A distributed real-time model of degradation in a solid oxide fuel cell, part II: Analysis of fuel cell performance and potential failures

Abstract Solid oxide fuel cells are characterized by very high efficiency, low emissions level, and large fuel flexibility. Unfortunately, their elevated costs and relatively short lifetimes reduce the economic feasibility of these technologies at the present time. Several mechanisms contribute to degrade fuel cell performance during time, and the study of these degradation modes and potential mitigation actions is critical to ensure the durability of the fuel cell and their long-term stability. In this work, localized degradation of a solid oxide fuel cell is modeled in real-time and its effects on various cell parameters are analyzed. Profile distributions of overpotential, temperature, heat generation, and temperature gradients in the stack are investigated during degradation. Several causes of failure could occur in the fuel cell if no proper control actions are applied. A local analysis of critical parameters conducted shows where the issues are and how they could be mitigated in order to extend the life of the cell.

[1]  Mogens Bjerg Mogensen,et al.  Solid Oxide Fuel Cell Performance under Severe Operating Conditions , 2006 .

[2]  G. Krishnan,et al.  Effect of various coal contaminants on the performance of solid oxide fuel cells: Part II. ppm and sub-ppm level testing , 2009 .

[3]  Harumi Yokokawa,et al.  Thermodynamic and kinetic considerations on degradations in solid oxide fuel cell cathodes , 2008 .

[4]  Daniel Favrat,et al.  Progressive activation of degradation processes in solid oxide fuel cell stacks: Part II: Spatial distribution of the degradation , 2012 .

[5]  Norbert H. Menzler,et al.  Stack Degradation in Dependence of Operation Parameters; the Real‐SOFC Sensitivity Analysis , 2009 .

[6]  Peter Vang Hendriksen,et al.  Assessment of the Cathode Contribution to the Degradation of Anode-Supported Solid Oxide Fuel Cells , 2008 .

[7]  Ayyakkannu Manivannan,et al.  The Role of Solid Oxide Fuel Cells in Advanced Hybrid Power Systems of the Future , 2009 .

[8]  Palitha Jayaweera,et al.  Effect of various coal contaminants on the performance of solid oxide fuel cells: Part I. Accelerated testing , 2009 .

[9]  D. Favrat,et al.  Progressive activation of degradation processes in solid oxide fuel cells stacks: Part I: Lifetime extension by optimisation of the operating conditions , 2012 .

[10]  Gregory A. Hackett,et al.  Interaction of nickel-based SOFC anodes with trace contaminants from coal-derived synthesis gas. , 2011 .

[11]  Peter Vang Hendriksen,et al.  Degradation of Anode Supported SOFCs as a Function of Temperature and Current Load , 2006 .

[12]  Alberto Traverso,et al.  A distributed real-time model of degradation in a solid oxide fuel cell, part I: Model characterization , 2016 .

[13]  Akira Ueno,et al.  Investigation on Degradation in Long-Term Operations of Four Different Stack/Modules , 2007 .

[14]  Nigel P. Brandon,et al.  The effect of current density and temperature on the degradation of nickel cermet electrodes by carbon monoxide in solid oxide fuel cells , 2009 .

[15]  Tomoo Iwata,et al.  Characterization of Ni‐YSZ Anode Degradation for Substrate‐Type Solid Oxide Fuel Cells , 1996 .

[16]  F. Tietz,et al.  Structure – Property Relationships of Ni/YSZ and Ni/(YSZ+TiO2) Cermets , 2001 .

[17]  C. Adjiman,et al.  Anode-supported intermediate temperature direct internal reforming solid oxide fuel cell. I: model-based steady-state performance , 2004 .

[18]  Alberto Traverso,et al.  A Real-Time Degradation Model for Hardware in the Loop Simulation of Fuel Cell Gas Turbine Hybrid Systems , 2015 .

[19]  David Tucker,et al.  A Real-Time Spatial SOFC Model for Hardware-Based Simulation of Hybrid Systems , 2011 .

[20]  Harumi Yokokawa,et al.  Thermodynamic considerations on Cr poisoning in SOFC cathodes , 2006 .

[21]  E. Ivers-Tiffée,et al.  Materials and technologies for SOFC-components , 2001 .

[22]  J. Brouwer,et al.  A Finite Volume SOFC Model for Coal-Based Integrated Gasification Fuel Cell Systems Analysis , 2009 .

[23]  I. Yasuda,et al.  3-D model calculation for planar SOFC , 2001 .

[24]  Shunsuke Taniguchi,et al.  Influence of water vapor on long-term performance and accelerated degradation of solid oxide fuel cell cathodes , 2011 .

[25]  Stephen J. Skinner,et al.  Impedance studies of cathode/electrolyte behaviour in SOFC , 2008 .