This paper studies the pitting corrosion of a structural component of A357 aluminium alloy obtained by a semisolid metal forming process. The mechanical properties of the A357 alloy were improved by applying standard heat treatments T5 and T6. Impedance measurements were conducted at the rest potential and polarisation curves were plotted using a 3% NaCl test solution. After polarisation experiments the specimens were analysed by scanning electron microscopy. The corrosion process is favoured through the eutectic regions. The results show that T6 heat treatment improved the corrosion resistance of the A357 aluminium alloy.
Lochkorrosion der durch Umformung im halbfestem Zustand erhaltenen Aluminiumlegierung A357
In der vorliegenden Arbeit wird die Lochkorrosion der Aluminiumlegierung A357 untersucht, die in tragenden Komponenten verwendet wird und durch einen Umformprozes in halbfestem Zustand erzeugt wird. Die mechanischen Eigenschaften der Legierung A357 werden durch Anwendung der standardisierten Temperaturbehandlungen T5 und T6 verbessert. Es wurden Impedanzmessungen des Ruhepotentials durchgefuhrt und die Polarisationskurven unter Verwendung einer 3%-iger NaCl-Losung bestimmt. Nach Abschlus der Polarisationsmessungen wurden die Proben mit Hilfe eines Elektronenmikroskops untersucht. Der Korrosionsprozes wird durch die eutektischen Bereiche gefordert. Die erzielten Ergebnisse deuten darauf hin, das die Korrosionsbestandigkeit der Aluminiumlegierung A357 durch die Temperaturbehandlung T6 verbessert wird.