Thermoelectric properties of InxGa1−xN alloys

Thermoelectric (TE) properties of InxGa1−xN alloys grown by metal organic chemical vapor deposition have been investigated. It was found that as indium concentration increases, the thermal conductivity decreases and power factor increases, which leads to an increase in the TE figure of merit (ZT). The value of ZT was found to be 0.08 at 300K and reached 0.23 at 450K for In0.36Ga0.64N alloy, which is comparable to those of SiGe based alloys. The results indicate that InGaN alloys could be potentially important TE materials for many applications, especially for prolonged TE device operation at high temperatures, such as for recovery of waste heat from automobile, aircrafts, and power plants due to their superior physical properties, including the ability of operating at high temperature/high power conditions, high mechanical strength and stability, and radiation hardness.Thermoelectric (TE) properties of InxGa1−xN alloys grown by metal organic chemical vapor deposition have been investigated. It was found that as indium concentration increases, the thermal conductivity decreases and power factor increases, which leads to an increase in the TE figure of merit (ZT). The value of ZT was found to be 0.08 at 300K and reached 0.23 at 450K for In0.36Ga0.64N alloy, which is comparable to those of SiGe based alloys. The results indicate that InGaN alloys could be potentially important TE materials for many applications, especially for prolonged TE device operation at high temperatures, such as for recovery of waste heat from automobile, aircrafts, and power plants due to their superior physical properties, including the ability of operating at high temperature/high power conditions, high mechanical strength and stability, and radiation hardness.

[1]  B. C. Daly,et al.  Optical pump-and-probe measurement of the thermal conductivity of nitride thin films , 2002 .

[2]  E. F. Steigmeier,et al.  Thermal and Electrical Properties of Heavily Doped Ge‐Si Alloys up to 1300°K , 1964 .

[3]  D. Cahill.  Thermal conductivity measurement from 30 to 750 K: the 3ω method , 1990 .

[4]  P. Schley,et al.  Universality of electron accumulation at wurtzite c- and a-plane and zinc-blende InN surfaces , 2007 .

[5]  Ali Shakouri,et al.  ErAs:InGaAs∕InGaAlAs superlattice thin-film power generator array , 2006, Applied Physics Letters.

[6]  Gang Chen,et al.  1ω,2ω, and 3ω methods for measurements of thermal properties , 2005 .

[7]  A. Balandin,et al.  Thermoelectric effects in wurtzite GaN and AlxGa1−xN alloys , 2005 .

[8]  D. Cahill,et al.  Thermal conductivity of a-Si:H thin films. , 1994, Physical review. B, Condensed matter.

[9]  S. S. Ballard,et al.  New Data on the Thermal Conductivity of Optical Crystals , 1951 .

[10]  R. Venkatasubramanian,et al.  Thin-film thermoelectric devices with high room-temperature figures of merit , 2001, Nature.

[11]  Rama Venkatasubramanian,et al.  Thermal conductivity of Si–Ge superlattices , 1997 .

[12]  P. Bhattacharya,et al.  Semiconductor Optoelectronic Devices , 1993 .

[13]  Robert O. Pohl,et al.  The intrinsic thermal conductivity of AIN , 1987 .

[14]  Sadao Adachi,et al.  Lattice thermal resistivity of III–V compound alloys , 1983 .

[15]  Mildred S. Dresselhaus,et al.  Effect of quantum-well structures on the thermoelectric figure of merit. , 1993, Physical Review B (Condensed Matter).

[16]  Atsushi Yamamoto,et al.  Thermal diffusivity and thermoelectric figure of merit of Al1−xInxN prepared by reactive radio-frequency sputtering , 2003 .

[17]  L. Lu,et al.  3ω method for specific heat and thermal conductivity measurements , 2001, quant-ph/0202038.

[18]  J. Pankove,et al.  Thermal Conductivity of GaN, 25-360 K , 1977 .

[19]  Chris G. Van de Walle,et al.  Microscopic origins of surface states on nitride surfaces , 2007 .

[20]  George S. Nolas,et al.  Thermoelectrics: Basic Principles and New Materials Developments , 2001 .

[21]  Ali Shakouri,et al.  Thermal conductivity of Si/SiGe and SiGe/SiGe superlattices , 2002 .

[22]  Kang L. Wang,et al.  Measurements of anisotropic thermoelectric properties in superlattices , 2002 .

[23]  Brian C. Sales,et al.  Thermoelectric Materials: New Approaches to an Old Problem , 1997 .

[24]  A. Yamamoto,et al.  Thermoelectric properties of Al1−xInxN and Al1−y−zGayInzN prepared by radio-frequency sputtering: Toward a thermoelectric power device , 2003 .

[25]  Seungmin Lee,et al.  Heat transport in thin dielectric films , 1997 .

[26]  Koji Miyazaki,et al.  Structure and thermoelectric properties of boron doped nanocrystalline Si0.8Ge0.2 thin film , 2006 .