Strain rate sensitivity and related plastic deformation mechanism transition in nanoscale Ag/W multilayers

Abstract Nanoscale metallic multilayers are a promising structural material for fabricating the next generation of nanoscale devices. Even though the mechanical properties of the multilayers have been extensively studied, the interpretation for the strain rate sensitivity of the multilayers is still lacking. In present study, the hardness and strain rate sensitivity of Ag/W multilayers with a wide range of modulation period Λ and modulation ratio η deposited by d.c. sputtering deposition were evaluated by nanoindentation testing. X-ray diffraction and transmission electron microscopy were carried out to investigate the texture and microstructure of the multilayers. Experimental results indicated that a mechanism transition occurred as the plastic deformation of the Ag/W multilayers was accommodated by the two constituent layers together at Λ ≤ 50 nm, while the plastic deformation localized mainly in Ag layers when Λ > 50 nm. A modified rule of mixture and plastic deformation localization model was proposed to describe the variation of strain rate sensitivity for the multilayers with smaller and larger Λ, respectively.

[1]  Miao Song,et al.  Microstructure and strengthening mechanisms in Cu/Fe multilayers , 2012 .

[2]  Xiaolei Wu,et al.  Microstructure and mechanical properties at different length scales and strain rates of nanocrystalline tantalum produced by high-pressure torsion , 2011 .

[3]  Fei Wang,et al.  Microstructure and flow stress of nanoscale Cu/Nb multilayers , 2013 .

[4]  Holm Geisler,et al.  Hardness enhancement and elastic modulus behaviour in sputtered Ag/Ni multilayers with different modulation wavelengths , 1999 .

[5]  Gang Liu,et al.  Mechanical properties of fcc/fcc Cu/Nb nanostructured multilayers , 2012 .

[6]  O. Bouaziz,et al.  Effective strain rate sensitivity of two phase materials , 2009 .

[7]  Guang-Ping Zhang,et al.  On plasticity and fracture of nanostructured Cu/X (X = Au, Cr) multilayers: The effects of length scale and interface/boundary , 2010 .

[8]  B. Diak,et al.  Assessment of decomposition products in an Al-Mg-Si alloy by instrumented micro-indentation , 2001 .

[9]  Nan Li,et al.  Suppression of irradiation hardening in nanoscale V/Ag multilayers , 2011 .

[10]  F. Zeng,et al.  Influence of plasticity mismatch and porosity on mechanical behavior of nanoscale Ag/W multilayers , 2007 .

[11]  K. T. Ramesh,et al.  Effect of nanocrystalline and ultrafine grain sizes on the strain rate sensitivity and activation volume: fcc versus bcc metals , 2004 .

[12]  Charles Feldman,et al.  Distinguishing thin film and substrate contributions in microindentation hardness measurements , 1990 .

[13]  B. Diak,et al.  The determination of solute clusters in dilute aluminum alloys using strain rate sensitivity , 1997 .

[14]  Amit Misra,et al.  Strain rate sensitivity and activation volume of Cu/Ni metallic multilayer thin films measured via micropillar compression , 2012 .

[15]  Tian Jian Lu,et al.  Strain rate sensitivity of unequal grained nano-multilayers , 2011 .

[16]  M. Demkowicz,et al.  Structure, shear resistance and interaction with point defects of interfaces in Cu–Nb nanocomposites synthesized by severe plastic deformation , 2011 .

[17]  Jingzhou Zhang,et al.  Size-dependent deformation mechanisms and strain-rate sensitivity in nanostructured Cu/X (X = Cr, Zr) multilayer films , 2012 .

[18]  B. Diak,et al.  Dislocation-defect analysis during micro-indentation using displacement rate changes , 1997 .

[19]  J. H. Chen,et al.  Mechanical properties of crystalline Cu/Zr and crystal–amorphous Cu/Cu–Zr multilayers , 2012 .