Rupture mechanisms in combined tension and shear : Experiments

An experimental investigation of the rupture mechanisms in a mid-strength and a high-strength steel were conducted employing a novel test configuration. The specimen used was a double notched tube ...

[1]  C. Barana.  Influence of non-singular stress terms and specimen geometry on small-scale yielding at crack tips in elastic-plastic materials , 2009 .

[2]  Frank A. McClintock,et al.  PLASTICITY ASPECTS OF FRACTURE , 1971 .

[3]  R. Narasimhan,et al.  Numerical simulations of hole growth and ductile fracture initiation under mixed-mode loading , 1996 .

[4]  Jinkook Kim,et al.  Modeling of void growth in ductile solids: effects of stress triaxiality and initial porosity , 2004 .

[5]  F. A. McClintock,et al.  A Criterion for Ductile Fracture by the Growth of Holes , 1968 .

[6]  R. H. Van Stone,et al.  Microstructural aspects of fracture by dimpled rupture , 1985 .

[7]  R. Narasimhan,et al.  An experimental investigation of constraint effects on mixed mode fracture initiation in a ductile aluminium alloy , 1999 .

[8]  Ke-Shi Zhang,et al.  Numerical analysis of the influence of the Lode parameter on void growth , 2001 .

[9]  D. P. Clausing,et al.  Effect of plastic strain state on ductility and toughness , 1970 .

[10]  D. M. Tracey,et al.  On the ductile enlargement of voids in triaxial stress fields , 1969 .

[11]  Jinkook Kim,et al.  Modeling of Ductile Fracture: Significance of Void Coalescence , 2006 .

[12]  W. Spitzig,et al.  Effect of volume fraction and shape of sulfide inclusions on through-thickness ductility and impact energy of high-strength 4340 plate steels , 1982 .

[13]  Y. Bréchet,et al.  Influence of microstructure-driven strain localization on the ductile fracture of metallic alloys , 2004 .

[14]  Robert H. Dodds,et al.  Ductile tearing in part-through cracks: experiments and cell-model predictions , 1998 .

[15]  A. A. Benzerga.  Micromechanics of coalescence in ductile fracture , 2002 .

[16]  A. Needleman,et al.  Analysis of the cup-cone fracture in a round tensile bar , 1984 .

[17]  T. Wierzbicki,et al.  Calibration and evaluation of seven fracture models , 2005 .

[18]  T. Pardoena,et al.  An extended model for void growth and coalescence , 2022 .

[19]  T. Wierzbicki,et al.  On fracture locus in the equivalent strain and stress triaxiality space , 2004 .

[20]  Percy Williams Bridgman,et al.  Studies in large plastic flow and fracture , 1964 .

[21]  Tomasz Wierzbicki,et al.  A Comparative Study on Various Ductile Crack Formation Criteria , 2004 .

[22]  J. W. Hancock,et al.  On the role of strain and stress state in ductile failure , 1983 .

[23]  Imad Barsoum,et al.  Rupture mechanisms in combined tension and shear—Micromechanics , 2007 .

[24]  J. Rice,et al.  Limitations to the small scale yielding approximation for crack tip plasticity , 1974 .

[25]  J. Hancock,et al.  On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states , 1976 .

[26]  A. Gurson.  Continuum Theory of Ductile Rupture by Void Nucleation and Growth: Part I—Yield Criteria and Flow Rules for Porous Ductile Media , 1977 .