PEC thermography for imaging multiple cracks from rolling contact fatigue

With the development and operation of high speed trains, condition based maintenance becomes an important approach for the improvement of reliability and safety of rail transportation. This paper reports a feasibility study using pulsed eddy current thermography for imaging multiple cracks caused by rolling contact fatigue (RCF). After reviewing rail track inspection and RCF cracks, a PEC thermography system is introduced and applied to the imaging of multiple rolling contact fatigue cracks. Potential on-line inspection for rail track is also discussed.

[1]  Paul O'Leary,et al.  Thermographic crack detection and failure classification , 2010, J. Electronic Imaging.

[2]  Paul O'Leary,et al.  Motion deblurring of infrared images from a microbolometer camera , 2010 .

[3]  Kristoffer Bruzelius,et al.  An initial investigation on the potential applicability of Acoustic Emission to rail track fault detection , 2004 .

[4]  Joseph L. Rose,et al.  A guided wave approach to defect detection under shelling in rail , 2009 .

[5]  Hans-Martin Thomas,et al.  NDT techniques for railroad wheel and gauge corner inspection , 2004 .

[6]  Beate Oswald-Tranta,et al.  Thermo-Inductive Surface Crack Detection in Metallic Materials , 2006 .

[7]  Gui Yun Tian,et al.  Quantitative evaluation of angular defects by pulsed eddy current thermography , 2010 .

[8]  C. Davis,et al.  Very early stage rolling contact fatigue crack growth in pearlitic rail steels , 2011 .

[9]  Robin Clark,et al.  Rail flaw detection: overview and needs for future developments , 2004 .

[10]  Gemma Nicholson,et al.  Modelling and experimental measurements of idealised and light-moderate RCF cracks in rails using an ACFM sensor , 2011 .

[11]  P. Cawley,et al.  Excitation of Surface Wave Modes in Rails and their Application for Defect Detection , 2006 .

[12]  Gernot Wally,et al.  The influence of crack shapes and geometries on the results of the thermo-inductive crack detection , 2007, SPIE Defense + Commercial Sensing.

[13]  W. J. Wang,et al.  Study on relationship between oblique fatigue crack and rail wear in curve track and prevention , 2009 .

[14]  Stuart L. Grassie,et al.  Rolling contact fatigue on the British railway system: treatment , 2005 .

[15]  Clive Roberts,et al.  High-speed inspection of rails using ACFM techniques , 2009 .

[16]  S. L. Grassie,et al.  Rail defects: an overview , 2003 .

[17]  Gui Yun Tian,et al.  Modelling and evaluation of eddy current stimulated thermography , 2010 .

[18]  Rachel S. Edwards,et al.  Characterisation of defects in the railhead using ultrasonic surface waves , 2006 .

[19]  W. Arnold,et al.  MECHANISMS AND MODELS FOR CRACK DETECTION WITH INDUCTION THERMOGRAPHY , 2008 .