Effect of resin and fibre properties on impact and compression after impact performance of CFRP

Abstract The effect of resin and fibre properties on composite impact, compression after impact (CAI) and mode II energy release rate (GIIC) performance has been studied. Impact events were instrumented to record values of Pc, the critical load for initiation of impact damage. Impact response of the laminates was strongly influenced by the fracture toughness of the resin. In contrast, use of high strength and high stiffness fibres did not improve the resistance to impact. The differences in impact and CAI response of the laminates were largely a consequence of the impact damage created at the damage threshold, Pc, rather than of the differences in delamination growth. As a strong correlation was found between GIIC values measured by delamination tests, and those calculated from measurements of Pc, it is suggested that instrumented impact testing may be a more convenient way of determining GIIC in CFRP laminates than delamination tests.

[1]  S. Abrate.  Impact on Laminated Composite Materials , 1991 .

[2]  H. P. Kan.  Enhanced Reliability Prediction Methodology for Impact Damaged Composite Structures , 1998 .

[3]  W. Cantwell,et al.  Comparison of the low and high velocity impact response of cfrp , 1989 .

[4]  G.A.O. Davies,et al.  Numerical modelling of impact damage , 1994 .

[5]  X. Zhang,et al.  IMPACT DAMAGE PREDICTION IN CARBON COMPOSITE STRUCTURES , 1995 .

[6]  The Influence of Velocity in Low-Velocity Impact Testing of Composites Using the Drop Weight Impact Tower , 1995 .

[7]  Tadaharu Adachi,et al.  Characterization of Impact Damage Resistance of CF/PEEK and CF/Toughened Epoxy Laminates under Low and High Velocity Impact Tests , 1997 .

[8]  J. G. Williams,et al.  Fracture of Polymers, Composites and Adhesives , 2000 .

[9]  Serge Abrate,et al.  Delamination threshold loads for low velocity impact on composite laminates , 2000 .

[10]  Paul Straznicky,et al.  Effects of stacking sequence on the impact resistance in composite laminates — Part 1: parametric study , 1998 .

[11]  Bhavani V. Sankar,et al.  Indentation-flexure and low-velocity impact damage in graphite/epoxy laminates , 1993 .

[12]  Dahsin Liu,et al.  Impact-Induced Delamination—A View of Bending Stiffness Mismatching , 1988 .

[13]  J. C. Prichard,et al.  The role of impact damage in post-impact compression testing , 1990 .

[14]  Serge Abrate,et al.  Impact on Laminated Composites: Recent Advances , 1994 .

[15]  W. Bascom,et al.  A microscopy study of impact damage of epoxy-matrix carbon-fibre composites , 1986 .

[16]  Inelastic Energy Curves: A Tool for Evaluating the Impact Response of Composite Plates , 1995 .

[17]  X. Zhang,et al.  Impact damage in composite aircraft structures-experimental testing and numerical simulation , 1998 .

[18]  R. Kemp,et al.  The effect of stacking sequence on impact damage in a carbon fibre/epoxy composite , 1995 .

[19]  Donald F. Adams,et al.  Instrumented drop weight impact testing of cross-ply and fabric composites , 1985 .