Air oxidation of Zircaloy-4 in the 600–1000 °C temperature range: Modeling for ASTEC code application

Abstract Progress in the treatment of air oxidation of zirconium in severe accident (SA) codes are required for a reliable analysis of severe accidents involving air ingress. Air oxidation of zirconium can actually lead to accelerated core degradation and increased fission product release, especially for the highly-radiotoxic ruthenium. This paper presents a model to simulate air oxidation kinetics of Zircaloy-4 in the 600–1000 °C temperature range. It is based on available experimental data, including separate-effect experiments performed at IRSN and at Forschungszentrum Karlsruhe. The kinetic transition, named “breakaway”, from a diffusion-controlled regime to an accelerated oxidation is taken into account in the modeling via a critical mass gain parameter. The progressive propagation of the locally initiated breakaway is modeled by a linear increase in oxidation rate with time. Finally, when breakaway propagation is completed, the oxidation rate stabilizes and the kinetics is modeled by a linear law. This new modeling is integrated in the severe accident code ASTEC, jointly developed by IRSN and GRS. Model predictions and experimental data from thermogravimetric results show good agreement for different air flow rates and for slow temperature transient conditions.

[1]  Martin Steinbrück,et al.  Prototypical experiments relating to air oxidation of Zircaloy-4 at high temperatures , 2009 .

[2]  C. Rosa Oxidation of zirconium—A critical review of literature , 1968 .

[3]  Brian J. Cox,et al.  Oxidation of Zirconium and its Alloys , 1976 .

[4]  P. Barbéris Zirconia powders and Zircaloy oxide films: tetragonal phase evolution during 400°C autoclave tests , 1995 .

[5]  Martin Steinbrück,et al.  Recent advances in understanding ruthenium behaviour under air-ingress conditions during a PWR severe accident , 2010 .

[6]  T. Vandergraaf,et al.  The Canadian Spent Fuel Storage Canister: Some Materials Aspects , 1977 .

[7]  I. Hwang,et al.  A working hypothesis on oxidation kinetics of Zircaloy , 2001 .

[8]  J. Szpunar,et al.  Tetragonal phase stability in ZrO2 film formed on zirconium alloys and its effects on corrosion resistance , 2007 .

[9]  F. Jacq,et al.  The ASTEC Integral Code for Severe Accident Simulation , 2009 .

[10]  Yi-bing Cheng,et al.  Role of Anion Vacancies in Nitrogen‐Stabilized Zirconia , 1993 .

[11]  Michel Soustelle,et al.  Differences in reactivity of oxide growth during the oxidation of Zircaloy-4 in water vapour before and after the kinetic transition , 2003 .

[12]  A. Bell,et al.  Water-Assisted Tetragonal-to-Monoclinic Phase Transformation of ZrO2 at Low Temperatures , 2000 .

[13]  C. Duriez,et al.  Separate-effect tests on zirconium cladding degradation in air ingress situations , 2009 .

[14]  H. B. Probst,et al.  Critical role of nitrogen during high temperature scaling of zirconium , 1973 .

[15]  C. Duriez,et al.  Zircaloy-4 and M5 ® high temperature oxidation and nitriding in air , 2008 .

[16]  L. N. Kmetyk,et al.  A review of the technical issues of air ingression during severe reactor accidents , 1994 .

[17]  M. Perez,et al.  Recherches sur les oxynitrures metalliques , 1967 .

[18]  M. Pijolat,et al.  Oxidation kinetics of ZrNbO in steam: differences between the pre-and post-transition stages , 2005 .