Atomic force microscope tip-induced anodization of titanium film for nanofabrication of oxide patterns

Nanometer-scale oxide patterns were fabricated on Ti films deposited on Si(100) surface by means of atomic force microscope tip-induced anodization. The application of a negative bias voltage to a heavily doped silicon tip relative to the sample substrate permitted nanoscale lines and dots of titanium oxide to be formed directly on the titanium surfaces. Their sizes were dependent on the relative humidity, the scanning rate of the tip, and the pulse duration time. The spatial resolution of titanium oxide patterns was improved by increasing the tip scan rate and also by lowering the relative humidity. The smallest linewidth obtained in this experiment was about 18 nm. With increasing pulse duration time, the growth rate of oxide rapidly decreased. This result can be attributed to the decrease of the transport rate of ionic species through the existing oxide layer due to a reduction of electric field strength with increasing the oxide thickness.

[1]  Brian R. Bennett,et al.  Nanostructure patterns written in III–V semiconductors by an atomic force microscope , 1997 .

[2]  Hyung Joun Yoo,et al.  Nanometer-scale lithography on H-passivated Si(100) by atomic force microscope in air , 1997 .

[3]  Eric S. Snow,et al.  Single‐atom point contact devices fabricated with an atomic force microscope , 1996 .

[4]  Phaedon Avouris,et al.  Atomic force microscope tip-induced local oxidation of silicon: kinetics, mechanism, and nanofabrication , 1997 .

[5]  N. Cabrera,et al.  Theory of the oxidation of metals , 1949 .

[6]  Hiroyuki Sugimura,et al.  Chemical Approach to Nanofabrication: Modifications of Silicon Surfaces Patterned by Scanning Probe Anodization , 1995 .

[7]  Xinlong Wang,et al.  Observations of collision behavior of parametrically excited standing solitons , 1994 .

[8]  Michael T. Postek,et al.  Modification of hydrogen-passivated silicon by a scanning tunneling microscope operating in air , 1990 .

[9]  Hiroshi Yokoyama,et al.  Understanding scanned probe oxidation of silicon , 1998 .

[10]  Francesc Pérez-Murano,et al.  Local oxidation of silicon surfaces by dynamic force microscopy: Nanofabrication and water bridge formation , 1998 .

[11]  Kazuhiko Matsumoto,et al.  Application of scanning tunneling microscopy nanofabrication process to single electron transistor , 1996 .

[12]  Hiroshi Masuhara,et al.  Scanning tunneling microscope tip‐induced anodization of titanium: Characterization of the modified surface and application to the metal resist process for nanolithography , 1994 .

[13]  Detlef Hommel,et al.  First order distributed feedback operation in ZnSe based laser structures , 1995 .

[14]  Kang L. Wang,et al.  Nanometer scale patterning of silicon (100) surfaces by an atomic force microscope operating in air , 1994 .

[15]  John Alexander,et al.  Nanometer-scale lithography using the atomic force microscope , 1992 .

[16]  David R. Allee,et al.  Selective area oxidation of silicon with a scanning force microscope , 1993 .

[17]  Emmanuel Dubois,et al.  NANOOXIDATION USING A SCANNING PROBE MICROSCOPE : AN ANALYTICAL MODEL BASED ON FIELD INDUCED OXIDATION , 1997 .

[18]  T. Hattori,et al.  Modification of Silicon Surface Using Atomic Force Microscope with Conducting Probe , 1993 .