Intrinsic kinetics of photocatalytic oxidation of formic and oxalic acid on immobilised TiO2 films

Titanium dioxide (TiO2) photocatalysis is a possible alternative/complementary technology to conventional water treatment methods. The TiO2 catalyst may be used as slurry or it may be immobilised onto a supporting substrate. With immobilised TiO2 films mass transfer problems occur in most photocatalytic reactors, which results in a reduction of reactor efficiency and in the accuracy of measured catalyst efficiency and kinetics. In order to determine the real intrinsic kinetics of photocatalytic reactions on immobilised TiO2 films a stirred tank reactor (STR) was used. The reactor incorporated a propeller and a baffle, thus providing good mixing and efficient mass transfer to the TiO2 film. Degussa P25 was immobilised onto borosilicate glass by a dip coating method and the kinetics of the photocatalytic degradation of the model pollutants, formic acid and oxalic acid were investigated as a function of catalyst loading, initial pollutant concentration and propeller rotation speed. The rate of degradation. of either acid. was not mass transfer limited at propeller speeds greater than 1000 rpm. The rate of formic acid degradation was dependent upon catalyst loading up to a maximum loading above which a decrease in the degradation rate was observed. The apparent quantum yield for the photocatalytic degradation was 5% for oxalic acid and 10% for formic acid. This compares very well with usual reported apparent quantum efficiencies for photocatalysis which are similar to1%. The photocatalytic oxidation of both acids could be described using a Langmuir-Hinshelwood kinetic model. (C) 2003 Elsevier B.V. All rights reserved.

[1]  A. Beenackers,et al.  Comparison of the efficiency of immobilized and suspended systems in photocatalytic degradation , 2001 .

[2]  Andrew Mills,et al.  An overview of semiconductor photocatalysis , 1997 .

[3]  N. Wu,et al.  A kinetic model for photocatalytic degradation of organic contaminants in a thin-film TiO2 catalyst , 2000 .

[4]  Ajay K. Ray,et al.  Development of a new photocatalytic reactor for water purification , 1998 .

[5]  David F. Ollis,et al.  Photocatalytic degradation of organic water contaminants: Mechanisms involving hydroxyl radical attack , 1990 .

[6]  Ajay K. Ray,et al.  Novel photocatalytic reactor for water purification , 1998 .

[7]  M. Anderson,et al.  Effects of pH and Applied Potential on Photocurrent and Oxidation Rate of Saline Solutions of Formic Acid in a Photoelectrocatalytic Reactor , 2000 .

[8]  M. Hoffmann,et al.  Photocatalytic oxidation of organic acids on quantum-sized semiconductor colloids. , 1994, Environmental science & technology.

[9]  R. W. Matthews,et al.  Photocatalytic oxidation of organic contaminants in water: An aid to environmental preservation , 1992 .

[10]  A. Mills,et al.  Photomineralisation of 4-chlorophenol sensitised by TiO2 thin films , 1998 .

[11]  Dong Hyun Kim,et al.  Solution factors affecting the photocatalytic and photoelectrocatalytic degradation of formic acid using supported TiO2 thin films , 1996 .

[12]  Andrew Mills,et al.  WATER-PURIFICATION BY SEMICONDUCTOR PHOTOCATALYSIS , 1993 .

[13]  J. Anthony Byrne,et al.  Immobilisation of TiO2 powder for the treatment of polluted water , 1998 .

[14]  C. Turchi,et al.  Comment. Photocatalytic reactor design: an example of mass-transfer limitations with an immobilized catalyst , 1988 .

[15]  M. Anderson,et al.  Photoelectrocatalytic degradation of formic acid using a porous titanium dioxide thin-film electrode. , 1994, Environmental science & technology.

[16]  R. W. Matthews.  Kinetics of photocatalytic oxidation of organic solutes over titanium dioxide , 1988 .

[17]  J. Krýsa,et al.  Photocatalytic degradation rate of oxalic acid on the semiconductive layer of n-TiO2 particles in the batch mode plate reactor Part I: Mass transfer limits , 1998 .

[18]  S. Martin,et al.  Environmental Applications of Semiconductor Photocatalysis , 1995 .