Effects of defects in composite wind turbine blades – Part 2: Progressive damage modeling of fiberglass-reinforced epoxy composites with manufacturing-induced waves

Abstract. Composite wind turbine blades are typically reliable; however, premature failures are often in regions of manufacturing defects. While the use of damage modeling has increased with improved computational capabilities, they are often performed for worst-case scenarios in which damage or defects are replaced with notches or holes. To better understand and predict these effects, an effects-of-defects study has been undertaken. As a portion of this study, various progressive damage modeling approaches were investigated to determine if proven modeling capabilities could be adapted to predict damage progression of composite laminates with typical manufacturing flaws commonly found in wind turbine blades. Models were constructed to match the coupons from, and compare the results to, the characterization and material testing study presented as a companion. Modeling methods were chosen from established methodologies and included continuum damage models (linear elastic with Hashin failure criteria, user-defined failure criteria, nonlinear shear criteria), a discrete damage model (cohesive elements), and a combined damage model (nonlinear shear with cohesive elements). A systematic, combined qualitative–quantitative approach was used to compare consistency, accuracy, and predictive capability for each model to responses found experimentally. Results indicated that the Hashin and combined models were best able to predict material response to be within 10 % of the strain at peak stress and within 10 % of the peak stress. In both cases, the correlation was not as accurate as the wave shapes were changed in the model; correlation was still within 20 % in many cases. The other modeling approaches did not correlate well within the comparative framework. Overall, the results indicate that this combined approach may provide insight into blade performance with known defects when used in conjunction with a probabilistic flaw framework.

[1]  Jared W. Nelson,et al.  EFFECTS OF DEFECTS IN COMPOSITE WIND TURBINE BLADES: ROUND 2 , 2012 .

[2]  M. Hyer,et al.  Effects of Layer Waviness on the Compression Strength of Thermoplastic Composite Laminates , 1993 .

[3]  Ugo Icardi,et al.  Assessment of Recent Theories for Predicting Failure of Composite Laminates , 2007 .

[4]  Ramesh Talreja,et al.  Modeling of Wrinkling in Sandwich Panels under Compression , 1999 .

[5]  Sanjib Goswami,et al.  A Finite Element Investigation on Progressive Failure Analysis of Composite Bolted Joints Under Thermal Environment , 2005 .

[6]  K Hazra,et al.  Experimental fabrication and characterization of out-of-plane fiber waviness in continuous fiber-reinforced composites , 2012 .

[7]  Sérgio Frascino Müller de Almeida,et al.  Critical Void Content for Polymer Composite Laminates , 2005 .

[8]  John F. Mandell,et al.  Compression Strength of Carbon Fiber Laminates Containing Flaws with Fiber Waviness , 2004 .

[9]  D. S. Dugdale.  Yielding of steel sheets containing slits , 1960 .

[10]  Michael R Wisnom,et al.  Modelling failure of composite specimens with defects under compression loading , 2013 .

[11]  D. Krajcinovic,et al.  Introduction to continuum damage mechanics , 1986 .

[12]  Daniel O. Adams,et al.  Compression strength reductions in composite laminates due to multiple-layer waviness , 1995 .

[13]  W. Paepegem,et al.  Modelling the nonlinear shear stress-strain response of glass fibre- reinforced composites. Part I: Experimental results , 2006 .

[14]  Yuyong Chen,et al.  Influence of voids on interlaminar shear strength of carbon/epoxy fabric laminates , 2009 .

[15]  Ramesh Talreja,et al.  A continuum mechanics characterization of damage in composite materials , 1985, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[16]  Donald M. Blackketter,et al.  Modeling Damage in a Plain Weave Fabric-Reinforced Composite Material , 1993 .

[17]  John F. Mandell,et al.  Design and manufacturing considerations for ply drops in composite structures , 1999 .

[18]  T. Tay,et al.  Progressive damage modeling of open-hole composite laminates under compression , 2015 .

[19]  Pedro P. Camanho,et al.  A continuum damage model for composite laminates: Part I - Constitutive model , 2007 .

[20]  M. Benzeggagh,et al.  Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus , 1996 .

[21]  Pierre J. A. Minguet,et al.  Residual strength evaluation of typical aircraft composite structures with a large notch , 2012 .

[22]  M. A. McCarthy,et al.  Progressive damage analysis of multi-bolt composite joints with variable bolt–hole clearances , 2005 .

[23]  Christophe Baley,et al.  Application of Interlaminar Tests to Marine Composites. A Literature Review , 2004 .

[24]  H. S. Schwartz,et al.  Fundamental Aspects of Fiber Reinforced Plastic Composites. , 1968 .

[25]  Ramesh Talreja,et al.  Effects of void geometry on elastic properties of unidirectional fiber reinforced composites , 2005 .

[26]  F. Chang,et al.  Modelling of splitting and delamination in notched cross-ply laminates , 2000 .

[27]  Z. Hashin.  Failure Criteria for Unidirectional Fiber Composites , 1980 .

[28]  Viggo Tvergaard,et al.  Effect of strain-dependent cohesive zone model on predictions of crack growth resistance , 1996 .

[29]  T. Belytschko,et al.  Analysis of three‐dimensional crack initiation and propagation using the extended finite element method , 2005 .

[30]  Alistair B. Ogilvie,et al.  Blade reliability collaborative , 2013 .

[31]  M. Wisnom,et al.  Reduction in interlaminar shear strength by discrete and distributed voids , 1996 .

[32]  T. Belytschko,et al.  Extended finite element method for cohesive crack growth , 2002 .

[33]  Vincent B. C. Tan,et al.  Damage progression by the element-failure method (EFM) and strain invariant failure theory (SIFT) , 2005 .

[34]  James R. Rice,et al.  Elastic Fracture Mechanics Concepts for Interfacial Cracks , 1988 .

[35]  Isaac M Daniel,et al.  Failure of Composite Materials , 2007 .

[36]  EFFECTS OF DEFECTS IN COMPOSITE WIND TURBINE BLADES: ROUND 1 , 2012 .

[37]  Jared W. Nelson,et al.  Effects of defects in composite wind turbine blades – Part 1: Characterization and mechanical testing , 2017 .

[38]  Michael R Wisnom,et al.  PREDICTION OF DELAMINATION INITIATION AND GROWTH FROM DISCONTINUOUS PLIES USING INTERFACE ELEMENTS , 1998 .

[39]  J. L. Curiel Sosa,et al.  Modelling of mixed damage on fibre reinforced composite laminates subjected to low velocity impact , 2013 .

[40]  F. L. Matthews,et al.  A Progressive Damage Model for Mechanically Fastened Joints in Composite Laminates , 1999 .

[41]  G. I. Barenblatt.  THE MATHEMATICAL THEORY OF EQUILIBRIUM CRACKS IN BRITTLE FRACTURE , 1962 .

[42]  Stephen W. Tsai,et al.  A General Theory of Strength for Anisotropic Materials , 1971 .

[43]  Pedro P. Camanho,et al.  An engineering solution for mesh size effects in the simulation of delamination using cohesive zone models , 2007 .

[44]  R. Christensen.  Stress based yield/failure criteria for fiber composites , 1997 .

[45]  E. H. Kerner.  The Elastic and Thermo-elastic Properties of Composite Media , 1956 .

[46]  Jinyang Zheng,et al.  Progressive failure analysis of carbon fiber/epoxy composite laminates using continuum damage mechanics , 2008 .

[47]  Michael R Wisnom,et al.  A combined stress-based and fracture-mechanics-based model for predicting delamination in composites , 1993 .

[48]  Ali Evcil.  Simulation of Three Dimensional Progressive Damage in Composite Laminates , 2008 .

[49]  F. L. Matthews,et al.  Predicting Progressive Delamination of Composite Material Specimens via Interface Elements , 1999 .

[50]  David H. Allen,et al.  A micromechanical model for a viscoelastic cohesive zone , 2001 .

[51]  Bent F. Sørensen,et al.  Determination of cohesive laws by the J integral approach , 2003 .

[52]  F. Chang,et al.  A Progressive Damage Model for Laminated Composites Containing Stress Concentrations , 1987 .

[53]  Anthony M. Waas,et al.  Prediction of progressive failure in multidirectional composite laminated panels , 2007 .

[54]  Ronald Krueger,et al.  The Virtual Crack Closure Technique : History , Approach and Applications , 2002 .

[55]  Vincent B. C. Tan,et al.  Element-Failure: An Alternative to Material Property Degradation Method for Progressive Damage in Composite Structures , 2005 .

[56]  P. Camanho,et al.  Prediction of size effects in notched laminates using continuum damage mechanics , 2007 .

[57]  Ling Liu,et al.  Critical Void Content for Thermoset Composite Laminates , 2009 .

[58]  Ignace Verpoest,et al.  On modelling of damage evolution in textile composites on meso-level via property degradation approach , 2007 .

[59]  Fu-Kuo Chang,et al.  Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Compressive Loadings: Part I—Analysis , 1991 .

[60]  Yi Xiao,et al.  Bearing failure in bolted composite joints: analytical tools development , 2002 .