Magnesium hydroxide sulfate hydrate whisker flame retardant polyethylene/montmorillonite nanocomposites

Flame retardant maleated polyethylene/magnesium hydroxide sulfate hydrate whisker (MAPE/MHSH) composites containing organo-modified montmorillonite (OMT) were prepared by direct melt intercalation. Their morphology, combustion behaviour and thermal stability were carried out by X-ray diffraction (XRD), transmission electron microscopy (TEM), cone calorimetry and thermogravimetric analyses (TGA). The exfoliation of silicate layers within MAPE has been verified by XRD and TEM images. Cone calorimetry results indicated that a synergistic flame retardant effect on reducing heat release rate (HRR) occurred when MHSH and OMT were both present in nanocomposite. The reduction in HRR improved as the mass fraction of OMT was increased from 2 to 10 wt%, but there was little improvement above 5 wt% OMT loading level. TGA profiles of the nanocomposites revealed that the thermodegradation stability of the nanocomposites decreased as the OMT fraction increased from 2 to 10 wt%.

[1]  T. Kashiwagi,et al.  Cone Calorimeter Combustion and Gasification Studies of Polymer Layered Silicate Nanocomposites. , 2002 .

[2]  K. Chawla,et al.  Mechanical Behavior of Materials , 1998 .

[3]  Charles A. Wilkie,et al.  Preparation and flammability properties of polyethylene-clay nanocomposites , 2003 .

[4]  Marco Zanetti,et al.  Fire Retardant Halogen-Antimony-Clay Synergism in Polypropylene Layered Silicate Nanocomposites , 2002 .

[5]  Richard H. Harris,et al.  Flammability Properties of Polymer - Layered-Silicate Nanocomposites. Polypropylene and Polystyrene Nanocomposites , 2000 .

[6]  P. Hornsby,et al.  A study of the mechanism of flame retardance and smoke suppression in polymers filled with magnesium hydroxide , 1990 .

[7]  P. Ma,et al.  Dehydration and desulfuration of magnesium oxysulfate whisker , 2000 .

[8]  Jeffrey W. Gilman,et al.  Flammability and thermal stability studies of polymer layered-silicate (clay) nanocomposites , 1999 .

[9]  W. Fan,et al.  Study of the Fire Performance of Magnesium Hydroxide Sulfate Hydrate Whisker Flame Retardant Polyethylene , 2004 .

[10]  C. Koo,et al.  Synthesis and characterization of maleated polyethylene/clay nanocomposites , 2001 .

[11]  P. Veselý,et al.  Peculiarities of mechanical response of heavily filled polypropylene composites , 1991, Journal of Materials Science.

[12]  T. Courtney,et al.  Mechanical Behavior of Materials , 1990 .

[13]  Takashi Kashiwagi,et al.  Flame retardant mechanism of polyamide 6–clay nanocomposites ☆ , 2004 .

[14]  Yuan Hu,et al.  Intumescent flame retardant–montmorillonite synergism in polypropylene‐layered silicate nanocomposites , 2003 .

[15]  Jennifer A. Lee,et al.  Influence of clay exfoliation on the physical properties of montmorillonite/polyethylene composites , 2002 .