

[5]  G. Martinelli,et al.  Preparation of nanosized titania thick and thin films as gas-sensors , 1999 .

[6]  J. Bartlett,et al.  Effect of Ageing on the Formation, Structure and Crystallisation of Titania Colloids , 1994 .

[7]  G. Martinelli,et al.  Structural characterization of Nb–TiO2 nanosized thick-films for gas sensing application , 2000 .

[8]  The environmental control of atmospheric pollution. The framework directive and its development. The new European approach , 1999 .

[9]  Vincenzo Guidi,et al.  Doping of a nanostructured titania thick film: structural and electrical investigations , 2000 .

[10]  R. Ionescu,et al.  Time-dependent humidity calibration for drift corrections in electronic noses equipped with SnO2 gas sensors , 2000 .

[11]  Giorgio Sberveglieri,et al.  Titanium dioxide thin films prepared for alcohol microsensor applications , 2000 .

[12]  Muralidhar K. Ghantasala,et al.  Sensitivity enhancement towards ethanol and methanol of TiO2 films doped with Pt and Nb , 2000 .

[13]  Jordi Arbiol,et al.  Surface activation by Pt-nanoclusters on titania for gas sensing applications , 2002 .

[14]  Prabir K. Dutta,et al.  Titanium dioxide based high temperature carbon monoxide selective sensor , 2001 .

[15]  N. Bârsan,et al.  Micromachined metal oxide gas sensors: opportunities to improve sensor performance , 2001 .

[16]  Prabir K. Dutta,et al.  Interaction of Carbon Monoxide with Anatase Surfaces at High Temperatures: Optimization of a Carbon Monoxide Sensor , 1999 .

[17]  Matteo Ferroni,et al.  Nanostructured pure and Nb-doped TiO2 as thick film gas sensors for environmental monitoring , 1999 .

[18]  M. Carotta,et al.  Preparation and characterization of nanosized titania sensing film , 2001 .