AlGaN/GaN heterostructures on insulating AlGaN nucleation layers

A single temperature process using AlGaN nucleation layers has been developed that produces device-quality, GaN-based materials with bilayer step surfaces. The AlGaN nucleation layer is deposited by flow modulation organometallic vapor phase epitaxy at temperatures in excess of 1000 °C, where GaN and AlGaN films can be subsequently grown. We have optimized this process on both sapphire and SiC substrates, where the conditions for nucleation are found to be quite different. For growth on SiC, aluminum mole fractions ranging from 6% to 35% result in featureless surfaces. Optimizing the alloy composition and thickness of the nucleation layer on SiC allows the deposition of GaN buffer layers exceeding 5 μm without the formation of cracks. A minimum of 15% aluminum in the nucleation layer is required for smooth growth on sapphire substrates. High room temperature two-dimensional electron gas mobilities of 1575 and 1505 cm2/Vs with sheet charge densities of 1.0×1013 and 1.4×1013 cm−2 are observed in undoped AlG...