Numerical Modelling of Microcracking in PV Modules Induced by Thermo-mechanical Loads

Abstract Micro-cracking in polycrystalline Silicon is a serious concern for the durability of photovoltaic (PV) modules due to the resulting electrical power-loss. In this contribution, a thermo-mechanical cohesive zone model is proposed to predict the evolution of micro-cracks under the action of mechanical and thermal loads. The classical nonlinear cohesive zone approach, used in fracture mechanics to depict the phenomenon of cracking as a result of progressive breakage of atomic bonds, is extended to thermo-elastic fields. The additional thermal resistance of micro-cracks due to imperfect bonding is estimated according to an analogy with a contact mechanics formulation, where the dependency on the crack opening is suitably accounted for. A numerical example shows the applicability of the proposed approach to practical problems.

[1]  Shivani Agarwal,et al.  Study on long term reliability of photo-voltaic modules and analysis of power degradation using accelerated aging tests and electroluminescence technique , 2011 .

[2]  J. Greenwood,et al.  Contact of nominally flat surfaces , 1966, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[3]  Xiaopeng Xu,et al.  Numerical simulations of fast crack growth in brittle solids , 1994 .

[4]  F. Chenlo,et al.  Early degradation of silicon PV modules and guaranty conditions , 2011 .

[5]  M. Köntges,et al.  The risk of power loss in crystalline silicon based photovoltaic modules due to micro-cracks , 2011 .

[6]  P. Wriggers,et al.  A nonlocal cohesive zone model for finite thickness interfaces – Part I: Mathematical formulation and validation with molecular dynamics , 2011 .

[7]  Marco Paggi,et al.  Contact conductance of rough surfaces composed of modified RMD patches , 2011 .

[8]  Mgd Marc Geers,et al.  A Thermo-mechanical cohesive zone model , 2010 .

[9]  J. Barber,et al.  Bounds on the electrical resistance between contacting elastic rough bodies , 2003, Proceedings of the Royal Society of London. Series A: Mathematical, Physical and Engineering Sciences.

[10]  Marco Paggi,et al.  A multi-physics and multi-scale numerical approach to microcracking and power-loss in photovoltaic modules , 2013, 1303.7452.

[11]  A. Balandin,et al.  Graphene-multilayer graphene nanocomposites as highly efficient thermal interface materials. , 2012, Nano letters.

[12]  Ulrich Eitner,et al.  Spatial and orientational distribution of cracks in crystalline photovoltaic modules generated by mechanical load tests , 2011 .

[13]  S. Kajari-Schršder,et al.  Criticality of Cracks in PV Modules , 2012 .

[14]  Peter Wriggers,et al.  A nonlocal cohesive zone model for finite thickness interfaces – Part II: FE implementation and application to polycrystalline materials , 2011 .

[15]  T. Siegmund,et al.  A thermomechanical cohesive zone model for bridged delamination cracks , 2004 .

[16]  Heinrich Kurz,et al.  Impact of Micro-Cracks on the Degradation of Solar Cell Performance Based On Two-Diode Model Parameters , 2012 .