Corrosion of Epoxy-Coated Rebar in Marine Bridges—Part 1: A 30-Year Perspective

Abstract The corrosion performance over a nearly 30-year service period of epoxy-coated rebar (ECR) in Florida marine bridges is presented. Severe ECR corrosion was noted earlier in several of those bridges, built with relatively high permeability concrete. Corrosion development took place later in some other structures with less permeable concrete, with instances where the corrosion was associated with preexisting cracks. Corrosion was found to be associated with coating imperfections and coating disbondment. Laboratory experiments and modeling indicated that macrocell coupling with remote cathodes was an aggravating factor. Quantitative damage functions relating the observed deterioration with service time of the affected bridges are presented. A predictive corrosion initiation-propagation model was developed and the model output is compared with the field results to identify suitable parameters for forecasting future rehabilitation needs. The prognosis for future corrosion development is discussed, wit...

[1]  S. C. Kranc,et al.  CORROSION FORECASTING FOR 75-YEAR DURABILITY DESIGN OF REINFORCED CONCRETE , 2001 .

[2]  A. Bentur.  Steel corrosion in concrete , 1997 .

[3]  Rodney G. Powers,et al.  Corrosion Performance of Epoxy-Coated Reinforcing Steel in Marine Substructure Service , 1991 .

[4]  Andrés A. Torres-Acosta,et al.  Concrete Cracking by Localized Steel Corrosion-Geometric Effects , 2004 .

[5]  Rodney G. Powers,et al.  Corrosion of Epoxy-Coated Rebar in Marine Bridges—Part 2: Corrosion in Cracked Concrete , 2010 .

[6]  Alberto A. Sagüés,et al.  Corrosion Evaluation of Bridges with Epoxy-Coated Rebar , 2009 .

[7]  Tinh Nguyen,et al.  Modes and mechanisms for the degradation of fusion-bonded epoxy-coated steel in a marine concrete environment , 2004 .

[8]  Rodney G. Powers,et al.  Coating Disbondment in Epoxy-Coated Reinforcing Steel in Concrete ? Field Observations , 1996 .

[9]  David B. McDonald,et al.  Corrosion Evaluation of Epoxy-coated, Metallic-clad and Solid Metallic Reinforcing Bars in Concrete , 2002 .

[10]  M. Raupach.  CHLORIDE-INDUCED MACROCELL CORROSION OF STEEL IN CONCRETE - THEORETICAL BACKGROUND AND PRACTICAL CONSEQUENCES , 1996 .

[11]  S. C. Kranc,et al.  CORROSION OF EPOXY COATED REBAR IN FLORIDA BRIDGES. FINAL REPORT , 1994 .

[12]  K. Tuutti.  Corrosion of steel in concrete , 1982 .

[13]  William H. Hartt,et al.  Condition Assessment and Deterioration Rate Projection for Chloride Contaminated Reinforced Concrete Structures , 1997 .

[14]  Rodney G. Powers,et al.  Corrosion processes and field performance of epoxy-coated reinforcing steel in marine substructures , 1994 .

[15]  Ns Berke,et al.  ESTIMATING THE LIFE CYCLE OF REINFORCED CONCRETE DECKS AND MARINE PILES USING LABORATORY DIFFUSION AND CORROSION DATA , 1992 .

[16]  Alberto A. Sagüés,et al.  Modeling the Effects of Corrosion on the Lifetime of Extended Reinforced Concrete Structures , 2003 .