The High Cycle Fatigue and Final Fracture Behavior of an Alloy Steel Used in Hydrogen Pressure Vessels: Influence of Notch

[1]  Yukitaka Murakami,et al.  The Effect of Hydrogen on Fatigue Properties of Metals used for Fuel Cell System , 2006 .

[2]  D. Koss,et al.  Temperature, strain rate, stress state and the failure of HY-100 steel , 2001 .

[3]  L. Tsay,et al.  Crack growth behaviour of heat-treated 4140 steel in air and gaseous hydrogen , 1998 .

[4]  C. Laird,et al.  Fractography of induction-hardened steel fractured in fatigue and overload , 1997 .

[5]  L. Tsay,et al.  Hydrogen embrittlement of a Ti-strengthened 250 grade maraging steel , 1997 .

[6]  Shuohong Gao,et al.  Temperature effects on gaseous hydrogen embrittlement of a high-strength steel , 1993 .

[7]  J. King,et al.  Hydrogen embrittlement contributions to fatigue crack growth in a structural steel , 1991 .

[8]  Viggo Tvergaard,et al.  Ductile fracture by cavity nucleation between larger voids , 1982 .

[9]  Robert P. Wei,et al.  Fatigue Crack Growth in 2-1/4-Cr-1Mo Steel Exposed to Hydrogen Containing Gases , 1979 .

[10]  Robert P. Wei,et al.  Fracture mechanics and surface chemistry studies of subcritical crack growth in AISI 4340 steel , 1978 .

[11]  Robert P. Wei,et al.  Gaseous hydrogen embrittlement of high strength steels , 1977 .

[12]  C. Mcmahon,et al.  Intergranular fracture in 4340-type steels: Effects of impurities and hydrogen , 1977 .

[13]  J. Hancock,et al.  On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states , 1976 .

[14]  A. Tetelman,et al.  Embrittlement of a ferrous alloy in a partially dissociated hydrogen environment , 1971 .

[15]  H. Nelson,et al.  Embrittlement of 4130 steel by low-pressure gaseous hydrogen , 1970, Metallurgical and Materials Transactions B.